Modified soybean aldehyde-free flame-retardant adhesive and preparation method thereof

A flame retardant adhesive and modification technology, applied in the field of modified soybean formaldehyde-free flame retardant adhesive and its preparation, can solve the problems of unsatisfactory flame retardant effect, fast drying time, high price, etc., and achieve good flame retardant effect , The effect of improving viscosity and low cost

Active Publication Date: 2020-06-05
浙江云峰莫干山地板有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the quality of flame retardants on the market is uneven, and the price of good flame retardant effect is high. On the contrary, the flame retardant effect of cheap ones cannot meet the requirements. If the flame retardant is directly compounded with soybean gum, there will be Problems such as fast glue drying, cold pressing without forming, finished product wet strength and impregnation peeling are unqualified, etc.
The formaldehyde-free flame-retardant glue disclosed in the patent application number CN201910843380.8 was used to trial-produce solid wood composite flooring. The test results showed that the flame-retardant grade and formaldehyde emission were all qualified, but the type II bonding strength was only 0.3-0.4MPa and the dipping peeling was unqualified. , not for parquet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified soybean aldehyde-free flame-retardant adhesive and preparation method thereof
  • Modified soybean aldehyde-free flame-retardant adhesive and preparation method thereof
  • Modified soybean aldehyde-free flame-retardant adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] 1. Preparation of activated modified flame retardant

[0047] Add 30 parts of ammonium polyphosphate APP, 15 parts of melamine phosphate MP, 3 parts of sodium dodecylbenzenesulfonate, and 5 parts of sodium silicate in the high-speed mixer, and stir for 15 minutes, then add 65 parts of aluminum hydroxide, Stir for another 20 minutes until uniform, and the activated modified flame retardant is obtained;

[0048] 2. Preparation of modified soybean formaldehyde-free flame retardant adhesive

[0049] Add 100 parts of modified polyamide resins, 70 parts of water, 140 parts of defatted soy flour, 80 parts of activated modified flame retardants, 6 parts of water-based tackifier 880G, and 0.15 parts of polyethylene glycol in the reaction kettle successively. Stir at ~85°C for 2 hours until uniform, and the modified soybean formaldehyde-free flame-retardant rubber is prepared;

[0050] 3. Preparation of formaldehyde-free flame-retardant parquet

[0051] 1) Coat the modified so...

Embodiment 2

[0055] The production process of step 3 in embodiment 1 is unchanged, and the changes are as follows:

[0056] 1. Preparation of activated modified flame retardant

[0057] Add 35 parts of ammonium polyphosphate APP, 15 parts of melamine phosphate MP, 2.5 parts of sodium dodecylbenzenesulfonate, and 6 parts of sodium silicate in the high-speed mixer, and stir for 15 minutes, then add 75 parts of aluminum hydroxide, Stir for another 20 minutes until uniform, and the activated modified flame retardant is obtained;

[0058] 2. Preparation of modified soybean formaldehyde-free flame retardant adhesive

[0059] Add 100 parts of modified polyamide resins, 65 parts of water, 130 parts of defatted soy flour, 110 parts of activated modified flame retardants, 7 parts of water-based tackifier 880G, and 0.15 parts of polyethylene glycol in the reactor. Stir at ~85°C for 2 hours until uniform, and the modified soybean formaldehyde-free flame-retardant rubber is prepared.

Embodiment 3

[0061] Step one and two production processes in embodiment 1 are all unchanged, and change part is as follows:

[0062] 3. Preparation of formaldehyde-free flame-retardant parquet

[0063] 1) Coat the modified soybean formaldehyde-free flame-retardant glue prepared in step 2 on the surface of eucalyptus veneer with a thickness of 2.2mm, and the coating amount is 250g / m 2 , according to the crisscross formation of each layer of multi-layer plywood for solid wood composite flooring, after cold pressing and hot pressing, it is made into a flame-retardant multi-layer substrate layer. The process conditions are cold pressing time 1h, unit pressure 9kg / cm 2 , hot pressing temperature 125 ℃, (52+25) s / mm, unit pressure 9kg / cm 2 ;

[0064] 2) After the flame-retardant multi-layer substrate layer is balanced, apply the modified soybean formaldehyde-free flame-retardant adhesive prepared in step 2, the upper surface is bonded to the oak wood surface with a thickness of 1.2 mm, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention aims to provide a modified soybean aldehyde-free flame-retardant adhesive. The modified soybean aldehyde-free flame-retardant adhesive comprises the following components in parts by weight: 100 parts of a cross-linking modifier, 50-100 parts of water, 100-200 parts of degreased bean flour, 50-150 parts of an activated modified flame retardant, 5-7 parts of a water-based tackifier and0.1-0.2 part of an assistant, wherein the activated modified flame retardant is prepared from the following components in parts by weight: 20-40 parts of ammonium polyphosphate APP, 10-20 parts of melamine phosphate MP, 2-3.5 parts of a coupling agent, 4-7 parts of a dispersing agent and 50-80 parts of aluminum hydroxide or magnesium hydroxide.

Description

technical field [0001] The invention relates to the technical field of production and processing of solid wood composite flooring, in particular to a modified soybean formaldehyde-free flame-retardant glue and a preparation method thereof. Background technique [0002] Wood flooring is a commonly used ground decoration material. The main varieties include laminate flooring, solid wood composite flooring, solid wood flooring, and impregnated paper laminate veneer multi-layer solid wood composite flooring. Compared with other ground decoration materials such as carpet, stone, ceramic tile, and plastic floor, wooden floor has natural and beautiful texture, light weight and easy processing, good heat preservation, can adjust indoor temperature and humidity, and has the characteristics of being elastic and shock-relieving. It gives people a feeling of returning to nature, so it is loved by people. The solid wood composite floor occupies a dominant position in the wooden floor pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J189/00C09J177/00C09J11/06C09J11/04B27D1/08B27M3/04
CPCC09J189/00C09J11/06C09J11/04B27D1/08B27M3/04C08L2205/035C08L2201/02C08K2003/323C08K2003/2227C08L77/00C08K13/06C08K9/04C08K9/02C08K3/32C08K5/34928C08K3/22
Inventor 施晓宏桂成胜敖景伟潘锦垭沈云芳赵建忠付珏杰朱海峰
Owner 浙江云峰莫干山地板有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com