Reinforced polypropylene material, preparation method and application thereof

A technology of polypropylene material and straight-chain polypropylene, which is applied in the field of engineering plastics, can solve the problems of low melt elongation, low melt strength, floating fibers on the surface, etc., achieve high surface gloss, improve melt strength, float slimming effect

Active Publication Date: 2021-04-27
KINGFA SCI & TECH CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the polyolefin materials suitable for blow molding and blister use are basically pure HDPE or PP resins. These resins can be molded well, but they still need to be improved in terms of heat resistance and strength.
In the industry, the high strength and high rigidity of glass fibers are usually used to improve product strength and heat resistance, but conventional glass fiber reinforced polypropylene materials have low melt strength, low melt elongation, surface floating fibers and poor toughness And other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reinforced polypropylene material, preparation method and application thereof
  • Reinforced polypropylene material, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-11 and comparative example 1-6

[0050] Examples 1-11 and Comparative Examples 1-6: Preparation of reinforced polypropylene materials

[0051] Weigh each component according to the formula content, and mix all components except the reinforcing fiber evenly, and then add the mixture to the main feeding system of the twin-screw extruder; at the same time, add the reinforcing fiber to the side feeding of the twin-screw extruder material system, and then through twin-screw extruder melt blending, extrusion granulation to prepare reinforced polypropylene material.

[0052] The position of the side feeding system of the extruder can be adjusted, and the reinforcing fiber can enter the extruder screw in the first to tenth zones, and can be added after the extruder die, and then directly combined with the polypropylene melt. By adjusting the position where the reinforcing fiber enters the screw of the extruder, the reinforcing fiber with different length and content distribution can be obtained.

[0053] Among them,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a reinforced polypropylene material, a preparation method and application thereof. The reinforced polypropylene material comprises the following components in parts by weight: 30-70 parts of straight-chain polypropylene, 2-50 parts of long branched chain polypropylene, 1-20 parts of a compatilizer, 5-60 parts of reinforcing fibers, 0.1-20 part of a fluorine compound. According to the invention, the polypropylene material prepared by the method is high in surface gloss, good in toughness and high in melt strength, and is mainly suitable for blow molding, plastic uptake and other occasions.

Description

technical field [0001] The invention relates to the technical field of engineering plastics, in particular to a reinforced polypropylene material and its preparation method and application. Background technique [0002] Polypropylene material is currently the most used polymer material. It has excellent processing properties and mechanical properties. It is widely used in daily life and industrial production fields, such as: agricultural film, wire and cable, communication, housing construction and aviation manufacturing. Wait. [0003] At present, the polyolefin materials suitable for blow molding and blister use are basically pure HDPE or PP resins. These resins can be molded well, but they still need to be improved in terms of heat resistance and strength. In the industry, the high strength and high rigidity of glass fibers are usually used to improve product strength and heat resistance, but conventional glass fiber reinforced polypropylene materials have low melt stren...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/06C08L27/18C08K7/14
CPCC08L23/12C08L2205/035C08L2205/025C08L2205/04C08K2201/014C08K2201/004C08L51/06C08L27/18C08K7/14
Inventor 陆湛泉黄险波叶南飚陈平绪程文建程书文姜向新杨霄云
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap