Fuzzing agent and preparation method thereof

A technology for raising agent and hair oil, applied in the direction of improved hand-feeling fibers, fiber types, textiles and papermaking, etc., can solve problems such as unfavorable environment and low price, and achieve reduced scratches, good antistatic and easy decontamination. , good wetting and sliding properties

Inactive Publication Date: 2020-06-05
浙江德彩新材料科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a raising agent and a preparation method thereof, so as to solve the problem that the raising agent with siloxane etc. as main raw materials in the prior art is not cheap and is not conducive to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A raising agent and a preparation method thereof, the raw materials of the raising agent and their mass percentages are: 55% of RT film emulsion, 30% of moisture-absorbing and sweat-wicking finishing agent; 10% of silicone mold release agent; 5% of silicone oil, comprising the following steps:

[0028] (1) Preparation of RT film emulsion: gradually add RT film to warm water, the temperature of the warm water is 30°C, the amount of RT film added is 5% of the warm water, stir for 30 minutes to decompose and emulsify, let stand and soak for 1 hour, and then stir at a low speed To a completely dissolved uniform slurry, add a filter to filter and discharge, and set aside;

[0029] (2) Dilution of the moisture-absorbing and sweat-wicking finishing agent: gradually add the raw materials of the moisture-absorbing and sweat-wicking finishing agent into water, the temperature of the water is 90°C, stir while adding the material, make it expand and melt slowly, after melting, lower...

Embodiment 2

[0033] A kind of raising agent and preparation method thereof, the raw material of raising agent and its mass percentage are: RT film emulsion 70%, moisture-wicking finishing agent 20%; Silicone release agent 6%; Silicone oil 4%, comprising the following steps:

[0034] (1) Preparation of RT film emulsion: gradually add RT film to warm water, the temperature of the warm water is 40°C, the amount of RT film added is 10% of the warm water, stir for 60 minutes to make it decompose and emulsify, let it stand for 2 hours, and then stir at a low speed To a completely dissolved uniform slurry, add a filter to filter and discharge, and set aside;

[0035] (2) Dilution of moisture-absorbing and sweat-wicking finishing agent: gradually add the raw materials of moisture-absorbing and sweat-wicking finishing agent into water, the temperature of water is 95°C, stir while adding material, make it expand and melt slowly, after melting, lower the temperature of the diluted environment to 85°C...

Embodiment 3

[0039] A raising agent and a preparation method thereof, the raw materials of the raising agent and their mass percentages are: 65% of RT film emulsion, 25% of a moisture-wicking finishing agent; 7% of a silicone release agent; and 3% of a silicone oil, comprising the following steps:

[0040] (1) Preparation of RT film emulsion: gradually add RT film to warm water, the water temperature of warm water is 30°C-40°C, the amount of RT film added is 8% of the warm water, stir for 45 minutes to make it decompose and emulsify, let stand and soak for 1.5h , and then stir at a low speed until it is completely dissolved into a uniform slurry, add a filter to filter and discharge, and set aside;

[0041] (2) Dilution of the moisture-absorbing and sweat-wicking finishing agent: gradually add the raw materials of the moisture-absorbing and sweat-wicking finishing agent into water, the temperature of the water is 92°C, stir while adding the material, make it expand and melt slowly, after me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fuzzing agent and a preparation method thereof. The fuzzing agent is prepared from the following raw materials in percentage by mass: 55-70% of RT soft sheet emulsion, 8-30%of a moisture absorption and sweat releasing finishing agent, 5-12% of fuzzing oil and 1-5% of silicon oil. The preparation method of the fuzzing agent comprises the steps of (1) preparing the RT softsheet emulsion; (2) diluting the moisture absorption and sweat releasing finishing agent; (3) preparing fuzzing oil and silicone oil, adding the fuzzing oil into the RT soft sheet emulsion prepared in the step (1), performing stirring to fully emulsify the fuzzing oil, then simultaneously adding the moisture absorption and sweat releasing finishing agent diluted in the step (2) and the silicone oil, continuously performing stirring for 20-30 minutes, adding a filter screen, and filtering and discharging the material to obtain a fuzzing agent finished product; and (4) performing weighing, performing warehousing and tidily placing the fuzzing agent after the detection is qualified. The preparation method of the fuzzing agent is simple in process, all the raw materials are placed in water tobe decomposed, emulsified, diluted and the like, water-based production is achieved, and the production environment is benefited, so that the prepared fuzzing agent can be dissolved in water in any proportion to be used, the use condition is simple and convenient, and energy conservation and environment protection are achieved.

Description

technical field [0001] The invention relates to the field of textile additives, in particular to a raising agent and a preparation method thereof. Background technique [0002] After the general gray cloth is pre-treated (desizing, smelting, back bleaching, mercerizing, etc.), the cloth surface is very smooth and smooth. Sanding is to use a roller wrapped in sand leather to rub on the cloth surface and grind it on the cloth surface. A layer of fluff is produced, and the general sanding is to improve the style and feel of the fabric, making it more plump and supple, and more comfortable to wear. Brushed fabrics are now very popular, especially in winter. Brushed clothing and bedding sets are very popular. It is soft, comfortable, rich in texture, strong in drape, easy to care, and suede. The plump new look appeals to consumers. In the sanding process, a raising agent is generally used when making long hair or thicker cloth. The general raising agents on the market are mainl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/507D06M15/643D06M13/352D06M101/06D06M101/08D06M101/32D06M101/34D06M101/38
CPCD06M15/507D06M15/643D06M13/352D06M2101/32D06M2101/34D06M2101/06D06M2101/08D06M2101/38D06M2200/50
Inventor 罗祖存
Owner 浙江德彩新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap