Halogen-free low-smoke flame-retardant crosslinked polyethylene material and preparation method thereof

A cross-linked polyethylene, low-smoke flame-retardant technology, applied in the field of flame-retardant materials, can solve problems such as harm, release a large amount of toxic and harmful gases, and be not environmentally friendly, achieve good flame-retardant effect, overcome the easy agglomeration of flame retardants, The effect of low smoke production

Pending Publication Date: 2021-04-06
WEIHAI HONGLIN ELECTRIC POWER TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the flame-retardant polyethylene materials and PVC containing halogens are mainly on the market. Because they contain halogens, they are not environmentally friendly. After burning, a large amount of toxic and harmful gases will be released, causing great harm.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free low-smoke flame-retardant crosslinked polyethylene material and preparation method thereof
  • Halogen-free low-smoke flame-retardant crosslinked polyethylene material and preparation method thereof
  • Halogen-free low-smoke flame-retardant crosslinked polyethylene material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] In this example, the halogen-free low-smoke flame-retardant cross-linked polyethylene material and its preparation method, the raw materials are composed as follows in parts by mass:

[0031] 30 parts of metallocene linear low density polyethylene, 60 parts of linear low density polyethylene, 10 parts of maleic anhydride grafted polyethylene, 100 parts of flame retardant, 5 parts of lubricant, 2 parts of antioxidant, coupling agent 1- 2 parts, 10 parts of black masterbatch, 2 parts of cross-linking accelerator.

[0032] Among them, the above-mentioned flame retardant is 70 parts of aluminum hydroxide, 20 parts of mining magnesium hydroxide, and 10 parts of red phosphorus.

[0033] Wherein, the above-mentioned lubricant is 3 parts of silicone powder and 2 parts of PE wax.

[0034] Among them, the above-mentioned maleic anhydride-grafted polyethylene is commercially available, with a graft rate of about 0.92%, the brand name is MC218, and the manufacturer is Ningbo Nengz...

Embodiment 2

[0055] In this example, the halogen-free low-smoke flame-retardant cross-linked polyethylene material and its preparation method, the raw materials are composed as follows in parts by mass:

[0056] 25 parts of metallocene linear low density polyethylene, 60 parts of linear low density polyethylene, 15 parts of maleic anhydride grafted polyethylene, 90 parts of flame retardant, 5 parts of lubricant, 2 parts of antioxidant, 1.5 parts of coupling agent , 10 parts of black masterbatch, 3 parts of cross-linking accelerator.

[0057] Wherein, the above-mentioned flame retardant is 75 parts of magnesium hydroxide and 15 parts of red phosphorus.

[0058] Wherein, the above-mentioned lubricant is 5 parts of silicone powder.

[0059] Among them, the above-mentioned maleic anhydride-grafted polyethylene is commercially available, with a graft rate of about 0.92%, the brand name is MC218, and the manufacturer is Ningbo Nengzhiguang New Material Technology Co., Ltd.

[0060] Wherein, th...

Embodiment 3

[0080] In this example, the halogen-free low-smoke flame-retardant cross-linked polyethylene material and its preparation method, the raw materials are composed as follows in parts by mass:

[0081] 25 parts of metallocene linear low density polyethylene, 65 parts of linear low density polyethylene, 10 parts of maleic anhydride grafted polyethylene, 80 parts of flame retardant, 5 parts of lubricant, 2 parts of antioxidant, 1 part of coupling agent , 10 parts of black masterbatch, 2 parts of cross-linking accelerator.

[0082] Among them, the above-mentioned flame retardant is 65 parts of aluminum hydroxide and 15 parts of aluminum diethylphosphinate.

[0083] Wherein, the above-mentioned lubricant is 4 parts of silicone powder and 1 part of PE wax.

[0084] Among them, the above-mentioned maleic anhydride-grafted polyethylene is commercially available, with a graft rate of about 0.92%, the brand name is MC218, and the manufacturer is Ningbo Nengzhiguang New Material Technolog...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a halogen-free low-smoke flame-retardant crosslinked polyethylene material and a preparation method thereof. The polyethylene material is prepared from the following raw materials in parts by weight: 25-35 parts of metallocene linear low-density polyethylene, 55-65 parts of linear low-density polyethylene, 10-15 parts of maleic anhydride grafted polyethylene, 80-100 parts of a flame retardant, 5 parts of a lubricant, 2 parts of an antioxidant, 1-2 parts of a coupling agent, 10 parts of black masterbatch and 2-3 parts of a cross-linking accelerator. According to the halogen-free low-smoke flame-retardant crosslinked polyethylene material provided by the invention, the processing technology is easier to control, and the production cost is reduced; and the defects that a flame retardant in an existing halogen-free flame-retardant cross-linked polyethylene material is prone to agglomeration, large in addition amount and poor in mechanical property are overcome, and the halogen-free flame-retardant cross-linked polyethylene material is good in flame-retardant effect, small in smoke generation amount, good in impact resistance and excellent in comprehensive mechanical property.

Description

technical field [0001] The patent of the present invention relates to the technical field of flame-retardant materials, in particular to a halogen-free low-smoke flame-retardant cross-linked polyethylene material and a preparation method thereof. Background technique [0002] Polyethylene is a commonly used thermoplastic with light weight, non-toxic and environmental protection, and excellent electrical insulation properties. It is widely used in the field of wires and cables. At present, the flame-retardant polyethylene materials and PVC containing halogens are mainly on the market. Because they contain halogens, they are not environmentally friendly. After burning, they will release a large amount of toxic and harmful gases, causing great harm. Therefore, it is necessary to develop a halogen-free low-smoke flame-retardant cross-linked polyethylene material to ensure that the material has good flame retardancy and excellent mechanical properties, low smoke generation, and g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/08C08L51/06C08K13/02C08K3/22C08K3/02C08K5/5313B29C48/92B29B9/06
CPCC08L23/0815B29C48/92B29B9/06C08L2201/02C08L2201/22C08L2205/035B29C2948/92704B29C2948/9259C08K2003/2227C08K2003/2224C08K2003/026
Inventor 李其峰贾海峰于文广王鹏张士明王文霞
Owner WEIHAI HONGLIN ELECTRIC POWER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com