Preparation method of polymer quick-drying early-strength corrosion-resistant mortar

A production method and polymer technology, which is applied in the production field of polymer quick-drying and early-strength anti-corrosion mortar, can solve the problems of poor impermeability and low flexural strength of the mortar layer, and achieve strong adhesion and high flexural strength High, good corrosion resistance

Inactive Publication Date: 2021-05-28
佛山优尼凯新材料有限公司
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a method for making polymer quick-drying, early-strength and anti-corrosion mortar, which has the advantages of filling internal gaps and good practicability, and solves the problem of existing mortars during construction. Many gaps lead to poor impermeability and low flexural strength of the mortar layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polymer quick-drying early-strength corrosion-resistant mortar
  • Preparation method of polymer quick-drying early-strength corrosion-resistant mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0025] see Figure 1-2 , a method for making polymer quick-drying early-strength anti-corrosion mortar, comprising the following raw materials: 160-180 parts of sulphoaluminate cement, 50-60 parts of plaster powder, 80-90 parts of Portland cement, 0.5-1 part of polycarboxylate superplasticizer, 3-6 parts of rheology additive, 5-10 parts of hydroxyethyl methyl cellulose ether, acrylic acid polymer.

[0026] A method for preparing polymer quick-drying early-str...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of mortar manufacturing and application, and discloses a manufacturing method of polymer quick-drying early-strength anti-corrosion mortar. The method comprises the following raw materials: 160-180 parts of sulphoaluminate cement, 50-60 parts of calcined gypsum powder, 80-90 parts of Portland cement, 0.5-1 part of a polycarboxylate superplasticizer, 3-6 parts of a rheological additive, 5-10 parts of hydroxyethyl methyl cellulose ether and an acrylic polymer. According to the manufacturing method of the polymer quick-drying early-strength corrosion-resistant mortar, the acrylic polymer is added into the quick-drying early-strength corrosion-resistant mortar according to the mixing ratio of 4: 1, and compared with a common mortar layer, besides quick drying and early strength, internal gaps are obviously filled due to the addition of the special acrylic polymer, the mortar is high in impermeability and breaking strength, so that the problems of poor impermeability and low breaking strength of a mortar layer due to more gaps during construction of the existing mortar are effectively solved.

Description

technical field [0001] The invention relates to the technical field of mortar production and application, in particular to a production method of polymer quick-drying early-strength anti-corrosion mortar. Background technique [0002] Mortar is a bonding substance used in building bricks. It is made of a certain proportion of sand and cementing materials (cement, lime paste, clay, etc.) Mortar), lime mortar and clay mortar. Mortar is used for masonry and plastering projects, and can be divided into masonry mortar and plastering mortar. The former is used for masonry and component installation of bricks, stones and blocks, while the latter is It is used for plastering on walls, floors, roofs and beam-column structures to meet protection and decoration requirements. [0003] Mortar has been widely used nowadays. With the development of economy and society, more and more places and sites have put forward requirements for corrosion resistance, such as sewage pools in sewage tre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B111/20
CPCC04B28/14C04B2201/05C04B2111/20
Inventor 罗建光余松涛刘鹏飞
Owner 佛山优尼凯新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap