PBAT/PHA/wood powder composition suitable for preparing thin film and preparation and application of PBAT/PHA/wood powder composition

A technology of composition and wood powder, which is applied in the field of PBAT/PHA/wood powder composition, can solve the problems of reducing costs and reducing the amount of PBAT from petrochemical sources, and achieves the effects of reducing costs, ensuring biodegradability, and reducing production costs

Active Publication Date: 2021-03-26
中广核俊尔(浙江)新材料有限公司 +1
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the material does not indicate whether it can be used in the film field. Therefore, it is necessary to develop a blend of PHA and PBAT, and use wood flour as a film-grade fully biodegradable material to reduce the amount of PBAT from petrochemical sources and reduce costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PBAT/PHA/wood powder composition suitable for preparing thin film and preparation and application of PBAT/PHA/wood powder composition
  • PBAT/PHA/wood powder composition suitable for preparing thin film and preparation and application of PBAT/PHA/wood powder composition
  • PBAT/PHA/wood powder composition suitable for preparing thin film and preparation and application of PBAT/PHA/wood powder composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] PBAT / PHA / wood flour composition, comprising the following raw materials:

[0068] 55 parts by weight of PBAT BX8145, 10 parts by weight of PHA F1005, 23 parts by weight of poplar wood powder;

[0069] Based on the total weight of PBAT, PHA and poplar wood powder, triethanolamine 8wt%, EMH3wt%, KC-37280.2wt%, triglyceryl distearate 0.8wt%, N,N'-bis(2,6- Diisopropylphenyl) carbodiimide 0.1 wt%.

Embodiment 2

[0071] PBAT / PHA / wood flour composition, comprising the following raw materials:

[0072] 45 parts by weight of PBAT C1200, 20 parts by weight of PHA EM40010, 25 parts by weight of poplar wood powder;

[0073] Based on the total weight of PBAT, PHA and poplar wood flour, diethanolamine 7.5wt%, PBS-g-GMA 2wt%, ADR-4468 0.2wt%, pentaerythritol stearate 0.3wt%, poly-di(1,3 , 5-triisopropylphenyl) carbodiimide 0.2wt%.

Embodiment 3

[0075] PBAT / PHA / wood flour composition, comprising the following raw materials:

[0076] 55 parts by weight of PBAT C1200, 12 parts by weight of PHA EM10080, 25 parts by weight of poplar wood powder;

[0077] Based on the total weight of PBAT, PHA and poplar wood powder, triglycerol 3.5wt%, EBA-GMA 4wt%, ADR-4400 0.3wt%, pentaerythritol stearate 0.2wt%, polymerized carbodiimide UN- 03 0.3 wt%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
tensile strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PBAT / PHA / wood powder composition suitable for preparing a thin film, preparation of the PBAT / PHA / wood powder composition and application of the PBAT / PHA / wood powder composition in preparation of the thin film. The composition comprises the following raw materials: basic components and additional components. The basic components comprise the following components in parts by weight: 30-80 parts of PBAT, 5-30 parts of PHA and 5-40 parts of wood flour. Based on the total weight of the basic components, the additional components comprise 1 wt%-20 wt% of a plasticizer, 1 wt%-10 wt% of a compatilizer, 0.1 wt%-1 wt% of a chain extender, 0.1 wt%-2 wt% of a lubricant and 0.1 wt%-1 wt% of an anti-hydrolysis agent. The preparation method comprises the following steps: uniformly mixing the above raw materials in proportion, adding the formed mixture into a twin-screw granulating unit, and carrying out extruding and granulating to obtain PBAT / PHA / wood flour particles, wherein the temperature of each section of the double-screw granulating unit is in a range of 45-200 DEG C, and the rotating speed of screws is 200-450 rpm.

Description

technical field [0001] The invention relates to the field of biodegradable film materials, in particular to a PBAT / PHA / wood powder composition suitable for preparing films and its preparation and application. Background technique [0002] Biodegradable plastics are a class of plastics that can be degraded by microorganisms that exist in nature. The ideal biodegradable plastic is non-toxic and harmless after degradation, and has excellent performance. [0003] Polybutylene terephthalate-adipate (PBAT) is a completely biodegradable aliphatic-aromatic copolyester, which has a higher elongation at break of more than 700%, and has Good flexibility and processability have been widely used in plastic flexible packaging, but the source of PBAT is still petrochemicals, which consume petroleum resources and generate more carbon dioxide emissions in the process of production and processing. [0004] Polyhydroxyalkanoate (PHA) is a kind of intracellular polyhydroxyalkanoate synthesize...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L67/04C08L97/02C08J5/18
CPCC08J5/18C08J2367/02C08J2467/04C08J2497/02
Inventor 马志宇张磊涂征黄瑞杰宋玉兴
Owner 中广核俊尔(浙江)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com