High-strength and high-toughness super-thick quenched and tempered hydroelectric steel plate and preparation method thereof

A high-strength and toughness, steel plate technology, applied in the field of alloy steel, can solve the problems of long process flow and limited maximum thickness, and achieve the effect of simple production process, strong toughness and strong practicability.

Pending Publication Date: 2021-10-19
NORTHEASTERN UNIV
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using continuous casting slabs, "normalizing + quenching + high temperature tempering" to produce thick steel plates with a maximum thickness of 115mm, the maximum thickness is limited, and the process flow is long

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and high-toughness super-thick quenched and tempered hydroelectric steel plate and preparation method thereof
  • High-strength and high-toughness super-thick quenched and tempered hydroelectric steel plate and preparation method thereof
  • High-strength and high-toughness super-thick quenched and tempered hydroelectric steel plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0054] The present invention will be further described below by examples.

[0055] like figure 1As shown, the steel plate metal tissue of the present invention is "slate martensite + slab bellite".

[0056] The chemical composition of the embodiment of the present invention is shown in Table 1;

[0057] The manufacturing process is shown in Table 2, Table 3, Table 4;

[0058] Mechanical properties are shown in Table 5, 6.

[0059] Table 1 Chemical composition table

[0060]

[0061] Table 2 Chemical composition table

[0062]

[0063] C eq (%) = C + Mn / 6 + Si / 24 + Ni / 40 + CR / 5 + MO / 4 + V / 14.

[0064] P cm (%) = C + Si / 30 + Mn / 20 + Cu / 20 + Ni / 60 + CR / 20 + MO / 15 + V / 10 + 5B.

[0065] Table 3 Steelmaking and Casting Process

[0066]

[0067] Table 4 Heating and rolling process

[0068]

[0069] Table 5 Heat treatment process

[0070]

[0071] Table 6 Template Steel Plate Performance (1 / 4 horizontal thickness)

[0072]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength and high-toughness super-thick quenched and tempered hydroelectric steel plate and a preparation method thereof. The steel plate comprises the following chemical components: 0.09-0.11% of C; 0.10-0.20% of Si; 0.70-0.90% of Mn; less than or equal to 0.010% of P; less than or equal to 0.003% of S; 0.20-0.40% of Ni; 0.30-0.40% of Cr; 0.85-0.95% of Mo; 0.25-0.35% of Cu; 0.02-0.04% of Nb; 0.010-0.020% of Ti; 0.035-0.055% of Als; 0.0004-0.0010% of B; less than 50 ppm of N; and the balance of Fe and inevitable impurities. Meanwhile, it is guaranteed that Pcm=C+Si / 30+(Mn+Cu+Cr) / 20+Ni / 60+Mo / 15+V / 10+5B is less than 0.26%; Ceq(%)=C+Mn / 6+Si / 24+Ni / 40+Cr / 5+Mo / 4 V / 14 is less than 0.56%. The thickness of the high-strength and high-toughness super-thick quenched and tempered hydroelectric steel plate is larger than 100 mm, the tensile strength is larger than or equal to 780 MPa, the yield strength is larger than or equal to 690 MPa, and the transverse Kv-70 DEG C is larger than or equal to 100 J.

Description

Technical field [0001] The present invention belongs to the field of alloy steel, which relates to a high-strength toughness ultra-thick mass-touched hydropower steel plate and a manufacturing method thereof. Background technique [0002] Japan's major steel companies have taken the use of B low-carbon low alloy steel component system in the 1960s, and developed a temperature steel plate for injection molded 800 MPa. 800MPa-level hydropower steel began to apply in Japan, Europe and China's Tombs. Entering the 21st century, 800MPa-level hydropower steel development in China, truly started to start, and applied to large power stations such as Hohhot Pumping Storage Power Station, Baihe Beach, Udao. [0003] China's 800MPA-grade hydropower steel is mainly steel plates with a thickness of 100 mm, and the strong toughness excellent 800MPA ultra-thick steel plate (thickness> 100mm ~ 200mm) is very high in the technical content of the technical content, less in China. [0004] China'...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/44C22C38/42C22C38/48C22C38/50C22C38/06C22C38/54C21D8/02C21D1/18
CPCC22C38/02C22C38/04C22C38/44C22C38/42C22C38/48C22C38/50C22C38/06C22C38/54C21D8/0226C21D1/18C21D2211/008C21D2211/002
Inventor 隋轶邓想涛王昭东付天亮吴浩
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap