A kind of high-strength and high flame-retardant organosilicon foam material and its preparation method

A technology of organosilicon foam and high flame retardancy, which is applied in the field of high strength and high flame retardancy organosilicon foam material and its preparation, which can solve the problems of poor mechanical properties and poor flame retardancy, so as to improve flame retardancy and slow down volatilization and diffusion, the effect of good thermal stability

Active Publication Date: 2022-03-15
新纳奇材料科技江苏有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nevertheless, silicone rubber itself also has some shortcomings. Taking the open-cell silicone rubber foam material as an example, although it has good compressive stress relaxation properties, its mechanical properties are poor, and its flame retardancy is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength and high flame-retardant organosilicon foam material and its preparation method
  • A kind of high-strength and high flame-retardant organosilicon foam material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A high-strength and highly flame-retardant silicone foam material, comprising component A and component B at a weight ratio of 1:1, wherein component A includes the following components in parts by weight:

[0035] 18 parts of hydroxyl silicone oil, 20 parts of vinyl silicone oil, 29 parts of flame retardant filler, 6 parts of fumed silica, 16 parts of hollow glass microspheres, 10 parts of nano calcium carbonate, 1 part of platinum catalyst;

[0036] Component B is in parts by weight and includes the following components:

[0037] 30 parts of hydroxyl silicone oil, 36 parts of vinyl silicone oil, 10 parts of flame retardant filler, 6 parts of fumed silica, 8 parts of hollow glass microspheres, 5 parts of nano-calcium carbonate, 1 part of carbon black, 1 part of acetylenic alcohol, hydrogen-containing silicone oil 4 parts;

[0038] The flame retardant filler is a mixture of molybdenum disulfide / zinc ferrite hybrid cyclic polyphosphazene composite material, aluminum hyd...

Embodiment 2

[0047] A high-strength and highly flame-retardant silicone foam material, comprising component A and component B at a weight ratio of 1:1, wherein component A includes the following components in parts by weight:

[0048] 18 parts of hydroxyl silicone oil, 20 parts of vinyl silicone oil, 29 parts of flame retardant filler, 6 parts of fumed silica, 16 parts of hollow glass microspheres, 10 parts of nano calcium carbonate, 1 part of platinum catalyst;

[0049] Component B is in parts by weight and includes the following components:

[0050] 30 parts of hydroxyl silicone oil, 36 parts of vinyl silicone oil, 10 parts of flame retardant filler, 6 parts of fumed silica, 8 parts of hollow glass microspheres, 5 parts of nano-calcium carbonate, 1 part of carbon black, 1 part of acetylenic alcohol, hydrogen-containing silicone oil 4 parts;

[0051] The flame retardant filler is a mixture of molybdenum disulfide / zinc ferrite hybrid cyclic polyphosphazene composite material, aluminum hyd...

Embodiment 3

[0060] A high-strength and highly flame-retardant silicone foam material, comprising component A and component B at a weight ratio of 1:1, wherein component A includes the following components in parts by weight:

[0061] 19 parts of hydroxyl silicone oil, 25 parts of vinyl silicone oil, 30 parts of flame retardant filler, 7 parts of fumed silica, 15 parts of hollow glass microspheres, 9 parts of nano-calcium carbonate, 2 parts of platinum catalyst;

[0062] Component B is in parts by weight and includes the following components:

[0063] 32 parts of hydroxyl silicone oil, 35 parts of vinyl silicone oil, 12 parts of flame retardant filler, 7 parts of fumed silica, 10 parts of hollow glass microspheres, 6 parts of nano-calcium carbonate, 1 part of carbon black, 1 part of acetylenic alcohol, hydrogen-containing silicone oil 5 copies;

[0064] The flame retardant filler is a mixture of molybdenum disulfide / zinc ferrite hybrid cyclic polyphosphazene composite material, aluminum h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength and high-flame-retardant organosilicon foam material, which includes component A and component B, component A includes the following components in parts by weight: 10-20 parts of hydroxyl silicone oil, 20-20 parts of vinyl silicone oil 70 parts, 10-40 parts of flame retardant filler, 5-10 parts of fumed white carbon black, 7-20 parts of hollow glass microspheres, 5-10 parts of nano-calcium carbonate, 1-3 parts of catalyst; component B is calculated in parts by weight , including the following components: 30-40 parts of hydroxyl silicone oil, 20-70 parts of vinyl silicone oil, 10-40 parts of flame-retardant filler, 5-10 parts of fumed silica, 7-20 parts of hollow glass microspheres, nano-calcium carbonate 5-10 parts, 1-3 parts of carbon black, 1-3 parts of inhibitor, 2-15 parts of hydrogen-containing silicone oil. The invention discloses a preparation method of the organosilicon foam material. The organosilicon foam material has good mechanical properties and good flame retardancy, and has a simple preparation method and low equipment requirements.

Description

Technical field: [0001] The invention relates to the field of polymer materials, in particular to a high-strength and high-flame-retardant organic silicon foam material and a preparation method thereof. Background technique: [0002] The foam materials currently on the market are mainly polyurethane foam plastics. However, the flame retardancy of polyurethane foam plastics is not ideal, and the limiting oxygen index (LOI) is only 19%, which belongs to a kind of flammable material. If it is used in the field of construction transportation, its safety cannot be effectively guaranteed. Therefore, the research and development of a new foam material with high flame retardant properties is very necessary. [0003] Silicone rubber is a kind of linear polysiloxane compound with silicon-oxygen bond as the main chain and side groups of silicon atoms connected to organic groups such as methyl, phenyl and vinyl groups. Silicone rubber foam material, also known as sponge silicone rubbe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/07C08L83/04C08L85/02C08L83/05C08K13/06C08K7/26C08K7/28C08K3/26C08K3/22C08K9/04C08K3/30C08K3/04C08K7/24C08J9/00
CPCC08J9/0061C08J9/0066C08J9/0071C08J9/0095C08J9/0085C08J2383/07C08J2483/04C08J2485/02C08J2483/05B29B7/90B29B7/7404B29B7/7485B29B7/823B29B7/88
Inventor 胡丽娜余跃
Owner 新纳奇材料科技江苏有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap