Penetration inhibition type stab-resistant cloth capable of preventing scratching and stabbing and process thereof

A stab-proof and high-tech technology, applied in the field of clothing production, can solve the problems of complex production process, low production efficiency and low stab-proof performance of stab-proof cloth

Pending Publication Date: 2021-09-14
深圳市汉唐世家服饰有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides a penetration-inhibiting anti-stab cloth and its technology for preventing scratches and punctures, which solves the problems of complex production process, low anti-stab performance and low production efficiency of the existing anti-stab cloth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Penetration inhibition type stab-resistant cloth capable of preventing scratching and stabbing and process thereof
  • Penetration inhibition type stab-resistant cloth capable of preventing scratching and stabbing and process thereof
  • Penetration inhibition type stab-resistant cloth capable of preventing scratching and stabbing and process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Such as Figure 1-3 As shown, the penetration-inhibiting stab-resistant cloth process for preventing scratches includes the following steps:

[0032] Sp1: Raw material pretreatment, the raw materials are ultra-high molecular weight polyethylene fiber filaments and high-strength viscose fiber filaments, and the ultra-high molecular weight polyethylene fiber filaments and high-strength viscose fiber filaments are cut to the same length;

[0033] Sp2: Twisting treatment, twisting ultra-high molecular weight polyethylene fiber filaments and high-strength viscose fiber filaments, using three filaments to twist into one, three twisted into one strand, and the twist is 300 twists / m;

[0034] Sp3: Three-dimensional plain weave, three-dimensional plain weave uses ultra-high molecular weight polyethylene fiber filament strands to carry out radial, weft and Z-direction simultaneous weaving and forming, three-dimensional plain weave has 24 vertical layers, and the first eight layer...

Embodiment 2

[0041] Penetration-inhibiting stab-resistant fabric for preventing scratches, including the main body of the stab-resistant fabric. The main body of the stab-resistant fabric includes a stab-resistant layer, a connecting layer and a soft layer. The stab-resistant layer is made of ultra-high molecular weight polyethylene fiber filament strands. Horizontal direction plain weave Forming, the soft layer is formed by high-strength viscose fiber strands in the horizontal direction plain weave, the connecting layer is formed by the vertical direction plain weave of ultra-high molecular weight polyethylene fiber filament strands, and the connection layer is woven through the anti-stab layer and the soft layer in turn Weaving, the soft layer and the anti-stab layer are staggered in 1:1, and there are 8 layers in total. The top and bottom surfaces of the soft layer and the anti-stab layer are symmetrically distributed, and there are 8 layers of anti-stab layers. The ultra-high molecular w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides penetration inhibition type stab-resistant cloth capable of preventing scratching and stabbing and a process thereof, and relates to the technical field of garment production. Ultra-high molecular weight polyethylene fiber filaments and high-strength viscose fibers are adopted for three-dimensional plain weaving, so that plain weaving between layers in the Z direction is carried out according to the number of layers while warp and weft plain weaving is carried out, the stab-resistant cloth is integrally woven and formed, the compactness between the layers is higher, and the strength between the layers is enhanced; twill weaving is performed by the high-strength viscose fibers, and the hydrophilicity of the stab-resistant cloth is improved while the stab-resistant performance of the stab-resistant cloth is improved through the ultra-high molecular weight polyethylene fiber filament layers and the high-strength viscose fiber layers which are distributed in a staggered mode, so that the softness of the stab-resistant cloth is improved; and the three-dimensional weaving process is simple and convenient, the working time is saved, the working efficiency is improved, and batch production and use are facilitated.

Description

technical field [0001] The invention relates to the technical field of clothing production, in particular to a penetration-inhibiting stab-proof cloth for preventing scratches and a process thereof. Background technique [0002] Anti-stab clothing is used to protect the wearer from harm when encountering sharp knives, sharp objects, etc. when cutting, cutting, chopping, scraping, scratching, etc. Wear it under the risk of being cut. The soft stab-resistant clothing is composed entirely of high-performance chemical fibers and other soft fibers. According to the flexibility and flexibility of the stab-resistant material, the stab-resistant clothing can be divided into three types, namely: Hard stab-resistant clothing, semi-hard and semi-soft stab-resistant clothing, and soft stab-resistant clothing are the best among the three types of stab-resistant clothing. High-performance chemical fibers can not only maintain the stab-resistant performance of the stab-resistant clothing, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D25/00D03D15/47D03D15/283D03D15/225D03D15/573D03D15/50F41H1/02
CPCD03D25/005D03D15/47D03D15/283D03D15/225D03D15/573D03D15/50F41H1/02D10B2321/0211D10B2201/24
Inventor 肖惠玲肖传淼谢婷华游淑朋
Owner 深圳市汉唐世家服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More