Preparation method of SrTiO3/SrSO4/Pt double-heterojunction nano material

A nanomaterial and double heterojunction technology, applied in catalyst activation/preparation, chemical instruments and methods, hydrogen production, etc. Low site and other issues, to achieve the effect of simple operation, cost-friendly and environment-friendly, process controllable

Active Publication Date: 2020-11-10
HEFEI UNIV OF TECH
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to: provide a kind of SrTiO 3 / SrSO 4 The preparation method of / Pt double heterojunction nanomaterials mainly solves the technical problem of improving the high photoelectron-hole recombination rate and the small specific surface area of ​​the current strontium titanate material in the application of photo-splitting water to hydrogen production technology. The problem of low point and low efficiency of hydrogen production by photolysis of water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of SrTiO3/SrSO4/Pt double-heterojunction nano material
  • Preparation method of SrTiO3/SrSO4/Pt double-heterojunction nano material
  • Preparation method of SrTiO3/SrSO4/Pt double-heterojunction nano material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A SrTiO 3 / SrSO 4 / Pt double heterojunction nanomaterial preparation method, the specific steps are as follows:

[0035] (1) First configure A solution, dissolve 10mmol cysteine ​​in 5ml deionized water, ultrasonically disperse in deionized water, stir vigorously on a magnetic stirrer for five minutes, then add 15mmol strontium nitrate, and then vigorously stir on a magnetic stirrer Stir until the liquid is clear without precipitates, and A solution is obtained.

[0036] (2) Then configure B solution, dissolve 2ml of glacial acetic acid in 40ml of absolute ethanol (AR, 99.5%) and stir for five minutes, then pour into a beaker filled with 10mmol TBT and continue stirring to obtain B solution.

[0037](3) Preparation of precursor solution: Add solution A dropwise during the stirring process of solution B. During the addition process, flocculent precipitates will gradually be found, and continue to stir vigorously for two hours to prepare a precursor solution.

[0038] ...

Embodiment 2

[0046] A SrTiO 3 / SrSO 4 / Pt double heterojunction nanomaterial preparation method, the specific steps are as follows:

[0047] (1) First configure A solution, dissolve 10mmol cysteine ​​in 5ml deionized water, ultrasonically disperse in deionized water, stir vigorously on a magnetic stirrer for five minutes, then add 20mmol strontium nitrate, and then vigorously stir on a magnetic stirrer Stir until the liquid is clear and free of sediment.

[0048] (2) Then configure solution B, dissolve 2ml of glacial acetic acid in 40ml of absolute ethanol (AR, 99.5%) and stir for five minutes, then pour into a beaker filled with 10mmol TBT and continue stirring. A solution of B was obtained.

[0049] (3) Preparation of the precursor: Add the A solution prepared in step (1) dropwise during the stirring process of the B solution. During the addition process, the generation of flocculent precipitates will gradually be found, and continue to stir vigorously for two hours to form a precurso...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a SrTiO3 / SrSO4 / Pt double-heterojunction nano material. The preparation method comprises the following specific steps: preparing deionized water, glacialacetic acid and absolute ethyl alcohol as solvents and preparing strontium nitrate and tetrabutyl titanate respectively as a strontium source and a titanium source, wherein the added cysteine not only serves as a chelating agent, but also serves as a sulfur source; then preparing a precursor by adopting a sol-gel method, drying theprecursor in a drying box at low temperature for 48 hours, grinding the precursor, and annealing the precursor in a muffle furnace to obtain composite powder of strontium titanate and strontium sulfate; and finally, depositing a layer of platinum on the surface through a photodeposition method to form as a cocatalyst, and thereby the SrTiO3 / SrSO4 / Pt double-heterojunction nano material is obtained. The SrTiO3 / SrSO4 / Pt double-heterojunction nano material disclosedby the invention has a porous structure and a relatively large specific surface area, and can provide more active sites for a photocatalytic reaction; besides, the SrTiO3 / SrSO4 / Pt has very high activity on the precipitation of H2 under the illumination. The nano-material shows great development prospect in the field of photocatalysis.

Description

technical field [0001] The invention belongs to the field of photocatalysts, in particular to a SrTiO 3 / SrSO 4 / Pt double heterojunction nanomaterials preparation method. Background technique [0002] SrTiO 3 It has adjustable band structure and proper bandgap width (3.4eV). It can be used for photocatalytic water splitting and photoreduction of carbon dioxide to produce fuel. At the same time, it has the advantages of low cost and environmental friendliness. SrTiO 3 It is a perovskite-type material with great potential for photocatalytic conversion of renewable energy. But SrTiO 3 The main factor limiting the development in the field of photocatalysis is the easy recombination of photogenerated electrons and holes. There are many ways to suppress the recombination of photogenerated electrons and holes, including the deposition of ion-doped metals or nonmetals and noble metals. Combining two semiconductors with different conduction band and valence band positions t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J27/053B01J35/00B01J35/10B01J37/08B01J37/03B01J37/16B01J37/34C01B3/04
CPCB01J37/036B01J37/344B01J37/16B01J37/0018B01J27/053C01B3/042B01J35/393B01J35/396B01J35/60B01J35/39Y02E60/36
Inventor 张勇蔡婧怡吴玉程张雪茹崔接武王岩秦永强舒霞
Owner HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com