A kind of highly crystalline modified PGA material and preparation method thereof

A high crystallinity, modified technology, applied in the field of PGA materials, can solve the problem of low glass transition temperature

Active Publication Date: 2022-04-29
HAINAN SHINER IND
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, due to the high melting point of the PGA material itself, the melting point exceeds 200 ° C, but its glass transition temperature is low, which makes its heat resistance temperature can be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of highly crystalline modified PGA material and preparation method thereof
  • A kind of highly crystalline modified PGA material and preparation method thereof
  • A kind of highly crystalline modified PGA material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The present invention provides a kind of preparation method of the highly crystalline modified PGA material described in above-mentioned technical scheme, comprises the following steps:

[0033] The polyglycolic acid resin, the filler, the plasticizer and the nucleating agent are mixed, extruded and granulated, and dried to obtain the modified PGA material.

[0034] In the present invention, the temperature of the feeding section in the extrusion granulation process is preferably 120-140°C, more preferably 130°C; the temperature of the mixing section is preferably 210-230°C, more preferably 220°C; the temperature of the extrusion section Preferably it is 220-240 degreeC, More preferably, it is 230 degreeC. The invention adopts a twin-screw extruder for extrusion granulation, and the aspect ratio of the extruder is at least 1:75.

[0035] In the present invention, the extrusion granulation adopts the method of water-stretching; the temperature of the water is 75°C-80°C....

Embodiment 1

[0048] Composition according to raw material weight ratio: 0.5 part of nucleating agent, 80 parts of polyglycolic acid resin (PGA), 15 parts of filler, 4.5 parts of plasticizer; Described nucleator is inositol; Described filler is edible starch; Described The weight-average molecular weight of the polyglycolic acid resin is 200,000 g / mol, and the melting point is 220°C; the plasticizer is mixed with polyvinyl alcohol and glycerol at a mass ratio of 1:2, dried at 75°C for 6 hours, and mixed 30min, obtain plasticizer, the molecular weight of described polyvinyl alcohol is 500g / mol, and alcoholysis degree is 99%;

[0049] First mix the above raw materials with a high-speed mixer for 1 hour, and then put them into twin-screw extruders for granulation; the length-to-diameter ratio of the twin-screw extruder must be at least 1:75, while the temperature of the feeding section is kept at about 130°C, and the temperature of the mixing section is 220°C, the temperature of the extrusion ...

Embodiment 2

[0055] Composition according to raw material weight ratio: 1 part of nucleating agent, 75 parts of polyglycolic acid resin (PGA), 15 parts of filler, 9 parts of plasticizer; Described nucleating agent is sebacic acid xylhydrazide; Described filler is Nanometer montmorillonite; the weight average molecular weight of the polyglycolic acid resin is 100,000 g / mol, and the melting point is 230 ° C; the plasticizer is after mixing polyvinyl alcohol and glycerin according to the mass ratio of 1:2.2, After drying at 80°C for 6 hours, mixing for 25 minutes to obtain a plasticizer, the polyvinyl alcohol has a molecular weight of 500 g / mol and a degree of alcoholysis of 95%;

[0056] First mix the above raw materials with a high-speed mixer for 1 hour, and then put them into twin-screw extruders for granulation; the length-to-diameter ratio of the twin-screw extruder must be at least 1:75, while the temperature of the feeding section is kept at about 130°C, and the temperature of the mixi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Vicat softening pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a highly crystalline modified PGA material and a preparation method thereof. The modified PGA material is prepared from the following raw materials in parts by weight: 70-80 parts of polyglycolic acid resin, 5-15 parts of filler, 4-25 parts 1 part of plasticizer and 0.5 to 1 part of nucleating agent; the plasticizer is a mixture of polyvinyl alcohol and glycerin with a mass ratio of 1:1.8 to 2.3, the molecular weight of polyvinyl alcohol is 300 to 500 g / mol, and the degree of alcoholysis ≥ 98 %; the nucleating agent is selected from one or more of talcum powder, inositol and sebacic acid xylene hydrazide; the filler is selected from one or more of nano-montmorillonite, nano-calcium carbonate and food-grade starch. The polyglycolic acid resin is modified by using the above-mentioned plasticizers, nucleating agents and fillers, so that the modified PGA material has high crystallization performance and can be used for the preparation of high heat-resistant products. The Vicat softening temperature is 205-210°C; the half-crystallization time is 5-15s; the relative crystallinity is 45-47%.

Description

technical field [0001] The invention belongs to PGA materials, in particular to a highly crystalline modified PGA material and a preparation method thereof. Background technique [0002] PGA (polyglycolic acid), also known as polyglycolide, has the fastest degradation rate among aliphatic polyester materials due to the shortest repeating unit in its molecular structure. At the same time, its low molecular weight product is an ideal complete microbial degradation inducer. [0003] However, due to the high melting point of the PGA material itself, the melting point exceeds 200 ° C, but its glass transition temperature is low, which makes its heat resistance temperature can be further improved. As we all know, the heat-resistant temperature of polymer materials is restricted by the glass transition temperature and melting point. The heat-resistant temperature of highly crystalline polymers is closer to the melting point, while the softening point and glass transition temperatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/04C08L29/04C08L3/02C08K5/053C08K5/25C08K3/34
CPCC08K3/34C08K5/053C08L3/02C08K5/25C08L29/04C08L67/04
Inventor 邢青涛黎坛王俊峰赵洁
Owner HAINAN SHINER IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com