A kind of method that dinuclear ionic liquid catalyzes and prepares polycarbonate

A technology of ionic liquid and polycarbonate, which is applied in clean catalysis and green fields, can solve the problems of catalyst inactivity, inability to promote molecular chain condensation, and inability to apply PC synthesis fields, etc., to shorten transesterification time and polycondensation time Effect

Active Publication Date: 2021-11-30
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports on the synthesis of PC from dicationic ionic liquids. Patent document CN201010503499.X reports a sulfonic acid dinuclear imidazole-based ionic liquid and its catalytic method for preparing butylene succinate. Ionic liquids cannot be used in the field of PC synthesis due to the inability to promote the condensation of molecular chains in the polycondensation stage, resulting in a catalyst that is basically inactive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method that dinuclear ionic liquid catalyzes and prepares polycarbonate
  • A kind of method that dinuclear ionic liquid catalyzes and prepares polycarbonate
  • A kind of method that dinuclear ionic liquid catalyzes and prepares polycarbonate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] At room temperature, 10.70 g (50 mmol) of diphenyl carbonate (hereinafter referred to as "DPC") and 7.35 g (50 mmol) of isosorbide (hereinafter referred to as "ISO") were added to a 250 ml four-necked flask (ISO The molar ratio with DPC is 1:1), pass into nitrogen protection, heat up to 130°C and add catalyst bis-(3-methyl-1-imidazole)-ethylene bromide (isosorbide 1.5×10 moles of alcohol -5 ), the prepolymerization stage was kept at 130°C for 3h under normal pressure. The polycondensation stage reduces the pressure in the reactor to 1×10 -5 Mpa gradually raised the reaction temperature to 240° C., and continued the reaction for 15 minutes.

[0065] Concrete reaction formula is as follows, and the productive rate that obtains product A through calculation is 99%, and characterization analysis obtains that product A weight average molecular weight is 89800g / mol, and glass transition temperature is (T g )173℃, thermal decomposition temperature is (T d5％ ) 328°C.

[00...

Embodiment 2

[0068] Same as Example 1, except that the catalyst is bis-(3-methyl-1-imidazole)-propylene bromide, other conditions remain unchanged. The productive rate that obtains product A through calculation is 97%, and characterization analysis obtains product A weight-average molecular weight to be 82600g / mol, T g 172°C, T d5％ is 325°C.

Embodiment 3

[0070] Same as Example 1, except that the catalyst is bis-(3-methyl-1-imidazole)-butylene bromide, other conditions remain unchanged. The productive rate that obtains product A through calculation is 98%, and characterization analysis obtains product A weight-average molecular weight to be 84500g / mol, T g 169°C, T d5％It is 321°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing polycarbonate by catalyzing a dual-nuclear ionic liquid. Dihydroxy compound and carbonic acid diester are used as raw materials, and are added to a reactor according to a molar ratio of 1:0.9 to 1:8, and are protected by an inert gas. , polycarbonate was synthesized by melt transesterification using binuclear imidazolium-based ionic liquids as catalysts. Compared with the literature reports, by adjusting the length of the alkyl chain between the bis-imidazole rings and changing the structure of the anion, the weight-average molecular weight of the synthesized polycarbonate reached 5×10 4 ~16×10 4 g / mol, the transesterification time is shortened by 25% to 50%, and the polycondensation time is shortened by 20% to 40%.

Description

technical field [0001] The invention relates to the field of green and clean catalysis, in particular to a method for preparing polycarbonate by catalyzing a binuclear ionic liquid. Background technique [0002] The catalysts currently used for the synthesis of polycarbonate are mainly organic base catalysts and metal catalysts. Among them, representative organic base catalysts include: 4-methylaminopyridine (CN102341363), triphenyl phosphite (CN103080201) and the like. Metal catalysts include alkali metal catalysts and alkaline earth metal catalysts. Such as sodium bicarbonate (JournalOf Applied Polymer Science: 2010, 134(30), 3658-3667; CN110461942), cesium carbonate (CN104094142), calcium acetate (CN107108873), zinc acetate (RSC ADVANCES, 2015, 5, 87311–87319) Wait. Compared with organic base catalysts, metal catalysts have higher reactivity, and the molecular weight of the synthesized polycarbonate is higher. However, metal catalysts often cause discoloration of prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G64/30
CPCC08G64/305C08G64/307
Inventor 徐菲王卫卫张锁江杨子锋张振才方文娟何宏艳
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More