A kind of H-shaped steel roll ring and its manufacturing method

A technology of H-beam and roll ring, applied in the field of rolling steel, can solve the problems of bad influence on the surface quality of rolling steel, slag inclusion in the surface working layer, etc., and achieve the effect of increasing wear resistance and fine structure

Active Publication Date: 2022-03-22
成都三强轧辊股份有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for large-diameter H-shaped roll rings (such as Φ1600), the existing manufacturing process will cause slag inclusions in the surface working layer, which will adversely affect the surface quality of rolled steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 1. An H-shaped steel roll ring, comprising an outer layer of 7160kg and a core of 2140kg; wherein, the composition and mass fraction of the outer layer are: C: 1.83%, Si: 0.5%, Mn: 0.6%, P: 0.032%, S : 0.01%, Cr: 1.3%, Ni: 1.2%, the rest is Fe and unavoidable impurities; the composition and mass fraction of the core are: C: 1.15%, Si: 2.2%, Mn: 0.5%, P: 0.032 %, S: 0.012%, Cr: 0.1%, Ni: 0.3%, and the rest are Fe and unavoidable impurities.

[0036] 2. A manufacturing method of an H-shaped steel roll ring, comprising the following steps:

[0037] S1. Smelting the outer layer and the core respectively:

[0038] 1) Smelting the outer layer: using pig iron with a mass ratio of 17:50:33, recycled material and scrap steel as raw materials, smelting in a furnace, and adjusting the amount of additives according to the composition of the outer layer, and finally undergoing spheroidization and Inoculation treatment to obtain the outer layer of molten iron;

[0039] 2) Smelting...

Embodiment 2

[0047]1. An H-shaped steel roll ring, comprising an outer layer of 7160kg and a core of 2140kg; wherein, the composition and mass fraction of the outer layer are: C: 1.8%, Si: 0.51%, Mn: 0.5%, P: 0.03%, S : 0.012%, Cr: 1.2%, Ni: 1.0%, the rest is Fe and unavoidable impurities; the composition and mass fraction of the core are: C: 1.2%, Si: 2.3%, Mn: 0.6%, P: 0.03 %, S: 0.01%, Cr: 0.1%, Ni: 0.3%, and the rest are Fe and unavoidable impurities.

[0048] 2. A manufacturing method of an H-shaped steel roll ring, comprising the following steps:

[0049] S1. Smelting the outer layer and the core respectively:

[0050] 1) Smelting the outer layer: using pig iron with a mass ratio of 17:50:33, recycled material and scrap steel as raw materials, smelting in a furnace, and adjusting the amount of additives according to the composition of the outer layer, and finally undergoing spheroidization and Inoculation treatment to obtain the outer layer of molten iron;

[0051] 2) Smelting cor...

Embodiment 3

[0059] 1. An H-shaped steel roll ring, comprising an outer layer of 7160kg and a core of 2140kg; wherein, the composition and mass fraction of the outer layer are: C: 1.85%, Si: 0.6%, Mn: 1.0%, P: 0.035%, S : 0.03%, Cr: 1.9%, Ni: 1.7%, the rest is Fe and unavoidable impurities; the composition and mass fraction of the core are: C: 1.25%, Si: 2.4%, Mn: 0.6%, P: 0.035 %, S: 0.03%, Cr: 0.2%, Ni: 0.4%, and the rest are Fe and unavoidable impurities.

[0060] 2. A manufacturing method of an H-shaped steel roll ring, comprising the following steps:

[0061] S1. Smelting the outer layer and the core respectively:

[0062] 1) Smelting the outer layer: using pig iron with a mass ratio of 17:50:33, recycled material and scrap steel as raw materials, smelting in a furnace, and adjusting the amount of additives according to the composition of the outer layer, and finally undergoing spheroidization and Inoculation treatment to obtain the outer layer of molten iron;

[0063] 2) Smelting ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of steel rolling, and discloses an H-shaped steel roll ring, which includes an outer layer and a core; the composition and mass fraction of the outer layer are: C: 1.8-1.85%, Si: 0.5-0.6%, Mn: 0.5 ~1.0%, P≤0.035%, S≤0.03%, Cr: 1.2~1.9%, Ni: 1.0~1.7%, the rest is Fe and unavoidable impurities; the composition and mass fraction of the core are: C: 1.15~ 1.25%, Si: 2.2-2.4%, Mn: 0.5-0.6%, P≤0.035%, S≤0.03%, Cr≤0.2%, Ni: 0.3-0.4%, and the rest are Fe and unavoidable impurities; the present invention The preparation method of the H-shaped steel roll ring is also disclosed, including smelting, pouring and post-treatment; the invention pours the outer layer of molten iron in sections, and controls parameters such as pouring temperature, pouring speed and interval time between each pouring , to achieve the effect of eliminating slag inclusions in the surface working layer.

Description

technical field [0001] The invention relates to the technical field of rolling steel manufacturing, in particular to an H-shaped steel roll ring and a manufacturing method thereof. Background technique [0002] The roll ring is the main component of the H-beam universal rolling mill, and it is divided into two types: the horizontal roll ring and the vertical roll ring. At present, with the development of national high-speed rail and the deepening of enterprise transformation, the demand for channel steel, I-beam, angle steel, U-shaped steel, and bridge rails is increasing, and the demand for the number of roll rings for manufacturing steel is also gradually increasing. Normally, the working layer on the surface of the roll ring should have good wear resistance and red hardness, while the core should have high strength and good toughness. In order to achieve the above purpose, centrifugal composite technology is widely used in industry to produce composite roller rings compo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/56B22D19/16
CPCC22C38/02C22C38/04C22C38/56B22D19/16
Inventor 付家双杨德明程东
Owner 成都三强轧辊股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com