Extremely-high-conductivity release film and preparation method thereof

A conductive, release film technology, used in conductive coatings, film/sheet release liners, film/sheet adhesives, etc., to solve the problem of high surface resistance and poor release stability of release films and other problems, to achieve the effect of stable release force, high residual adhesion rate and high cleanliness

Inactive Publication Date: 2020-05-29
佛山市佳世达薄膜科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved in the present invention is to overcome the problems of high surface resistance and poor release stability of the release film in the prior art, and provide a very high conductivity release film and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Extremely-high-conductivity release film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of extremely high conductivity release film, the formula of release agent comprises each component of following parts by weight:

[0036] Silicone oil A 45 parts

[0037] Silicone oil B 46 parts

[0038] Bridge agent 2 parts

[0039] Adhesive 2 parts

[0040] Catalyst 1.5 parts

[0041] 130 parts of white electric oil

[0042] D30 90 copies

[0043] 45 parts of isopropanol

[0044] 58 parts of cyclohexanone.

[0045] The preparation method of the extremely high conductivity release film comprises the following steps:

[0046] S1. Coating soluble conductive polymer on the corona surface of 75μm silver aluminized PET film, the speed is 60m / min, the temperature T1 / T2 / T3 / T4 / T5 / T6 / T7=80 / 130 / 145 / 155 / 155 / 130 / 70;

[0047] S2. Coating soluble conductive polymer on the back of 75μm silver aluminized film PET, the speed is 60m / min, the temperature T1 / T2 / T3 / T4 / T5 / T6 / T7=80 / 130 / 145 / 155 / 155 / 130 / 70;

[0048] S3 is released on the soluble conductive polymer layer on ...

Embodiment 2

[0050] A kind of extremely high conductivity release film, the formula of release agent comprises each component of following parts by weight:

[0051] Silicone oil A 54 parts

[0052] Silicone oil B 52 parts

[0053] 3 parts bridging agent

[0054] Adhesive 3.5 parts

[0055] Catalyst 2.8 parts

[0056] 150 parts of white electric oil

[0057] D30 110 copies

[0058] 52 parts of isopropanol

[0059] 65 parts of cyclohexanone.

[0060] The preparation method of the extremely high conductivity release film comprises the following steps:

[0061] S1. Coating soluble conductive polymer on the corona surface of 75μm silver aluminized PET film, the speed is 60m / min, the temperature T1 / T2 / T3 / T4 / T5 / T6 / T7=80 / 130 / 145 / 155 / 155 / 130 / 70;

[0062] S2. Coating soluble conductive polymer on the back of 75μm silver aluminized film PET, the speed is 60m / min, the temperature T1 / T2 / T3 / T4 / T5 / T6 / T7=80 / 130 / 145 / 155 / 155 / 130 / 70;

[0063] S3 is released on the soluble conductive polymer laye...

Embodiment 3

[0066] A kind of extremely high conductivity release film, the formula of release agent comprises each component of following parts by weight:

[0067] Silicone oil A 50 parts

[0068] Silicone oil B 50 parts

[0069] 2.3 parts of bridging agent

[0070] Adhesive 2.4 parts

[0071] Catalyst 2.4 parts

[0072] 140 parts of white electric oil

[0073] D30 100 copies

[0074] 49 parts of isopropanol

[0075] 61 parts of cyclohexanone.

[0076] The preparation method of this embodiment is the same as embodiment 2.

[0077] The test parameter of embodiment 3

[0078]

[0079] From the data in the above table, it can be seen that the highly conductive release film of the present invention has stable release force, high residual adhesion rate, good surface smoothness and mechanical processing, and extremely low surface resistance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a release film with extremely high conductivity. The formula of the release agent comprises the following components in parts by weight: 45-54 parts of silicone oil A, 46-52 parts of silicone oil B, 2-3 parts of a bridging agent, 2-3.5 parts of an adhesion promoter, 1.5-2.8 parts of a catalyst, 130-150 parts of n-heptane, 90-110 parts of D30, 45-52 parts of isopropanol and58-65 parts of cyclohexanone. The base material of the release film is subjected to a sputtering treatment; the release film is suitable for releasing and die cutting punching of various adhesive materials, is generally suitable for adhesion processing of protective films, double faced adhesive tapes and other adhesive materials, and has the advantages of high cleanliness, stable release force, high residual adhesion rate, favorable surface flatness, favorable machining property and extremely low surface resistance.

Description

technical field [0001] The invention relates to a very high conductivity release film and a preparation method thereof. Background technique [0002] The release film is also called the release film, which refers to a film with a separable surface. The release film is not sticky or slightly sticky after contacting with a specific material under limited conditions. Usually, in order to increase the release force of the plastic film, the plastic film will be treated with plasma, or coated with fluorine, or coated with a silicone release agent on the surface of the film material, such as PET, PE, OPP, etc., to make it For various organic pressure-sensitive adhesives, such as hot-melt adhesives, acrylic adhesives and rubber-based pressure-sensitive adhesives, it can exhibit extremely light release force. However, the existing release films often have the problems of high surface resistance and poor release stability. Contents of the invention [0003] The technical problem t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/40C09D183/04C09D5/24
CPCC08L2205/025C09D5/24C09D183/04C09J2467/005C09J7/401C09J7/403C08L83/04
Inventor 冯彬许晋嘉李益玮施绍富杨雍华张玉平涂青青
Owner 佛山市佳世达薄膜科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products