Preparation method of phase change ink

A technology of phase change ink and phase change microcapsules, applied in the directions of ink, chemical instruments and methods, heat exchange materials, etc., can solve the problems of weak adhesion, poor temperature control ability of phase change ink, etc., and save energy. , Improve the effect of heat preservation and cooling effect

Active Publication Date: 2020-12-22
高邮鑫润龙印刷科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a preparation method of phase change ink, which solves the problems of poor temperature control ability and weak adhesion of existing phase change ink

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of phase change ink
  • Preparation method of phase change ink
  • Preparation method of phase change ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Preparation of phase change microcapsules:

[0030] (1-1) Preparation of styrene maleic anhydride copolymer sodium salt (SMAHNa) emulsifier: 15g of SMA powder, 4.2g of sodium hydroxide and 130.6g of deionized water were added to a three-necked round-bottomed flask and placed in a constant temperature water bath Stir mechanically at 50° C. for 5 h to obtain a styrene-maleic anhydride copolymer sodium salt emulsifier (SMAHNa emulsifier) ​​with a mass fraction of 10%, which is put in a beaker for subsequent use;

[0031] (1-2) Preparation of core material: Add 10g of SMAHNa emulsifier, 12g of n-octadecane and 100ml of deionized water into another three-neck round bottom flask, melt it in a water bath at a temperature of 70°C, and then rotate at 900rpm Emulsify for 2 hours under the condition of / min to obtain a stable O / W emulsion, keep the O / W emulsion in a stirring state for use;

[0032] (1-3) Preparation of resin aqueous solution: put 9g of gelatin in room tempera...

Embodiment 2

[0036] (1) Preparation of phase change microcapsules:

[0037] (1-1) Preparation of styrene-maleic anhydride copolymer sodium salt (SMAHNa) emulsifier: 18g of SMA powder, 5g of sodium hydroxide and 133g of deionized water were added to a three-necked round-bottomed flask and placed in a constant temperature water bath at 45°C Under mechanical stirring for 4h, the styrene-maleic anhydride copolymer sodium salt emulsifier (SMAHNa emulsifier) ​​with a mass fraction of 10% was obtained, which was put in a beaker for subsequent use;

[0038] (1-2) Preparation of core material: Add 13g of SMAHNa emulsifier, 10g of liquid paraffin and 100ml of deionized water into another three-neck round bottom flask, melt it in a water bath at a temperature of 60°C, and then rotate at 500rpm / min Under emulsification for 2.2 hours, a stable O / W emulsion was obtained, and the O / W emulsion was kept under stirring for use;

[0039] (1-3) Preparation of resin aqueous solution: put 8.4g of gelatin in ro...

Embodiment 3

[0043] (1) Preparation of phase change microcapsules:

[0044] (1-1) Preparation of styrene-maleic anhydride copolymer sodium salt (SMAHNa) emulsifier: 14g of SMA powder, 4g of sodium hydroxide and 128g of deionized water were added to a three-neck round-bottomed flask and placed in a constant temperature water bath at 55°C Under mechanical stirring for 5.5 hours, the styrene-maleic anhydride copolymer sodium salt emulsifier with a mass fraction of 10% was obtained, which was put in a beaker for subsequent use;

[0045] (1-2) Preparation of core material: Add 9g of SMAHNa emulsifier, 11g of n-eicosane and 100ml of deionized water into another three-necked round-bottomed flask, melt at a water bath temperature of 80°C, and then rotate at 550rpm / Emulsify for 2.2 hours under the condition of min to obtain a stable O / W emulsion, keep the O / W emulsion in a stirring state for use;

[0046] (1-3) Preparation of resin aqueous solution: put 10g of gelatin in normal temperature water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of phase-change ink, belonging to the technical field of ink preparation. The preparation method comprises the steps of preparing phase-change microcapsules, preparing the phase-change ink and the like. The phase-change microcapsule ink prepared by using the method is a new material which takes a high-molecular polymer as a shell and contains a phase-change material inside; the phase-change ink has excellent phase-change latent heat, and the temperature control effect of a microcapsule can be brought into full play; and the phase-change ink can release or absorb heat in a surrounding environment to achieve the effects of recycling energy and saving energy of a product, so the function of the ink is broadened, and the ink can play more roles in various fields.

Description

technical field [0001] The invention relates to the technical field of ink preparation, in particular to a preparation method of phase change ink. Background technique [0002] There are many types of inks, but most inks mainly play the role of transmitting information and beautifying patterns, while microcapsule inks not only have the role of information transmission, but also have specific functions. For example, thermal expansion (foaming) ink, its function is to realize the three-dimensional sense and velvet touch, but the three-dimensional control effect of this ink is still closely related to information transmission and patterning. [0003] At present, phase change microcapsules embedded with phase change materials have attracted more and more attention as a new green material with high efficiency and energy saving. The function of phase change microcapsules is mainly reflected in the ability to absorb or release heat as the ambient temperature changes to maintain th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/107C09D11/102C09D11/106C09D11/03C09K5/06
CPCC09D11/107C09D11/102C09D11/106C09D11/03C09K5/06
Inventor 孙志成王红明吉顺华李芙蓉李忠东
Owner 高邮鑫润龙印刷科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com