Electrochemical repair method for dual deterioration of alkali aggregate damage and steel corrosion

A steel bar corrosion and repair method technology, applied in building maintenance, construction, building construction, etc., can solve problems that cannot be solved, have not been proposed or considered, and have not been proposed to solve problems, so as to prolong the service life, prevent steel bar from rusting, The effect of improving durability

Active Publication Date: 2022-01-25
SHANGHAI JIAO TONG UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this patent has the following problems: the corrosion potential of corroded steel bars can be improved by adding different rust inhibitors while removing chlorine, but it cannot solve the defects that may induce alkali-aggregate reaction or the inherent alkali-aggregate reaction in concrete components
However, this patent has the following problems: it only addresses the durability of concrete structures caused by chloride salt erosion, and does not involve the treatment of alkali-aggregate reactions that may be induced or inherent alkali-aggregate reactions in concrete components; and it cannot address different chloride salts Erosion and Aggregate Activity Levels of Concrete Members Adjusting Electrochemical Repair Parameters
However, the patent has the following problems: the addition of concrete admixtures in the early stage of construction can only prevent the occurrence of alkali aggregate reaction, and cannot treat the existing structure that has already undergone alkali aggregate reaction
[0006] According to the search of the prior art by the applicant, it is found that the existing electrochemical repair methods focus on improving the efficiency of chlorine removal and inhibiting the corrosion of steel bars, but do not propose or consider the process of electrochemical chlorine removal due to the alkaline, The alkali-aggregate reaction that may be caused by a large increase in temperature; at the same time, the existing technology mainly prevents the alkali-aggregate damage of concrete by adding admixtures in the early stage of construction, and does not propose a solution to the inherent alkali-aggregate damage in the existing structure Program

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrochemical repair method for dual deterioration of alkali aggregate damage and steel corrosion
  • Electrochemical repair method for dual deterioration of alkali aggregate damage and steel corrosion
  • Electrochemical repair method for dual deterioration of alkali aggregate damage and steel corrosion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] The present invention will be described in detail below in conjunction with specific embodiments. The following examples will help those skilled in the art to further understand the present invention, but do not limit the present invention in any form. It should be noted that those skilled in the art can make several modifications and improvements without departing from the concept of the present invention. These all belong to the protection scope of the present invention.

[0039] refer to figure 1 As shown, it is a schematic diagram of the state of the concrete electrochemical repair method for the double deterioration of alkali aggregate damage and steel corrosion for a preferred embodiment of the present invention. The repair method includes the following steps:

[0040] S1: Monitor the aggregate activity and chloride ion content of concrete specimen 1, and evaluate the degree of deterioration of different concrete specimen 1.

[0041] S2: Based on the assessed d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a concrete electrochemical repair method aimed at the dual deterioration of alkali aggregate damage and steel bar corrosion, comprising: monitoring the aggregate activity and chloride ion content of concrete specimens, and assessing the degree of deterioration of different concrete specimens; based on the assessed Determine the degree of deterioration of concrete specimens, and determine the best technical parameters for electrochemical repair; technical parameters include electrolyte concentration, current density, and electrification time; use lithium compound solution as electrolyte, and use the best technical parameters for electrochemical repair, the concrete specimens Electrochemical repair is carried out to suppress the inherent alkali-aggregate reaction of the existing structure and the alkali-aggregate reaction induced by the increase in alkalinity caused by the electrochemical reaction on the surface of the steel bar while removing chlorine. The present invention can set the optimal repair parameter group according to the concrete test pieces with different deterioration degrees in different environments, and improve the repair efficiency, so as to achieve the dual purposes of effectively preventing alkali aggregate damage and steel bar corrosion.

Description

technical field [0001] The invention relates to the field of electrochemical durability repair of concrete structures, in particular to a concrete electrochemical repair method aimed at double deterioration of alkali aggregate damage and steel bar corrosion. Background technique [0002] Chloride erosion and alkali-aggregate reaction (also known as alkali-silicon reaction, alkali-aggregate reaction) are important reasons for the decline in structural durability. Chloride corrosion will induce steel bar corrosion, and the hydroxide released by the cement matrix during the corrosion process will also cause or intensify the alkali aggregate reaction, resulting in durability damage to the existing structure; Microcracks will not only affect the mechanical properties of concrete, but also intensify the erosion of harmful media such as chloride ions and sulfate ions, thereby further aggravating the premature failure of service structures. The economic losses caused by the two can...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/65C04B41/72E04G23/02
CPCC04B41/65C04B41/72C04B41/50C04B41/5376E04G23/02C04B41/4535C04B41/4564
Inventor 刘清风毛丽璇胡志夏晋
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products