Inflaming-retarding fabric and preparation method thereof

A flame retardant, fabric technology, applied in the direction of textile, yarn, fabric, etc., can solve the problem that the flame retardant effect of flame retardant textile fabric can not meet the requirements of use, poor softness, etc., to enhance strength and toughness, improve flame retardancy, The effect of good comfort

Pending Publication Date: 2020-07-17
JIANGXI INST OF FASHION TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, the technical problem to be solved by the present invention is to overcome the defects of the flame-retardant textile fabrics in the prior art that the flame-retardant effect cannot meet the use requirements and the softness is poor, so as to provide a flame-retardant fabric and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inflaming-retarding fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment provides a flame-retardant fabric and a preparation method thereof. The flame-retardant fabric includes a fabric substrate and a flame-retardant coating coated on the surface of the fabric substrate;

[0047] Fabric matrix includes warp and weft; warp raw materials include 1kg polyacrylonitrile fiber, 4kg modal fiber and 5kg chitin fiber; weft raw material includes 2kg stainless steel fiber, 4kg polybendazole fiber and 4kg polylactic acid fiber;

[0048]The raw materials of flame retardant coating include 10kg polybutadiene epoxy resin, 5kg polyparaphenylene terephthalamide, 4kg polymethacrylate, 5kg modified polysiloxane X-200, 4kg γ-aminopropyl Triethoxysilane, 6kg 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 3kg polyether (ethylene oxide / propylene oxide block copolymer) and 4kg Wood fiber powder.

[0049] The preparation method of the above-mentioned flame-retardant fabric includes,

[0050] Install the warp and weft in the weaving machine re...

Embodiment 2

[0056] This embodiment provides a flame-retardant fabric and a preparation method thereof. The flame-retardant fabric includes a fabric substrate and a flame-retardant coating coated on the surface of the fabric substrate;

[0057] Fabric matrix includes warp and weft; warp raw materials include 1kg polyacrylonitrile fiber, 3kg modal fiber and 6kg chitin fiber; weft raw material includes 1.5kg stainless steel fiber, 4.5kg polybendazole fiber and 4kg polylactic acid fiber;

[0058] The raw materials of flame retardant coating include 20kg polybutadiene epoxy resin, 15kg polyparaphenylene terephthalamide, 10kg polymethacrylate, 15kg modified polysiloxane X-200, 10kg γ-aminopropyl Triethoxysilane, 10kg 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 9kg polyether (ethylene oxide / propylene oxide block copolymer) and 10kg Wood fiber powder.

[0059] The preparation method of the above-mentioned flame-retardant fabric includes,

[0060] Install the warp and weft in the weaving...

Embodiment 3

[0066] This embodiment provides a flame-retardant fabric and a preparation method thereof. The flame-retardant fabric includes a fabric substrate and a flame-retardant coating coated on the surface of the fabric substrate;

[0067] Fabric matrix includes warp and weft; warp raw materials include 1kg polyacrylonitrile fiber, 4kg modal fiber and 5kg chitin fiber; weft raw material includes 2kg stainless steel fiber, 4kg polybendazole fiber and 4kg polylactic acid fiber;

[0068] The raw materials of the flame retardant coating include 12kg polybutadiene epoxy resin, 6kg polyparaphenylene terephthalamide, 5kg polymethacrylate, 7kg modified polysiloxane X-200, 6kg γ-aminopropyl Triethoxysilane, 7kg 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 4kg polyether (ethylene oxide / propylene oxide block copolymer) and 5kg Wood fiber powder.

[0069] The preparation method of the above-mentioned flame-retardant fabric includes,

[0070] Install the warp and weft in the weaving machi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of textile fabric preparation, and particularly relates to an inflaming-retarding fabric and a preparation method thereof. The fabric comprises a fabric base and an inflaming-retarding coating smeared on the surface of the fabric base. The fabric base comprises first yarn and second yarn. The first yarn is made from polyacrylonitrile fibers, chitin fibers and modal fibers. The second yarn is made from polybenzimidazole fibers, polylactic acid fibers and stainless steel fibers. The inflaming-retarding fabric can achieve good comfort, air permeabilityand inflaming-retarding performance. The first yarn and the second yarn are woven together to form the fabric, and the fibers can give full play to respective performance and advantages; and meanwhile, the performance of other fibers is not weakened, the comfort degree, air permeability and inflaming-retarding performance of the fabric can be greatly improved through the manual synergistic effect, and the fabric is applied to clothing preparation.

Description

technical field [0001] The invention belongs to the technical field of textile fabric preparation, and in particular relates to a flame-retardant fabric and a preparation method thereof. Background technique [0002] In recent years, with the development of the national economy and the improvement of people's living standards, the rapid development of high-rise buildings, commercial buildings, high-end apartments, hotels, airports, auditoriums, indoor entertainment venues, transportation, etc., all kinds of civil, decorative and The application fields of industrial fibers and textiles are gradually expanding. Because most of the textiles are flammable, they have become the main hidden danger of indoor fires and have become a serious social problem. The average annual fire loss is billions of yuan. Therefore, More attention has been paid to the development and application of flame-retardant fibers and textiles than before. Various flame-retardant standards and regulations are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D03D15/02D02G3/04D06N3/00D06N3/12D06N3/04D03D15/20D03D15/225D03D15/25D03D15/283D03D15/47D03D15/50D03D15/513D03D15/533
CPCD03D15/00D02G3/04D06N3/12D06N3/042D06N3/0015D06N3/0036D06N3/0061D06N3/0006D10B2321/10D10B2201/20D10B2331/14D10B2331/04D10B2101/20D06N2201/085D06N2209/067D06N2209/123D06N2211/10D03D15/593
Inventor 杨陈
Owner JIANGXI INST OF FASHION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap