Automobile tire

A technology for automobile tires and treads, which is applied in special tires, tire parts, vehicle parts, etc., can solve the problem that the grip performance needs to be improved, and achieve the effect of improving the grip performance and grip durability.

Inactive Publication Date: 2020-07-14
HUNAN CHENLI NEW MATERIAL CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the rubber composition described in the invention needs to be improved in flame retardant performance and road grip performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of rubber composition for medium and large automobile tire treads according to the present invention is specifically composed of: base rubber: 65 parts of styrene-butadiene rubber, 35 parts of natural rubber; functional filler: 30 parts of KH570 modified Sexual fumed silica, 60 parts of carbon black; tackifying resin: 10 parts of specific bora-methylvinyl MQ silicone resin, 10 parts of synthetic terpene resin; 8 parts of dibenzoyl peroxide, 4 parts Zinc dibutyldithiocarbamate.

[0026] Wherein, the specific bora-hybridized methyl vinyl MQ silicone resin has -O-B-O, -O-Si-O as the main chain and vinyl as the active functional group, and its preparation method is as follows: add 15 parts of Orthosilicate, 4 parts of hexamethyldisiloxane, 10 parts of tributyl borate, 10 parts of dimethylvinylchlorosilane, 20 parts of xylene, heated to 80 ° C, and then added 10 parts of 10% salt acid, react for 2 to 4 hours to obtain a hydrolyzate; add caustic soda to the hydrolyzat...

Embodiment 2

[0028] A kind of rubber composition for tread of medium and large automobile tires according to the present invention, concrete composition: wherein said base rubber is: 75 parts of styrene-butadiene rubber, 25 parts of natural rubber; functional filler is: 60 parts Parts of KH570 modified fumed silica, 30 parts of carbon black; tackifying resin: 20 parts of specific boronized methyl vinyl MQ silicone resin, 5 parts of synthetic terpene resin; 5 parts of tetramethyl autumn disulfide Lamb, 5 parts ethylene dicarbamate.

[0029] Wherein, the specific bora-hybridized methyl vinyl MQ silicone resin has -O-B-O, -O-Si-O as the main chain and vinyl as the active functional group, and its preparation method is as follows: add 15 parts of Orthosilicate, 8 parts of methyltriethoxysilane, 5 parts of triisopropyl borate, 20 parts of dimethylvinylchlorosilane, 20 parts of xylene, heated to 70 ° C, and then added 10 parts of 10% hydrogen Bromic acid, reacted for 2-4 hours to obtain a hydro...

Embodiment 3

[0031] A rubber composition for treads of medium and large automobile tires according to the present invention, the specific composition: matrix rubber: 68 parts of styrene-butadiene rubber, 32 parts of natural rubber; functional filler: 42 parts of KH570 modified Fumed silica, 48 parts of carbon black; tackifying resin: 18 parts of specific bora methyl vinyl MQ silicone resin, 7 parts of synthetic terpene resin; 10 parts of barium peroxide, 2 parts of N,N' - m-phenylene bismaleimide.

[0032] Wherein, the specific bora-hybridized methyl vinyl MQ silicone resin has -O-B-O, -O-Si-O as the main chain and vinyl as the active functional group, and its preparation method is as follows: add 15 parts of Orthosilicate, 6 parts of methyltrimethoxysilane, 7 parts of n-propyl borate, 8 parts of dimethylvinylchlorosilane, 20 parts of xylene, heated to 78 ° C, and then added 10 parts of 10% hydroiodic acid , react for 2 to 4 hours to obtain a hydrolyzate; add caustic soda to the hydrolyza...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
iodine adsorptionaaaaaaaaaa
Login to view more

Abstract

The invention relates to an automobile tire, the tread material of which is a rubber composition comprising the following components in parts by weight: 65-75 parts of styrene-butadiene rubber and 25-35 parts of natural rubber as matrix rubber; 30 to 60 parts of modified fumed silica and 30 to 60 parts of carbon black as a functional filler; 10-20 parts of specific boron hybrid methyl vinyl MQ silicon resin and 5-10 parts of synthetic terpene resin as tackifying resin; 5-10 parts of a vulcanizing agent and 2-5 parts of a vulcanization accelerator. The cured automobile tire has the advantages of high elasticity, self-flame retardancy, favorable wear resistance, excellent road holding performance and excellent road holding durability, and has wide application prospects in the field of medium / large-sized automobile tires.

Description

technical field [0001] This invention is a divisional application of the Chinese patent "Rubber Composition for Treads of Medium and Large Automobile Tires". The application date is October 31, 2017, and the application number is 201711049174.7. The invention relates to an automobile tire and belongs to the technical field of automobiles. [0002] technical background [0003] Tires are one of the most important components of a car. Its main function is to support the entire weight of the vehicle, bear the load of the car, transmit traction and braking torque, and ensure the adhesion between the wheel and the road. Most of the tires are rubber material. But in recent years, with the development of the economy, the number of cars has increased, and the requirements for rubber have become higher and higher. Not only does it require its wear resistance, but now in order to pursue the comfort of the car, how to reduce and absorb the rubber of the car? Vibration and impact force...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L7/00C08L83/14C08L45/00C08K13/06C08K9/06C08K7/26C08K3/04C08K5/14C08K5/39C08K5/3415B60C1/00C08G77/54
CPCB60C1/0016C08G77/54C08L9/06C08L2201/02C08L2205/035C08L2312/00C08L7/00C08L83/14C08L45/00C08K13/06C08K9/06C08K7/26C08K3/04C08K5/14C08K5/39C08K5/3415
Inventor 朱佳媚
Owner HUNAN CHENLI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap