Hydrogenation pretreatment catalyst as well as preparation method and application thereof

A hydrogenation pretreatment and catalyst technology, which is applied in the direction of catalyst activation/preparation, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the problems of catalyst pore structure performance degradation, avoid local coking, improve utilization rate, Reduce the effect of migration

Active Publication Date: 2021-04-30
CHINA PETROLEUM & CHEM CORP +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The pore volume and specific surface area of ​​titanium dioxide are small, and a large amount of this component is introduced into the carrier to reduce the pore structure performance of the catalyst. It is not suitable for the treatment of coal tar components containing macromolecular aromatics, colloids and asphaltenes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogenation pretreatment catalyst as well as preparation method and application thereof
  • Hydrogenation pretreatment catalyst as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Weigh the powder according to the fact that the alumina powder a accounts for 30% of the total alumina weight. Calculating that magnesium oxide accounts for 4% of the weight of alumina powder a, weigh magnesium citrate to prepare an aqueous solution, and impregnate alumina powder a in equal volume; calculate that phosphorus accounts for 3.5% of the weight of alumina powder b, weigh ten The octaalkyl phosphate is configured into an aqueous solution, and an equal volume of alumina powder b is impregnated. The alumina powder loaded with additives was dried at 90°C for 18h. The alumina powder modified by the two additives was mixed with 2.3% of citric acid and 3.6% of the weight of the alumina, and then added to the acidic solution. The concentration of nitric acid in the acidic solution was 2.3wt%, and the rest was distilled water. Mix in a kneader for 15 minutes to form a plastic body and extrude into 1.7mm clover strips. The molding material was dried at 110° C. for 8 ...

Embodiment 2

[0046] Weigh the powder according to the alumina powder a accounting for 43% of the total alumina weight. Other subsequent steps were the same as in Example 1 to obtain catalyst Cat-2.

Embodiment 3

[0048] Weigh the powder according to the fact that the alumina powder a accounts for 60% of the total alumina weight. Other subsequent steps were the same as in Example 1 to obtain catalyst Cat-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrogenation pretreatment catalyst as well as a preparation method and application thereof. The method comprises the following steps: (1) loading a magnesium-containing compound solution to aluminum oxide powder a, and performing drying treatment; (2) loading the phosphorus-containing compound solution to alumina powder b, and carrying out drying treatment; (3) molding, drying and roasting the aluminum oxide powder dried in the step (1) and the step (2) to obtain a catalyst carrier; and (4) loading active metal on the carrier obtained in the step (3), and drying and roasting to obtain the final hydrogenation pretreatment catalyst. The catalyst prepared by the method has the advantages of appropriate pore size, centralized distribution, excellent stability and strong raw material adaptability. The catalyst can be used in the hydrogenation pretreatment process of inferior hydrocarbon raw materials with high oxygen content, high nitrogen content, high aromatic hydrocarbon content and the like.

Description

technical field [0001] The invention relates to a hydrogenation pretreatment catalyst and its preparation method and application, in particular to a hydrocarbon raw material with the characteristics of high oxygen content, high nitrogen content and high aromatic hydrocarbon content, which has good anti-coking performance and hydrothermal Properties of Hydroprocessing Catalyst Preparation Method. Background technique [0002] With the rapid development of my country's economy, the demand for fuel oil and chemical raw materials continues to increase, and the amount of crude oil processed every year continues to rise. At present, most of my country's processed crude oil depends on foreign crude oil imports. With the increase of crude oil extraction, the quality of crude oil at home and abroad is gradually deteriorating, and the trend of heavy quality is becoming more and more obvious. In order to meet the requirements of environmental protection and maximize the use of existi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/188B01J35/10B01J23/888B01J37/02B01J37/08C10G45/08
CPCB01J27/188B01J23/888B01J37/0201B01J37/0203B01J37/082B01J37/0018C10G45/08C10G2300/202B01J35/633B01J35/615
Inventor 王会刚杨占林姜虹刘奕丁思佳王继锋
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com