Modified concrete brick containing sludge gasification dry distillation slag and preparation method thereof

A technology for sludge gasification and concrete bricks, which is applied in clay preparation devices, chemical instruments and methods, and pyrolysis treatment of sludge, etc., can solve the problems of low utilization rate of urban sludge, lack of green building materials, etc. The effect of production costs

Active Publication Date: 2022-03-01
郑州市格沃环保开发有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problems of low urban sludge utilization rate and lack of green building materials in the prior art, the present invention provides a modified concrete brick containing sludge gasification and retort slag and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified concrete brick containing sludge gasification dry distillation slag and preparation method thereof
  • Modified concrete brick containing sludge gasification dry distillation slag and preparation method thereof
  • Modified concrete brick containing sludge gasification dry distillation slag and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A modified concrete brick containing sludge gasification and retort slag, the raw materials include: sludge gasification and retort slag 65%, cement 20%, lithium carbonate 0.03%, water 15%, wherein the powder in the sludge gasification and retort slag The slag ratio is 1:3.

[0027] Preparation process: crush the gasified dry distillation slag through a roller crusher, control the coarse particle size to 5-15mm, and then sieve the powder through a 3mm sieve, and the rest is slag; weigh the raw materials according to the formula ratio, mix Stir evenly; pour the mixture into the mold and press to form. The pressing pressure is 20Mpa, and the pressure holding time is 10s. After forming, it is demoulded and placed in a cool place for natural curing.

[0028] The basic mechanical properties of the prepared concrete bricks were tested according to GBT 21144-2007. The ratio and basic mechanical properties of the concrete bricks in this embodiment are shown in Table 1.

[0029...

Embodiment 2

[0033] A modified concrete brick containing sludge gasification and retort slag, raw materials include: sludge gasification and retort slag 70%, cement 15%, calcium formate 0.02%, water 15%, wherein the powder in the sludge gasification and retort slag The slag ratio is 2:3.

[0034] Preparation process: crush the gasified dry distillation slag through a roller crusher, control the coarse particle size to 5-15mm, and then sieve the powder through a 3mm sieve, and the rest is slag. Weigh the raw materials according to the proportion of the formula, mix and stir evenly; pour the mixture into the mold and press to form. The pressing pressure is 30Mpa, and the pressure holding time is 15s. After forming, the mold is demoulded and placed in a cool place for natural curing.

[0035] The basic mechanical properties of the prepared concrete bricks were tested according to GBT 21144-2007. The proportion and basic mechanical properties of the concrete bricks in this embodiment are shown...

Embodiment 3

[0040] A modified concrete brick containing sludge gasification and retort slag, the raw materials include: sludge gasification and retort slag 60%, cement 25%, calcium formate 0.05%, water 15%, wherein the powder in the sludge gasification and retort slag The slag ratio is 1:2.

[0041] Preparation process: crush the gasified dry distillation slag through a roller crusher, control the coarse particle size to 5-15mm, and then sieve the powder through a 3mm sieve, and the rest is slag. Weigh the raw materials according to the proportion of the formula, mix and stir evenly; pour the mixture into the mold and press to form, the pressing pressure is 25Mpa, and the holding time is 10s. After forming, the mold is demoulded and placed in a cool place for natural curing.

[0042] The basic mechanical properties of the prepared concrete bricks were tested according to GBT 21144-2007. The proportion and basic mechanical properties of the concrete bricks in this embodiment are shown in T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of reuse of urban and industrial waste resources, and specifically relates to a modified concrete brick containing sludge gasification and retort slag and a preparation method thereof. 15-25% cement, 10-15% water, 0.01-0.05% accelerator, and the ratio of powder and slag in the gasification and retort slag is (1-2):3. The preparation method is: dry the gasified dry distillation slag until the water content is ≤10%, pass it through a roller crusher, control the coarse particle size to 5-15mm, and then sieve the powder through a 3mm sieve, weigh cement, gas Distillation slag, accelerator and water are mixed uniformly; the mixture is poured into a mold and then pressed into shape, and then naturally cured after demoulding. The invention obtains sludge gasification dry distillation slag by drying, granulating and gasifying urban sludge, and uses it as a raw material for preparing modified concrete bricks, which is beneficial to environmental protection and reduces the production cost of factories.

Description

technical field [0001] The invention belongs to the field of reuse of urban and industrial waste resources, and in particular relates to a modified concrete brick containing sludge gasification and retort slag and a preparation method thereof. Background technique [0002] With the increase of urban population and the development of industrial production, the discharge of urban wastewater and sewage is increasing, which also leads to a surge in the discharge of urban sludge. According to reports, my country's sewage discharge has reached 5.11×10 4 billion tons per year, and the amount of sludge accounts for about 0.3% to 0.5% of the treated water, and the annual discharge is huge. Sludge contains some heavy metals, pathogenic bacteria and toxic organic substances, which will cause environmental hazards such as land pollution, decay, odor, and groundwater pollution. However, municipal sludge is also rich in biological sources, organic matter and some inorganic components, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04B28C5/00B28B11/24B28B3/00C02F11/10C02F11/12
CPCC04B28/04B28C5/00B28B3/00B28B11/245C02F11/12C02F11/10C04B2111/00017C02F2303/06C04B18/06C04B18/0427C04B22/10C04B24/04Y02W10/40
Inventor 赵琦白浩张伟锟罗忠玉冯晨杨智李兵刘宇
Owner 郑州市格沃环保开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com