Low-temperature once-fired ceramic with opacified glaze and preparation method thereof

Abstract

The invention relates to the field of ceramic products and production methods thereof, and specifically relates to a low-temperature once-fired ceramic with opacified glaze and a preparation method. The bottom glaze layer is characterized by comprising the following raw materials in parts by weight: 5-6 parts of industrial iron oxide, 5-10 parts of wood ash, 3-5 parts of flint, 10-12 parts of quartz and 10-15 parts of orthoclase. The surface glaze layer is prepared from the following raw materials in parts by weight: 10 to 15 parts of fused powder, 15 to 18 parts of quartz, 10 to 15 parts of feldspar, 21 to 25 parts of albite, 2 to 3 parts of calcined talc, 8 to 10 parts of calcite, 2 to 3 parts of zircon and 1 to 2 parts of zinc oxide. According to the low-temperature once-fired ceramic with opacified glaze and the preparation method provided by the invention, the firing temperature is reduced, the opacified effect is good, the glaze form is rich, the fuel is effectively saved, the adaptability of the blank glaze is good, and the strength and hardness of the blank glaze are high.

Description

technical field [0001] The invention relates to the field of ceramic products and production methods thereof, in particular to a low-temperature primary-fired ceramic with an opaque glaze surface and a preparation method thereof. Background technique [0002] With the energy crisis and the gradual depletion of fossil fuels, my country's economic development will face a crisis, so people pay more and more attention to low temperature technology. In the field of ceramic production, traditional ceramic firing generally adopts high-temperature firing (firing temperature above 1200 degrees Celsius), which consumes a lot of fuel, and the burning cost accounts for more than 30% of the ceramic production cost. Firing not only increases the production cost, but also brings great pressure to the environment. With the transformation of the national industry, the replacement of ceramic technology in the ceramic industry is also imminent. Disclosed is a low-temperature once-fired cerami...

AI Technical Summary

Problems solved by technology

[0003] Although the low-temperature once-fired ceramic products and manufacturing process disclosed in the above invention patent application can reduce the temperature in the firing process, the potassium feldspar powder and albite powder need to be calcined at a medium and high temperature at 1300°C in the raw material calcination process, which adds an additional Fuel cost, in addition, in order to reduce the firing temperature, reduce SiO 2 and Al 2 o 3 If the content is too high, it will lead to defects such as poor fluidity of the glaze, low hardness, pinholes on the glaze surface, etc.

[0004] In addition, the oxides of tin, zirconium and titanium in the existing opacifying glaze formulations are often used as opacifying agents. Among them, tin oxide and titanium oxide have good opacifying effect, but the raw material cost is high, while zirconia raw material cost is cheap, but opacifying The effect is not good. In view of this, the case arises from the