A technology of green sand and acid consumption value, which is applied in the field of green sand regeneration and recycling technology, can solve the problems that can not be produced by casting self-hardening sand and coated sand, and the acid consumption value of recycled sand is high.

Inactive Publication Date: 2020-12-15
重庆长江造型材料常州有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a green mold sand regeneration and recycling process with controllable acid consumption, so as to solve the problem that the regenerated sand acid consumption is too high and cannot be used for casting self-hardening sand and coated sand. production problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] This embodiment provides a green mold sand recycling process with controllable acid consumption, which specifically includes the following steps:

[0024] S1. Collect the green mold sand waste sand. During the collection process, the dust in the green mold sand waste sand is adsorbed and collected by the air blowing equipment;

[0025] S2. Cutting and pulverizing the green mold sand waste sand processed in step S1, conveying the cut and pulverized green mold sand waste sand through a cyclone separator after the pulverization treatment, and collecting a small amount of green mold sand waste sand through a magnetic core Metal residue, so as to realize the separation of a small amount of separated metal residue and green sand mixture; then the separated metal residue is sent to step S8, and the separated green sand is sent to step S2;

[0026] S3, then carry out sieving process to the green molding sand after step S2 processing;

[0027] S4. Take the total weight of the s...

Embodiment 2

[0040] This embodiment provides a green mold sand recycling process with controllable acid consumption, which specifically includes the following steps:

[0041] S1. Collect the green mold sand waste sand. During the collection process, the dust in the green mold sand waste sand is adsorbed and collected by the air blowing equipment;

[0042] S2. Cutting and pulverizing the green mold sand waste sand processed in step S1, conveying the cut and pulverized green mold sand waste sand through a cyclone separator after the pulverization treatment, and collecting a small amount of green mold sand waste sand through a magnetic core Metal residue, so as to realize the separation of a small amount of separated metal residue and green sand mixture; then the separated metal residue is sent to step S8, and the separated green sand is sent to step S2;

[0043] S3, then carry out sieving process to the green molding sand after step S2 processing;

[0044] S9, performing a secondary grindin...

Embodiment 3

[0052] This embodiment provides a green mold sand recycling process with controllable acid consumption, which specifically includes the following steps:

[0053] S1. Collect the green mold sand waste sand. During the collection process, the dust in the green mold sand waste sand is adsorbed and collected by the air blowing equipment;

[0054] S2. Cutting and pulverizing the green mold sand waste sand processed in step S1, conveying the cut and pulverized green mold sand waste sand through a cyclone separator after the pulverization treatment, and collecting a small amount of green mold sand waste sand through a magnetic core metal residue, so as to realize the separation of a small amount of separated metal residue and green sand mixture; then the separated metal residue is sent to step S8, and the separated green sand is sent to step S2;

[0055] S3, then carry out sieving process to the green molding sand after step S2 processing;

[0056] S4. Take the total weight of the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a green sand regeneration and cyclic utilization process with a controllable acid demand value. The process comprises the following steps of collecting waste green sand, cutting and grinding the treated waste green sand, conveying the cut and ground waste green sand by a cyclone separator after grinding, collecting a small amount of metal residues in the waste green sand bya magnetic core, then collecting and smelting the small amount of metal residues, and sieving the green sand obtained through separation; weighing the total weight of the sieved green sand, weighingthe weight of brown fused alumina abrasives according to the obtained total weight of the green sand, and adding the brown fused alumina abrasives into the weighed waste green sand; putting a mixtureof the ground waste green sand and the brown fused alumina abrasives into a roasting furnace to be subjected to fluidized bed roasting; then cooling; and separating the waste green sand from the brownfused alumina abrasives to obtain a green sand reclaimed material. Therefore, the controllable acid demand value is realized by changing the content ratio of the brown fused alumina abrasives to thewaste green sand, so that resource waste is avoided.

Description

technical field [0001] The invention relates to the technical field of green mold sand recovery, in particular to a green mold sand recycling process with controllable acid consumption. Background technique [0002] Green sand is also called green sand. In foundry production, the sand mixture uses bentonite as a binder, then mixes with water and other additives, and then it can be used for molding and making cores. The sand mold (core) can be poured directly without drying. In the foundry industry, this kind of sand is called green mold sand. At present, the green sand molding process has been widely used in the auto parts production industry, but green sand will become foundry waste sand after repeated use in the system. Direct disposal of waste sand will easily cause environmental pollution, and a large amount of waste sand The generation of green mold sand also increases the production cost virtually, so green mold sand waste sand needs to be recycled, but at present, it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C5/10B22C5/06B22C5/04B22C5/00
CPCB22C5/00B22C5/04B22C5/06B22C5/10
Inventor 吴长松
Owner 重庆长江造型材料常州有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap