Nickel pretreatment method for improving appearance of nickel layer of stainless steel/copper-nickel-zinc alloy material

A nickel-nickel-nickel and stainless steel technology, which is applied in the field of connector electroplating, can solve the problems of white spot, nickel-nickel-nickel material and stainless steel surface, etc., and achieve the effect of reducing cost, reducing assembly process, and the method is simple and easy.

Pending Publication Date: 2021-07-23
苏州磊屹光电科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a nickel pretreatment method for improving the appearance of the nickel layer of stainless steel / nickel-nickelite material, so as to overcome the appearance defects of blooming and white spot after nickel-plated nickel-nickel material and stainless steel surface in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel pretreatment method for improving appearance of nickel layer of stainless steel/copper-nickel-zinc alloy material
  • Nickel pretreatment method for improving appearance of nickel layer of stainless steel/copper-nickel-zinc alloy material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] (1) Preparation of liquid medicine: Dissolve nickel chloride in deionized water, then add hydrochloric acid solution, mix well and then add special additives in 3-5 times, mix well and set volume, set aside, wherein the concentration of nickel chloride is 200g / L, the concentration of hydrochloric acid is 100mol / L;

[0068] (2) Check the equipment: check the conductive clamp, the wire is not loose, the rectifier ripple rate is less than 5%, and the setting range is 50A / 12V;

[0069] (3) Electroplating treatment: Provide stainless steel / nickel-nickel-nickel material that needs nickel surface treatment, and immerse in the liquid medicine prepared in step (1), electroplating for 10 seconds under the condition of room temperature and current density of 5ASD;

[0070] (4) Cleaning treatment: immerse the electroplated stainless steel / nickel-nickel-nickel material that needs nickel surface treatment in deionized water, wash 3-5 times until the residual liquid medicine on the s...

Embodiment 2

[0072] (1) Preparation of liquid medicine: Dissolve nickel chloride in deionized water, then add hydrochloric acid solution, mix well and then add special additives in 3-5 times, mix well and set volume, set aside, wherein the concentration of nickel chloride is 150g / L, the concentration of hydrochloric acid is 120mol / L;

[0073] (2) Check the equipment: check the conductive clamp, the wire is not loose, the rectifier ripple rate is less than 5%, and the setting range is 50A / 12V;

[0074] (3) Electroplating treatment: Provide stainless steel / nickel-nickel-nickel material that needs nickel surface treatment, and immerse in the liquid medicine prepared in step (1), electroplating for 10 seconds under the condition of room temperature and current density of 5ASD;

[0075] (4) Cleaning treatment: immerse the electroplated stainless steel / nickel-nickel-nickel material that needs nickel surface treatment in deionized water, wash 3-5 times until the residual liquid medicine on the s...

Embodiment 3

[0077] (1) Preparation of liquid medicine: Dissolve nickel chloride in deionized water, then add hydrochloric acid solution, mix well and then add special additives in 3-5 times, mix well and set volume, set aside, wherein the concentration of nickel chloride is 250g / L, the concentration of hydrochloric acid is 150mol / L;

[0078] (2) Check the equipment: check the conductive clamp, the wire is not loose, the rectifier ripple rate is less than 5%, and the setting range is 50A / 12V;

[0079] (3) Electroplating treatment: Provide stainless steel / nickel-nickel-nickel material that needs nickel surface treatment, and immerse in the liquid medicine prepared in step (1), electroplating for 10 seconds under the condition of room temperature and current density of 5ASD;

[0080] (4) Cleaning treatment: immerse the electroplated stainless steel / nickel-nickel-nickel material that needs nickel surface treatment in deionized water, wash 3-5 times until the residual liquid medicine on the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention provides a nickel pretreatment method for improving the appearance of a nickel layer of a stainless steel / copper-nickel-zinc alloy material. The method comprises the steps of liquid medicine preparation, equipment inspection, electroplating treatment and cleaning treatment, wherein the step of liquid medicine preparation comprises the steps of dissolving nickel chloride in deionized water, then adding a hydrochloric acid solution, uniformly mixing, then adding a special additive for 3-5 times, uniformly mixing, and fixing the volume for later use. According to the nickel pretreatment method for improving the appearance of the nickel layer of the stainless steel and the copper-nickel-zinc alloy material, the problem that a product containing the stainless steel and the copper-nickel-zinc alloy material at the same time is poor in appearance after nickel plating is solved, the idea is expanded for product design and material selection, more molds do not need to be used, the assembling procedures are effectively reduced, the whole product cost is reduced, and the appearance defects of floating and white spots after nickel plating on the surfaces of the copper-nickel-zinc alloy material and the stainless steel in the prior art are overcome. The method provided by the invention is simple and easy to implement, green and environment-friendly, and is an environment-friendly process.

Description

technical field [0001] The application relates to a nickel pretreatment method for improving the appearance of a nickel layer of a stainless steel / nickel nickel material, which belongs to the field of connector electroplating. Background technique [0002] In the prior art, the product has stainless steel and nickel-nickel metal materials at the same time. Since the stainless steel and nickel-nickel metal materials contain different alloy components, appearance defects such as blooming and white spots will appear after nickel-plating on the surface of the nickel-nickel metal material and stainless steel. Therefore, how to provide a new surface nickel pretreatment process, so that the surface after nickel plating is smooth and bright, and the color and luster is uniform, is an urgent problem to be solved. Contents of the invention [0003] The object of the present invention is to provide a nickel pretreatment method for improving the appearance of the nickel layer of stain...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/12C25D5/48
CPCC25D3/12C25D5/48
Inventor 刘辉陈龙蔡礼超彭翔吴树升
Owner 苏州磊屹光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com