A kind of liquid polishing wax and preparation method thereof

A technology of polishing wax and liquid, which is applied in the direction of polishing compositions, chemical instruments and methods, and polishing compositions containing abrasives, etc., which can solve the problems of poor brightness and low polishing efficiency, and achieve improved polishing brightness and high polishing efficiency , Process environmental protection and pollution-free effect

Active Publication Date: 2021-06-29
徐州威聚电子材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently there are liquid polishing waxes on the market, but their common problems are: low polishing efficiency and poor brightness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A liquid polishing wax, comprising the following raw materials in parts by mass: 20 parts of silicon carbide, 5 parts of ferrate, 15 parts of palmitic acid, 5 parts of paraffin oil, 3 parts of rosin, 10 parts of fatty alcohol polyoxyethylene ether, 0.5 part of phosphoric acid .

[0022] Preparation steps of liquid polishing wax:

[0023] 1) Under the condition of rotating speed of 400-1000r / min, grind silicon carbide to a particle size of 100-150nm, and set aside;

[0024] 2) Under the condition of the rotation speed of 200-400r / min, the crushed rosin is granular and ready for use;

[0025] 3) Heating the paraffin oil in the above mass parts to 90-95°C, adding the above-mentioned mass of palmitic acid and the above-mentioned crushed rosin, stirring and melting at a speed of 100-150r / min, and mixing uniformly to obtain organic Liquid I;

[0026] 4) Cool the organic liquid I obtained above to 40-45°C, stir at a speed of 80-120r / min, add the above-mentioned parts by mas...

Embodiment 2

[0030] A liquid polishing wax, comprising the following raw materials in parts by mass: 25 parts of silicon carbide, 7.5 parts of ferrate, 25 parts of palmitic acid, 7.5 parts of paraffin oil, 5.5 parts of rosin, 15 parts of fatty alcohol polyoxyethylene ether, and 2 parts of phosphoric acid .

[0031] The preparation steps of the liquid polishing wax of this embodiment are exactly the same as that of Embodiment 1.

[0032] The liquid polishing wax obtained in this example was used to polish the iron sheet, the polishing pressure was set at 5.5 psi, the rotation speed of the bottom plate of the polishing machine was 60 RPM, the rotation speed of the upper plate was 60 RPM, and the polishing time was 15 minutes. The test results show that the surface roughness of the iron sheet is 0.006, smooth and bright in color.

Embodiment 3

[0034] A liquid polishing wax, comprising the following raw materials in parts by mass: 50 parts of silicon carbide, 10 parts of ferrate, 35 parts of palmitic acid, 10 parts of paraffin oil, 8 parts of rosin, 20 parts of fatty alcohol polyoxyethylene ether, and 3 parts of phosphoric acid .

[0035] The preparation steps of the liquid polishing wax of this embodiment are exactly the same as that of Embodiment 1.

[0036] The liquid polishing wax obtained in this example was used to polish the iron sheet, the polishing pressure was set to 5.5 psi, the rotation speed of the bottom plate of the polishing machine was 60 RPM, the rotation speed of the upper plate was 60 RPM, and the polishing time was 40 minutes. The test results show that the surface roughness of the iron sheet is 0.005, smooth and bright in color.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a liquid polishing wax, which comprises the following raw materials in parts by mass: 20-50 parts of silicon carbide, 5-10 parts of ferrate, 15-35 parts of palmitic acid, 5-10 parts of paraffin oil, and 3-8 parts of rosin 10-20 parts of fatty alcohol polyoxyethylene ether, 0.5-3 parts of phosphoric acid, and prepare liquid polishing wax. The invention can improve the polishing efficiency and has good polishing brightness; the preparation process is environment-friendly and pollution-free.

Description

technical field [0001] The invention relates to a liquid polishing wax and a preparation method thereof, belonging to the technical field of surface polishing wax. Background technique [0002] Polishing is one of the important processes in surface treatment. Polishing refers to the process of leveling the surface of an object with polishing materials, reducing roughness, and improving surface gloss and appearance quality. In the polishing process, solid polishing wax is generally used for polishing, but solid polishing wax will form residues on the stainless steel surface due to instantaneous high temperature and high pressure, and it is difficult to completely clean it even with wax removal water. Polishing wax gradually solid polishing wax. There are currently liquid polishing waxes on the market, but their common problems are: low polishing efficiency and poor brightness. Contents of the invention [0003] Aiming at the above-mentioned problems in the prior art, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09G1/02C09G1/08C23F3/06
CPCC09G1/02C09G1/08C23F3/06
Inventor 李炜王看看
Owner 徐州威聚电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com