Esterification product for preparing water reducing agent, preparation method of esterification product, shrinkage-reducing ether polycarboxylate water reducing agent and preparation method of shrinkage-reducing ether polycarboxylate water reducing agent

A technology of ether polycarboxylic acid and water reducing agent, which is applied in the field of construction admixtures, can solve the problems of low water reducing rate and poor shrinkage reduction effect, and achieve the effects of reducing drying shrinkage, reducing surface tension, and maintaining slump

Active Publication Date: 2021-04-27
科之杰新材料集团四川有限公司
View PDF13 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problem of low water-reducing rate and poor shrinkage-reducing effect of the existing shrinkage-reducing water-reducing agent mentioned in the above-mentioned background technology, the present invention provides an esterification product for preparing the water-reducing agent, the esterification product includes Monomers and unsaturated esterification products with amides and dihydroxyl groups

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Esterification product for preparing water reducing agent, preparation method of esterification product, shrinkage-reducing ether polycarboxylate water reducing agent and preparation method of shrinkage-reducing ether polycarboxylate water reducing agent
  • Esterification product for preparing water reducing agent, preparation method of esterification product, shrinkage-reducing ether polycarboxylate water reducing agent and preparation method of shrinkage-reducing ether polycarboxylate water reducing agent
  • Esterification product for preparing water reducing agent, preparation method of esterification product, shrinkage-reducing ether polycarboxylate water reducing agent and preparation method of shrinkage-reducing ether polycarboxylate water reducing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Preparation of esterification products: In parts by weight, add 48.5 parts of fumaric acid and 100 parts of cocoic acid diethanolamide to the first reaction vessel and mix them. Under nitrogen conditions, add 0.75 parts of antimony trioxide, 0.45 parts of Parts of methyl hydroquinone, and adjust the temperature at 110 ° C, react for 5 hours, that is, monomers with amide and double hydroxyl groups and unsaturated esterification products are obtained;

[0037] (2) Copolymerization reaction: in parts by weight, 2 parts of the esterified product obtained in step (1), 50 parts of methallyl alcohol polyoxyethylene ether with a molecular weight of 600 and 50 parts of methyl alkene with a molecular weight of 3000 Propanol polyoxyethylene ether, 0.45 parts of sodium dodecylbenzenesulfonate, 0.9 parts of diethylene glycol monolaurate and 120 parts of water are added to the second reaction vessel and stirred evenly, and 3.5 parts of hydrogen peroxide are mixed with 20 parts of ...

Embodiment 2

[0040] (1) Preparation of esterification product: in parts by weight, 45.2 parts of acrylic acid and 100 parts of coconut acid diethanolamide are added to the first reaction vessel for mixing, and under nitrogen conditions, 2.17 parts of cerium sulfate and 1.16 parts of 4-hydroxyl piperidinol oxygen free radical, and adjust the temperature at 120°C, and react for 6 hours to obtain monomers with amide and double hydroxyl groups and unsaturated esterified products;

[0041] (2) Copolymerization reaction: in parts by weight, 1 part of esterification product obtained in step (1), 50 parts of 600 methallyl alcohol polyoxyethylene ether and 50 parts of methallyl alcohol with a molecular weight of 3000 Polyoxyethylene ether, 0.5 parts of sodium dodecylbenzenesulfonate, 1 part of diethylene glycol monolaurate and 120 parts of water are added to the second reaction vessel and stirred evenly, and 2.8 parts of hydrogen peroxide and 20 parts of water are mixed evenly in In the first dropp...

Embodiment 3

[0044] (1) Preparation of esterification product: in parts by weight, 60.6 parts of fumaric acid and 100 parts of cocoic acid diethanolamide are added to the first reaction vessel for mixing, and under nitrogen conditions, 4 parts of cerium sulfate and 2.4 parts of formazan are added Hydroquinone, and adjust the temperature at 80°C, and react for 5 hours to obtain monomers and unsaturated esterification products with amides and dihydroxy groups;

[0045] (2) Copolymerization reaction: in parts by weight, 3 parts of esterification products obtained in step (1), 50 parts of 600 methallyl alcohol polyoxyethylene ethers and 50 parts of methallyl alcohols with a molecular weight of 3000 Polyoxyethylene ether, 0.3 parts of sodium dodecylbenzenesulfonate, 0.6 parts of diethylene glycol monolaurate and 117 parts of water are added to the second reaction vessel and stirred evenly, and 2.5 parts of hydrogen peroxide and 20 parts of water are mixed evenly in In the first dropping device;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of building additives, in particular to an esterification product for preparing a water reducing agent, a preparation method thereof, a shrinkage-reducing ether polycarboxylate water reducing agent and a preparation method of the shrinkage-reducing ether polycarboxylate water reducing agent. The esterification product comprises a monomer with amide and dihydroxy and an unsaturated acid esterification product. According to the shrinkage-reducing ether polycarboxylate superplasticizer prepared from the esterification product, the esterification product is prepared by esterification of coconut diethanolamide and unsaturated acid and has the advantages of low cost and simplicity and convenience in operation, and the prepared esterification product and a shrinkage-reducing functional monomer are subjected to copolymerization reaction, so that the polycarboxylate water reducing agent main chain is provided with amide and other hydrophilic groups and shrinkage reducing groups, the prepared polycarboxylate water reducing agent has lower surface tension, the drying shrinkage of concrete is effectively reduced, the concrete has better dispersity and dispersity retention performance, the internal mechanical property and strength of the concrete are effectively improved, and remarkable effect is achieved.

Description

technical field [0001] The invention relates to the technical field of building admixtures, in particular to an esterification product used for preparing a water reducer and a preparation method thereof, a shrinkage-reducing ether polycarboxylate water reducer and a preparation method thereof. Background technique [0002] As a new type of water reducer, polycarboxylate water reducer has the advantages of low dosage, high water reducing rate, good slump retention, small shrinkage, relatively good adaptability to cement and admixtures, and obvious reinforcement effect. The outstanding performance of the series has been widely used in various engineering fields. With the construction of national large-scale infrastructure nuclear power, water conservancy, bridges and various large-scale projects, the performance requirements of concrete are constantly improving. It also has the effect of reducing the drying shrinkage of hardened concrete. This multifunctional polycarboxylate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/06C08F220/14C08F220/20C08F2/26C04B24/26C04B103/30
CPCC08F283/065C08F2/26C04B24/2694C04B2103/302C08F220/14C08F220/20
Inventor 张小芳林艳梅方云辉史艳娜郭元强朱少宏
Owner 科之杰新材料集团四川有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap