Polycarbonate material as well as preparation method and application thereof

A polycarbonate and hyperbranched polyester technology, applied in the field of polymer materials, can solve the problems of poor impact toughness of materials, and achieve the effects of improving high and low temperature impact toughness, improving gloss retention rate and increasing dispersibility

Active Publication Date: 2020-09-01
SHANGHAI ZHONGLEI NEW MATERIAL SCI CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

By adding a large amount of high-hardness PMMA resin to the PC matrix to improve its surface scratch resistance, but this will lead to poor impact toughness of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polycarbonate material as well as preparation method and application thereof
  • Polycarbonate material as well as preparation method and application thereof
  • Polycarbonate material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] This embodiment provides a high-gloss black scratch-resistant polycarbonate material, which includes the following components by weight:

[0074]

[0075] The components in the above formula are uniformly mixed with a high-speed mixer for 8 minutes, and then the mixture is added to the twin-screw extruder for melt blending. The working parameters of the extruder are as follows: the temperature in the first zone is 250℃, and the temperature in the second zone is 260℃, the temperature in zone three is 270℃, zone four is 270℃, zone five is 270℃, zone six is ​​270℃, zone seven is 270℃, zone eight is 270℃, zone nine is 270 ℃, the temperature in the ten zones is 270℃, the temperature in the eleven zones is 265℃, the screw speed is 500 rpm, and the residence time is 2 min. After extrusion, it is cooled, dried, and pelletized to obtain the high-gloss black scratch-resistant polymer Carbonate material.

[0076] Wherein, the preparation method of the modified nano oxide includes the ...

Embodiment 2

[0082] This embodiment provides a high-gloss black scratch-resistant polycarbonate material, which includes the following components by weight:

[0083] Component Weight parts / parts PC (Mitsubishi, M7026U)99 Modified nano oxide1 Toner 0.5

[0084] The components in the above formula are uniformly mixed with a high-speed mixer for 10 minutes, and then the mixture is added to the twin-screw extruder for melt blending. The working parameters of the extruder are as follows: the temperature in the first zone is 230℃, and the temperature in the second zone is 240℃, the temperature in zone three is 250℃, zone four is 250℃, zone five is 250℃, zone six is ​​250℃, zone seven is 250℃, zone eight is 250℃, zone nine is 250 ℃, temperature in ten zones is 250℃, temperature in eleven zones is 245℃, screw speed is 350 rpm, residence time is 3 min, cooling, drying and pelletizing after extrusion to obtain the high-gloss black scratch-resistant polycarbonate Ester material.

[0085] Wherein, t...

Embodiment 3

[0091] This embodiment provides a high-gloss black scratch-resistant polycarbonate material, which includes the following components by weight:

[0092]

[0093] The components in the above formula are uniformly mixed with a high-speed mixer for 5 minutes, and then the mixture is added to the twin-screw extruder for melt blending. The working parameters of the extruder are as follows: the temperature in the first zone is 270℃, and the temperature in the second zone is 280℃, the temperature in zone three is 290℃, zone four is 290℃, zone five is 290℃, zone six is ​​290℃, zone seven is 290℃, zone eight is 290℃, zone nine is 290 ℃, the temperature in the ten zones is 290℃, the temperature in the eleven zones is 285℃, the screw speed is 850 revolutions / min, the residence time is 1 min, cooling, drying, and pelletizing after extrusion to obtain the high-gloss black scratch-resistant polycarbonate Ester material.

[0094] Wherein, the preparation method of the modified nano oxide include...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a polycarbonate material as well as a preparation method and application thereof. The polycarbonate material is prepared from the following components in parts by weight: 80 to99 parts of polycarbonate and 0.1 to 15 parts of a modified nano oxide. Wherein the modified nano oxide is modified by a coupling agent, a hyperbranched polyester and a rare earth ion together; the modified nano oxide has good dispersibility in a polycarbonate matrix material, not only can the scratch resistance and tensile strength of the polycarbonate material be improved, but also the influenceof the modified nano oxide on the impact toughness, blackness and surface gloss of the obtained material is small through a reasonable proportion and a scientific preparation method. The polycarbonate material provided by the invention is relatively good in scratch resistance, high in gloss retention rate, relatively good in tensile strength, and relatively excellent in physical properties such as surface gloss, blackness and impact toughness.

Description

Technical field [0001] The invention belongs to the field of polymer materials, and specifically relates to a polycarbonate material and a preparation method and application thereof, and in particular to a high-gloss black scratch-resistant PC material, and a preparation method and application thereof. Background technique [0002] Polycarbonate (PC) is an aromatic polymer containing carbonate groups in the molecular chain. It is an excellent engineering plastic with good comprehensive properties, high mechanical strength, good impact resistance, dimensional stability, and light transmission. With good heat resistance and electrical insulation, it is widely used in machinery, automobiles, electrical appliances and other industries. [0003] However, when applied to the interior and exterior of automobiles (such as dashboard decoration panels, heat dissipation grilles, etc.), communication equipment (such as smart phone casings, wireless network card casings, etc.), secondary proces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L51/00C08K13/06C08K9/06C08K9/04C08K3/36C08K5/134
CPCC08K13/06C08K9/06C08K9/08C08K9/04C08K3/36C08K5/1345C08L69/00C08K2201/011C08L51/003
Inventor 刘春艳
Owner SHANGHAI ZHONGLEI NEW MATERIAL SCI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka