Waste aluminum recycling and direct forming device and method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of aluminum recycling and direct technology, applied in the direction of workpiece cooling device, workpiece surface treatment equipment, coating, etc., can solve the problem of non-implementation, and achieve the effect of reducing cost, improving interface bonding strength, and reasonable equipment structure design
Active Publication Date: 2020-11-24
ZHONGBEI UNIV
View PDF10 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] At present, research on the reuse of aluminum scrap composite panels for mass production has not yet been realized.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0032] In order to make the technical problems, technical solutions and beneficial effects to be solved by the present invention clearer, the present invention will be further described below in conjunction with the accompanying drawings and embodiments.
[0033] Such as figure 1 As shown, a waste aluminum recycling direct forming device includes a conveying device 1, a heating system 2, a melting furnace I3, a temperature regulating device I4, a composite material stirring device 5, a temperature regulating device II6, a melting furnace II7 and a twin-roll rolling device 8; Heating system 2, melting furnace I3, temperature regulating device I4, composite material stirring device 5, temperature regulating device II6, melting furnace II7, and twin-roll rolling device 8 are all placed around the conveying device 1.
[0034] Such as figure 2 As shown, the heating system 2 includes a laser 201, a focusing mirror 202, a temperature sensor 203 and a distance sensor 204, and the fo...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a waste aluminum recycling and direct forming device and method. The waste aluminum recycling and direct forming device comprises an induction heating system, smelting furnaces, temperature adjusting devices, a composite material stirring device, a conveying device and a double-roller rolling device, wherein the heating system, the smelting furnace I, the temperature adjusting device I, the composite material stirring device, the temperature adjusting device II, the smelting furnace II and the double-roller rolling device are all arranged around the conveying device, atreated stainless steel plate is conveyed into the heating system, heated and slightly melted and then conveyed to the smelting furnace, molten waste aluminum is sprayed to the steel plate, temperature measurement and temperature adjustment are carried out, strengthening particles are sprayed to the surface of the waste aluminum, secondary temperature measurement and temperature adjustment are carried out, the surfaces of the strengthening particles are covered with molten aluminum, the strengthening particles are sent into double rollers, rolling forming is carried out to obtain a steel / aluminum / strengthening particle / aluminum wavy composite plate, and laser shock is carried out on the surface of the steel / aluminum / strengthening particle / aluminum wavy composite plate. The wavy compositeplate is directly machined and formed from waste aluminum, the problems of high cost, difficulty in operation, complex structure and the like are solved, the yield is high, the production efficiency and the qualified rate of products are favorably improved, continuous production can be realized, and the wavy composite plate has the advantages of energy conservation and environmental protection.
Description
technical field [0001] The invention belongs to the technical field of plastic processing of metal layered composite materials, and in particular relates to a waste aluminum recycling direct forming device and method. Background technique [0002] With the development of science and technology, the mechanical properties of single-element metal materials have been difficult to meet the needs of work. The development and development of multi-metal composite materials with excellent properties of dissimilar metals has become the main direction of new material production. Metal composite panels are for two It is a plate made of layered combination of two or more dissimilar metals with different physical and chemical properties. Through scientific selection of metal components and reasonable design of processing technology, it can give full play to the performance advantages of different metals. , so that it has a comprehensive performance that no metal component can possess. Now...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.