Preparation method of high-temperature-resistant modified asphalt waterproof coiled material and waterproof coiled material prepared by preparation method

A technology of modified asphalt and waterproof membrane, which is applied in the direction of chemical instruments and methods, flat products, and other household appliances, etc. It can solve the problem of low quality of modifier waterproof membrane, and achieve the effect of improving quality and improving precise control

Active Publication Date: 2021-06-04
潍坊市宇虹防水材料(集团)有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is used to overcome the problem of low quality of prepared waterproof membranes caused by the inability to accurately control the mixing of modifiers in asphalt in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-temperature-resistant modified asphalt waterproof coiled material and waterproof coiled material prepared by preparation method
  • Preparation method of high-temperature-resistant modified asphalt waterproof coiled material and waterproof coiled material prepared by preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0080] In order to make the objects and advantages of the present invention clearer, the present invention will be further described below in conjunction with the examples; it should be understood that the specific examples described here are only for explaining the present invention, and are not intended to limit the present invention.

[0081] Preferred embodiments of the present invention are described below with reference to the accompanying drawings. Those skilled in the art should understand that these embodiments are only used to explain the technical principle of the present invention, and are not intended to limit the protection scope of the present invention.

[0082] It should be noted that, in the description of the present invention, terms such as "upper", "lower", "left", "right", "inner", "outer" and other indicated directions or positional relationships are based on the terms shown in the accompanying drawings. The direction or positional relationship shown is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a high-temperature-resistant modified asphalt waterproof coiled material and the waterproof coiled material prepared by the preparation method, and relates to the technical field of waterproof coiled material preparation. The method comprises the following steps that asphalt is added into a high-speed shearing machine and heated to be completely melted; a modifier is added into the high-speed shearing machine, heating is performed, and a motor and an ultrasonic vibrator are started to enable a stirring paddle to stir and vibrate the mixed material; after being obtained, high-temperature-resistant modified asphalt is added into a screw extruder, a stabilizer is added, and melt extrusion is performed; and after stable high-temperature-resistant modified asphalt is obtained, sequential coating is performed on a coating machine according to the sequence of a bottom film layer, a lower modified asphalt layer, a lower isolating layer, a padding layer, an upper isolating layer and an upper modified asphalt layer to obtain the high-temperature-resistant modified asphalt waterproof coiled material. The standard dispersity coefficient range, the standard compatibility coefficient range and the standard viscosity range are set in a central control processor, and whether the modified asphalt reaches the standard or not is determined by judging whether actual values are in the ranges or not, so that the quality of the prepared waterproof coiled material is improved.

Description

technical field [0001] The invention relates to the technical field of waterproof coil preparation, in particular to a method for preparing a high-temperature-resistant modified asphalt waterproof coil and the waterproof coil. Background technique [0002] Modified asphalt waterproofing membranes are widely used in waterproofing projects such as roofs, basements, and toilets in industrial and civil buildings, as well as waterproofing and moisture-proofing in projects such as roof gardens, roads, bridges, tunnels, parking lots, and swimming pools. There is no leakage connection between them, which is the waterproof barrier of the whole project. The existing modified asphalt waterproofing membrane uses modified petroleum asphalt as the covering layer, polyester fiber non-woven fabric, jute cloth, glass fiber mat and other materials as the base, and plastic film as the anti-adhesive isolation layer. It is processed through certain processing procedures, and it has good water r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29D7/00B32B27/32B32B27/02B32B27/36B32B17/02B32B33/00
CPCB29D7/00B32B27/32B32B5/02B32B5/08B32B33/00B32B2262/0276B32B2262/101B32B2262/14B32B2255/10B32B2307/306B32B2307/7265
Inventor 王伟
Owner 潍坊市宇虹防水材料(集团)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com