Lightweight high-strength Mg-Ta composite metal plate and room-temperature rolling forming method thereof

A clad metal, room temperature rolling technology, applied in the field of metal material processing, can solve the problems of unsatisfactory performance, strength and performance, affecting the engineering production efficiency of clad sheets, etc.

Active Publication Date: 2021-09-07
NORTH CHINA ELECTRIC POWER UNIV (BAODING) +1
View PDF15 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, in terms of rolling forming of Mg / Ta in China, as disclosed in Chinese patent CN112742870A, the preparation method of heterogeneous shielding type magnesium-tantalum multilayer composite plate is used in the rolling forming of Mg / Ta. Although the hot-rolled forming of pure tantalum can obtain the formed Mg / Ta composite plate, its performance, especially the strength performance, is not very satisfactory, and the hot-rolled forming process affects the engineering production efficiency of the composite plate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lightweight high-strength Mg-Ta composite metal plate and room-temperature rolling forming method thereof
  • Lightweight high-strength Mg-Ta composite metal plate and room-temperature rolling forming method thereof
  • Lightweight high-strength Mg-Ta composite metal plate and room-temperature rolling forming method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The room temperature rolling forming method (one-pass rolling) of the lightweight and high-strength Mg-Ta composite metal plate described in this embodiment comprises the following steps:

[0045] (1) Prepare AZ31B magnesium alloy, 1060 aluminum alloy and pure tantalum plate, the thickness of magnesium alloy plate is 1±0.2mm, the thickness of 1060 aluminum alloy is 0.1±0.03mm, and the thickness of pure tantalum plate is 1±0.2mm, among which The chemical composition of the AZ31B material and the pure aluminum intermediate layer should comply with the provisions of the national standards GB / T5153-2016 and GB / T3190-2020. The chemical composition of pure tantalum is shown in Table 1, and the dimensions of each material are shown in Table 2 below ;

[0046] Table 1 Composition of pure tantalum

[0047] element C H O Nb Fe W Mo Si Ta (wt%) 0.010 0.015 0.015 0.050 0.005 0.010 0.010 0.005 Bal.

[0048] Table 2 Size chart of magnesium...

Embodiment 2

[0066] The room temperature rolling method of the lightweight and high-strength Mg-Ta / Al composite metal plate described in this embodiment comprises the following steps:

[0067] (1) Prepare AZ31B magnesium alloy, 1060 aluminum alloy and pure tantalum plate, the performance of each plate is the same as embodiment 1; the above-mentioned magnesium alloy plate is carried out annealing pretreatment, promptly in the vacuum tube type high-temperature furnace, at 230 ℃ constant temperature insulation 2 Hours, then air-cooled for later use;

[0068] Grind the surface of the above-mentioned AZ31 magnesium alloy (after annealing), pure aluminum plate, and pure tantalum plate with an angle grinder to remove the oxide film on the surface of the material. The surface of the magnesium alloy is polished for about 0.5 minutes, and the surface of the pure tantalum plate is polished for about 1 minute; then, Wipe the surface of the polished material with absolute ethanol to remove the oil stai...

Embodiment 3

[0073] The room temperature rolling method of the lightweight and high-strength Mg-Ta / Al composite metal sheet described in this embodiment includes the following steps:

[0074] (1) prepare AZ31B magnesium alloy, 1060 aluminum alloy and pure tantalum plate, the performance of each plate is the same as embodiment 1; The above-mentioned magnesium alloy plate is carried out annealing pretreatment, promptly in the vacuum tube type high-temperature furnace, under 250 ℃ constant temperature insulation 1.8 Hours, then air-cooled for later use;

[0075] Grind the surface of the above-mentioned AZ31 magnesium alloy (after annealing), pure aluminum plate, and pure tantalum plate with an angle grinder to remove the oxide film on the surface of the material. The surface of the magnesium alloy is polished for about 0.5 minutes, and the surface of the pure tantalum plate is polished for about 1 minute; then , wipe the surface of the polished material with absolute ethanol to remove the oil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of metal material processing, particularly relates to a lightweight high-strength Mg-Ta composite metal plate, and further discloses a room-temperature rolling preparation method of the lightweight high-strength Mg-Ta composite metal plate. According to the lightweight high-strength Mg-Ta composite metal plate, the light metal rolling pure aluminum middle layer is additionally arranged between the magnesium alloy plate and the tantalum metal plate, and low-temperature annealing treatment and high-temperature diffusion bonding treatment between rolling passes are supplemented, so that a high-strength interface with mechanical connection and metallurgical bonding is formed between magnesium and tantalum dissimilar metals; and the lightweight high-strength Mg-Ta composite metal plate is successfully prepared, a new thought is provided for room-temperature forming between a light structural material and a heavy metal material, and meanwhile the magnesium-tantalum composite metal plate has positive significance in improving the structural technical level of a deep space exploration spacecraft.

Description

technical field [0001] The invention belongs to the technical field of metal material processing, and in particular relates to a light-weight and high-strength Mg-Ta composite metal plate, and further discloses a room-temperature rolling forming method thereof. Background technique [0002] With the development of my country's aerospace technology, from a traditional aerospace power to an aerospace power, deep space exploration is one of the important supports to realize my country's aerospace transformation. Deep space exploration is to launch manned / unmanned spacecraft from the earth into space to conduct scientific investigation and space utilization on distant extraterrestrial bodies. For this reason, based on the current technical level of my country's current carrying and deep space spacecraft, it is impossible to successfully deliver some multifunctional loads to the predetermined orbit. Therefore, it is necessary to reduce the weight of the spacecraft structure to a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/01B32B15/20B32B15/00B32B38/00B32B38/16C21D9/00C22F1/02C22F1/04C22F1/06C22F1/18
CPCB32B15/017B32B38/0036B32B38/0012B32B38/162C22F1/02C22F1/04C22F1/06C22F1/18C21D9/0081B32B2038/0048B32B2250/40B32B2307/718
Inventor 韩修柱罗文博薛志勇孔钦可许焕宾
Owner NORTH CHINA ELECTRIC POWER UNIV (BAODING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap