Welding spatter prevention agent and preparing method

A technology of anti-splash agent and solvent oil, which is applied in the direction of welding equipment, welding medium, welding/cutting medium/material, etc. It can solve the problems of reducing welding slag and the surface adhesion of objects, not cleaning it off, and poor welding molding. Achieve the effects of improving operation efficiency and product delicacy, reducing dust and noise pollution, and reducing labor intensity

Active Publication Date: 2020-06-09
柯福(上海)化工科技有限公司
View PDF15 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the limitation of the components of the existing welding anti-spatter agent, the water-soluble substance used in it cannot effectively form an isolation film between the welding slag and the surface of the object, and it is easy to volatilize when heated, and it is easily denatured by the heat of the welding slag. Good anti-welding slag spattering effect; penetrating into the weld, it is easy to cause poor welding formation; it cannot be cleaned after welding, resulting in poor electroplating and coating, and there are limitations in application. The invention provides the use of oil-based materials as main raw materials , supplemented with solvent oil and petroleum ether. In the application, the oil-based material can effectively form an isolation film between the welding slag and the surface of the object, reducing the adhesion between the welding slag and the surface of the object, thereby effectively preventing Welding slag adheres to the surface of the object, and even if it penetrates into the weld, it will not affect the welding quality; it replaces the traditional manual grinding and spatter, and prevents the surface of the object from grinding damage; it brings convenience to the welding operation and reduces the labor intensity of the staff. A kind of welding anti-splash agent and its preparation method which improves operation efficiency and product delicacy, and reduces dust and noise pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding spatter prevention agent and preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] figure 1 As shown in, a welding anti-splash agent, including solvent oil (one of 6#, 120#, 200#, the present embodiment uses 6#), petroleum ether, oil-based materials; the oil-based materials are lubricating Oil, oil-based materials, solvent naphtha, and petroleum ether are three materials in equal parts per hundred, which are 70 parts, 25 parts, and 5 parts respectively. The above-mentioned raw materials are mixed and stirred at high temperature to obtain finished products; the preparation method of welding anti-splash agent includes Weighing, initial stirring, re-stirring, filling and packaging five processes.

[0016] figure 1 As shown in , in the weighing process, the oil-based material, solvent naphtha, and petroleum ether are weighed according to the proportion of each hundred equal parts, and put into containers for use. In the initial mixing process, first pour lubricating oil into the constant temperature stirring container, after the temperature inside the c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a welding spatter prevention agent. The welding spatter prevention agent comprises 25 parts of solvent naphtha, 5 parts of petroleum ether and 70 parts of oil-based materials per centum, wherein the base-based materials are lubricating oil, the above raw materials are subjected to high-temperature blending and stirring, and the agent is obtained. A preparing method of the welding spatter prevention agent comprises the five procedures of weighing, primary stirring, secondary stirring, filling and packaging. When the agent is used, a user directly sprays the agent to thesurface of a non-welding surface, due to the fact that the oil-based materials that is the lubricating oil are used as the main raw materials, the oil-based materials can effectively form an isolationfilm between welding slag and the object surface, adhesive power between the welding slag and the object surface can be reduced, and the welding slag is prevented from being bonded on the object surface. Convenience is brought to the welding work, labor intensity of a worker is reduced, work efficiency and product fineness can be improved, dust and noise pollution can be reduced, and on the basis, the agent has the good application prospect.

Description

technical field [0001] The invention relates to the field of auxiliary materials used in welding processes and production methods, in particular to a welding anti-splash agent and a preparation method. Background technique [0002] During the welding work, the welding slag generated by the welding parts and welding wire tends to adhere to the non-welding area of ​​the object. Therefore, in many cases, after the welding work is completed, it is necessary to clean up the welding slag on the object. Because cleaning the welding slag often requires the use of tools such as electric grinding wheels, it will not only cause inconvenience to the operator, but also cause damage to the object if it is not properly operated. The surface is damaged due to the removal of welding slag, and it takes a lot of labor and the work efficiency is low. In order to reduce the impact of welding slag on objects as much as possible and improve production efficiency, welding anti-spatter agents have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/36B23K35/40
CPCB23K35/3612B23K35/40
Inventor 李弯
Owner 柯福(上海)化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products