A kind of recovery method of lithium iron phosphate positive plate with low energy consumption and low Al content

A technology for lithium iron phosphate and recovery methods, which is applied in the direction of chemical instruments and methods, positive electrodes, battery recovery, etc. It can solve the problems of unfavorable industrial application, high recovery energy consumption, and high calcination temperature, and achieve shortened calcination time and low energy consumption. , the effect of reducing the calcination temperature

Active Publication Date: 2022-02-18
HUAZHONG UNIV OF SCI & TECH
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method has high calcination temperature and long calcination time, so the recovery energy consumption is high, which is not conducive to industrial application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of recovery method of lithium iron phosphate positive plate with low energy consumption and low Al content
  • A kind of recovery method of lithium iron phosphate positive plate with low energy consumption and low Al content
  • A kind of recovery method of lithium iron phosphate positive plate with low energy consumption and low Al content

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A method for recovering lithium iron phosphate cathode sheet with low energy consumption and low Al content, comprising the following steps:

[0049] S1. Use a crusher to crush the lithium iron phosphate cathode sheet to be recovered into coarse particles, and control the particle size to about 5-10 mm to obtain a crushed material;

[0050] S2. Use a roller furnace to put a broken material in N 2 Calcining under the atmosphere, set the temperature of the holding zone to 450°C, the heating time is 2h, the holding time is 1h, and after cooling to below 95°C, it is released from the furnace to obtain the calcined material;

[0051] S3. Grinding the calcined material with a pulverizer into a powder with a particle size D50 between 50 and 80 μm to obtain a secondary crushed material;

[0052] S4. Classify the secondary crushed material with an airflow classifier, screen out the Al element therein, and obtain a lithium iron phosphate positive electrode material with a low Al...

Embodiment 2～6 and comparative example 1～7

[0055] Compared with Example 1, the recovery method of lithium iron phosphate positive electrode sheet provided by Examples 2-6 and Comparative Examples 1-7 with low energy consumption and low Al content is different in that the calcination temperature and time in step S2 are as shown in the table 1, and Comparative Examples 1 to 4 and Comparative Example 6 cancel the S3 step, and the others are substantially the same as in Embodiment 1, and will not be repeated here.

[0056] Preparation conditions and Al content of Table 1 Examples 1-6 and Comparative Examples 1-7

[0057]

[0058]

[0059] Table 2 Comparison of internal resistance of batteries with different Al impurity contents

[0060]

[0061] From Table 1 and Figure 3-4 It can be seen that when the calcination temperature of S2 is higher than 500°C, or the holding time of S2 exceeds 2h, the Al content of the product exceeds 200ppm, and with the increase of temperature, the Al content tends to increase. In ad...

Embodiment 7～9 and comparative example 8

[0064] Compared with Example 1, the recovery method of low energy consumption and low Al content of the lithium iron phosphate positive electrode sheet provided in Examples 7-9 and Comparative Example 8 is different in that the particle size of the first crush and the D50 of the second crush are shown in Table 3 , and others are substantially the same as those in Embodiment 1, and will not be repeated here.

[0065] Table 3 Preparation conditions and Al content of Examples 7-9 and Comparative Example 8

[0066] sample Particle size(mm) Secondary crushed material D50(μm) Al content / ppm Example 7 1～5 50～80 196 Example 8 10～15 50～80 174 Example 9 5～10 80～100 207 Comparative example 8 5～10 30～50 234

[0067] It can be seen from Table 3 that when the particle size of step S1 is between 1-15 mm, if the D50 of S3 exceeds 80 μm or is lower than 50 μm, the Al content of the obtained product will exceed 200 ppm. Only when the particle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a method for recovering lithium iron phosphate cathode sheets with low energy consumption and low Al content. In this method, firstly, the positive electrode sheet to be recovered is crushed into coarse particles with a crusher to obtain a crushed material with a particle size of 1-15mm; Cool out of the furnace to obtain calcined materials; then crush the calcined materials into powder with a pulverizer to obtain secondary crushed materials with a D50 of 50 μm to 80 μm; finally classify the secondary crushed materials with an airflow classifier to obtain positive electrode materials with an Al content of less than 200 ppm . The invention can separate and recover positive electrode materials from aluminum foil through primary crushing, calcination, secondary crushing and airflow classification. And in this process, through the control of process parameters such as the particle size of the primary particle, the calcination temperature and time, and the particle size of the secondary particle, the recovery of the positive electrode material with low energy consumption and low Al content can be realized.

Description

technical field [0001] The invention relates to the technical field of recycling lithium-ion waste batteries, in particular to a method for recycling lithium iron phosphate cathode sheets with low energy consumption and low Al content. Background technique [0002] In recent years, lithium-ion batteries have been widely used in automotive power batteries, energy storage power systems, and power tools, electric bicycles, electric motorcycles, military equipment, aerospace, 3C and other fields, and the number is very large. However, as the service life of lithium-ion batteries approaches, a large number of decommissioned and scrapped batteries will be produced. For the recovery of these decommissioned and scrapped lithium-ion batteries, fire or wet processes were mainly used to recover precious metals, such as Li and Co. However, this method not only has a low utilization rate of various materials in lithium-ion batteries, but also causes great pollution to the environment, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/54H01M4/58C01B25/45C01B25/37
CPCH01M10/54H01M4/5825C01B25/45C01B25/375Y02W30/84Y02E60/10H01M2004/028H01M4/1397H01M4/136H01M4/62H01M10/0525
Inventor 曹元成赵玉振肖益帆
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap