Quick-drying silver paste for large keyboard conductive film circuit, and preparation method thereof

A technology of conductive film and circuit, which is applied in the direction of circuits, printed circuits, printed circuit components, etc., can solve the problems of long drying and curing time, and achieve the effects of accelerated shrinkage drying, fast curing, and stable structure

Active Publication Date: 2020-08-07
上海玖银电子科技有限公司
View PDF14 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The large keyboard conductive film circuit is made of silver paste through screen printing. Due to the long drying and curing time of the existing silver paste, it needs to go through two drying and curing processes, that is, after the film line is pre-dried by IR oven, It needs to be baked in an oven before entering the subsequent process. According to statistics, the per capita monthly production capacity of each factory is 10,000 sets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick-drying silver paste for large keyboard conductive film circuit, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A quick-drying silver paste for a large keyboard conductive film circuit, comprising the following components in parts by mass: 52 parts of metallic silver powder, 6 parts of polymer resin, 1 part of auxiliary agent, and 30 parts of solvent;

[0020] Among them, the metal silver powder is a mixture of flaky silver powder and nano-silver powder, and the components in the metal silver powder are composed of 80 parts of flaky silver powder and 10 parts of nano-silver powder, wherein the average particle size of the flaky silver powder is 5-10 μm , The average particle size of nano silver powder is 20-80nm. The polymer resin is vinyl resin. The auxiliary agent includes nano-oxide and dispersant, wherein the weight ratio of nano-oxide and dispersant is 3:1, and the nano-oxide used is a mixture of silicon oxide, lithium oxide and magnesium oxide with a mass ratio of 3:2:2 , the dispersant used is a commercially available hyperdispersant. The solvent is a dibasic acid ester....

Embodiment 2

[0026] A quick-drying silver paste for a large keyboard conductive film circuit, comprising the following components by mass: 45 parts of metallic silver powder, 5 parts of polymer resin, 0.5 parts of additives, and 32 parts of solvent;

[0027] Among them, the metal silver powder is a mixture of flaky silver powder and nano-silver powder, and the components in the metal silver powder are composed of 84 parts of flaky silver powder and 6 parts of nano-silver powder, wherein the average particle size of the flaky silver powder is 5-10 μm , The average particle size of nano silver powder is 20-80nm. The polymer resin is vinyl resin. The auxiliary agent includes nano-oxide and dispersant, wherein the weight ratio of nano-oxide and dispersant is 7:1, and the nano-oxide used is a mixture of silicon oxide, lithium oxide and magnesium oxide with a mass ratio of 4:2:2 , the dispersant used is a commercially available hyperdispersant. The solvent is a dibasic acid ester.

[0028] Fo...

Embodiment 3

[0030] A quick-drying silver paste for a large keyboard conductive film circuit, comprising the following components in parts by mass: 60 parts of metallic silver powder, 10 parts of polymer resin, 3 parts of additives, and 40 parts of solvent;

[0031] Among them, the metal silver powder is a mixture of flaky silver powder and nano-silver powder, and the components in the metal silver powder are composed of 87 parts of flaky silver powder and 4 parts of nano-silver powder, wherein the average particle size of the flaky silver powder is 5-10 μm , The average particle size of nano silver powder is 20-80nm. The polymer resin is vinyl resin. The auxiliary agent includes nano-oxide and dispersant, wherein the weight ratio of nano-oxide and dispersant is 1:1, and the nano-oxide used is a mixture of silicon oxide, magnesium oxide and bismuth oxide with a mass ratio of 1:1:1 , the dispersant used is a commercially available hyperdispersant. The solvent is a dibasic acid ester.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses quick-drying silver paste for a large keyboard conductive film circuit. The quick-drying silver paste is prepared from, by mass, 45-65 parts of metal silver powder, 5-10 partsof a macromolecule resin, 0-5 parts of an auxiliary agent and 30-40 parts of a solvent, wherein the metal silver powder is a mixture of flaky silver powder and nano silver powder, the metal silver powder is prepared from the following components in parts by mass: 80 to 90 parts of flaky silver powder and 5 to 10 parts of nano silver powder, the average particle size of the flaky silver powder is 5to 10 microns, the average particle size of the nano silver powder is 20 to 80 nm, and the macromolecular resin is an ethylene resin. The quick-drying silver paste can be quickly cured, is wide in base material application range and good in conductivity, can meet the full-automatic production process of customers, and achieves the purposes of reducing the labor cost and improving the product competitiveness.

Description

technical field [0001] The invention relates to the technical field of conductive paste, in particular to a quick-drying silver paste for a large keyboard conductive film circuit and a preparation method thereof. Background technique [0002] The large keyboard conductive film circuit is made of silver paste through screen printing. Due to the long drying and curing time of the existing silver paste, it needs to go through two drying and curing processes, that is, after the film line is pre-dried by IR oven, It needs to be baked in an oven before entering the subsequent process. According to statistics, the per capita monthly production capacity of each factory is 10,000 sets. In order to improve the production effect, the factory adopts the automatic printing process and the back-end process also adopts the fully automatic process, and requires only one pass through the IR baking process to complete the baking process of the film route products made of silver paste, which r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H05K1/09H01B1/22H01B13/00
CPCH01B1/22H01B13/00H05K1/092
Inventor 丰勇柳嘉凯
Owner 上海玖银电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products