A far-infrared quartz tube applied to a low-temperature non-combustible electronic smoke nebulizer and its preparation method

An electronic cigarette atomizer, low temperature non-combustion technology, applied in the field of quartz tubes, can solve the problems of uneven heating and low heating efficiency, and achieve the effects of uniform heating, good heating effect and improved adhesion

Active Publication Date: 2021-11-02
东莞市中科智恒新材料有限公司
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention also has the problems of low heating efficiency and uneven heating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A far-infrared quartz tube applied to a low-temperature non-combustible electronic smoke nebulizer and its preparation method
  • A far-infrared quartz tube applied to a low-temperature non-combustible electronic smoke nebulizer and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The far-infrared quartz tube used in the low-temperature non-combustible electronic vaporizer is composed of a conductive film layer, a far-infrared coating and a quartz tube connected in sequence. The far-infrared coating is coated on the surface of the conductive film layer, and the conductive film layer is coated on the Quartz tube surface; Wherein, far-infrared coating is formed by far-infrared coating, and far-infrared coating is prepared by the component of following parts by weight: pure acrylic emulsion 36 parts, sodium lauryl phosphate 2.5 parts, kaolin 12 parts, 96 parts of a mixture of propylene glycol methyl ether acetate and absolute ethanol, 1.5 parts of ethylene glycol, 42 parts of far-infrared powder, 9 parts of tin tetrachloride, and 3.5 parts of modifier; the conductive film layer is formed of conductive paste, conductive The slurry is prepared from the following components in parts by weight: 4.5 parts of sodium carboxymethylcellulose, 84 parts of N,N-...

Embodiment 2

[0050] The far-infrared quartz tube used in the low-temperature non-combustible electronic vaporizer is composed of a conductive film layer, a far-infrared coating and a quartz tube connected in sequence. The far-infrared coating is coated on the surface of the conductive film layer, and the conductive film layer is coated on the Quartz tube surface; Wherein, far-infrared coating is formed by far-infrared coating, and far-infrared coating is prepared from the component of following parts by weight: 32 parts of pure acrylic emulsions, 2.7 parts of sodium lauryl phosphate, 15 parts of kaolin, 90 parts of a mixture of propylene glycol methyl ether acetate and absolute ethanol, 1.6 parts of ethylene glycol, 48 parts of far-infrared powder, 7 parts of tin tetrachloride, and 3 parts of modifier; the conductive film layer is formed of conductive paste, conductive The slurry is prepared from the following components in parts by weight: 5 parts of sodium carboxymethylcellulose, 81 parts...

Embodiment 3

[0060] The far-infrared quartz tube used in the low-temperature non-combustible electronic vaporizer is composed of a conductive film layer, a far-infrared coating and a quartz tube connected in sequence. The far-infrared coating is coated on the surface of the conductive film layer, and the conductive film layer is coated on the Quartz tube surface; Wherein, far-infrared coating is formed by far-infrared coating, and far-infrared coating is prepared from the component of following parts by weight: 30 parts of pure acrylic emulsions, 3 parts of sodium lauryl phosphate, 14 parts of kaolin, 92 parts of a mixture of propylene glycol methyl ether acetate and absolute ethanol, 2 parts of ethylene glycol, 40 parts of far-infrared powder, 10 parts of tin tetrachloride, and 3 parts of modifier; the conductive film layer is formed of conductive paste, conductive The slurry is prepared from the following components in parts by weight: 4 parts of sodium carboxymethylcellulose, 80 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a far-infrared quartz tube applied to a low-temperature non-combustible electronic smog vaporizer. The far-infrared quartz tube is composed of a conductive film layer, a far-infrared coating and a quartz tube connected in sequence; wherein, the far-infrared coating is composed of a far-infrared Infrared coatings are formed. Far-infrared coatings are prepared from the following components by weight: 30-40 parts of pure acrylic emulsion, 2-3 parts of wetting and dispersing agents, 10-15 parts of fillers, 90-100 parts of solvents, film-forming 1-2 parts of auxiliary agent, 40-45 parts of far-infrared powder, 7-10 parts of tin tetrachloride, 3-4 parts of modifier; the conductive film layer is formed by conductive paste, and the conductive paste consists of the following parts by weight It is prepared from the following components: 4-5 parts of sodium carboxymethylcellulose, 80-90 parts of N,N-dimethylacetamide, and 12-18 parts of conductive graphite. The invention also provides a preparation method of the far-infrared quartz tube. The far-infrared quartz tube provided by the invention adopts a far-infrared heating mode and has better heating performance.

Description

technical field [0001] The invention relates to a quartz tube, in particular to a far-infrared quartz tube used in a low-temperature non-combustion electronic smoke nebulizer and a preparation method thereof. Background technique [0002] As people gradually become more aware of the dangers of traditional cigarettes, e-cigarettes, as an electronic product imitating cigarettes, are gaining more and more popularity. E-cigarettes use means such as atomization to turn e-liquid or cream into vapor, allowing users to inhale smoke that has a similar taste and feel to traditional cigarettes. [0003] There are two types of electronic cigarettes popular on the market, one is steam type and the other is low temperature non-combustible type. Among them, the low-temperature heating and non-burning electronic cigarette refers to heating and roasting the shredded tobacco through the low temperature generated by the atomizer, turning the nicotine in the shredded tobacco into steam and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A24F40/46A24F40/70
CPCA24F40/46A24F40/70
Inventor 周云徐中立胡瑞龙余庚俞其灿
Owner 东莞市中科智恒新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com