A kind of preparation method of high strength and high barrier TPU composite material

A composite material, high barrier technology, applied in the field of polymer composite material synthesis, to achieve the effect of increasing the number of hydroxyl groups, increasing the degree of cross-linking, and increasing the number of reaction sites

Active Publication Date: 2021-08-31
FUZHOU UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the inadequacy of existing TPU synthesis methods that cannot obtain TPU composite materials with both high barrier performance and high mechanical properties, the present invention provides a preparation method for high-strength and high-barrier TPU composite materials. TPU composite material has high mechanical properties and barrier properties at the same time, and the comprehensive performance is more excellent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high strength and high barrier TPU composite material
  • A kind of preparation method of high strength and high barrier TPU composite material
  • A kind of preparation method of high strength and high barrier TPU composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037]1) Preparation of graphene oxide: Take 1g of flake graphite, add it to 23mL of concentrated sulfuric acid and mix well, keep magnetic stirring; slowly add 3g of KMnO in batches under the condition of temperature 4 , 0.5g of NaNO 3 , the reaction continued for 4 hours, raised to 35°C and reacted for 2 hours, then raised the temperature to 98°C; added 44mL deionized water to the system, and added 5wt% H 2 o 2 Until the solution is golden yellow and no bubbles are generated, finally add 20mL of 5wt% HCl; centrifuge and wash the suspension several times until pH = 7, and freeze-dry at -80°C after ultrasonication for 2 hours to obtain graphene oxide;

[0038] 2) Preparation of modified graphene oxide: Add 0.0335g of graphene oxide prepared in step 1) into 10mL of DMF to obtain graphene oxide / DMF suspension, ultrasonically disperse for 1h, add 0.1675g of chitosan under magnetic stirring at 500rpm, React at 25°C for 12 hours to obtain a modified graphene oxide solution.

[00...

Embodiment 2

[0045] 1) Preparation of graphene oxide: Take 1g of flake graphite, add it to 23mL of concentrated sulfuric acid and mix well, keep magnetic stirring; slowly add a total of 3g of KMnO in batches at low temperature (4 , 0.5g NaNO 3 , the reaction continued for 4 hours, raised to medium temperature (35°C) and then reacted for 2 hours, then raised the temperature to 98°C; added 44mL deionized water to the system, and added 5wt%H2 dropwise after 10min 2 o 2 Until the solution is golden yellow and no bubbles are generated, finally add 20mL of 5wt% HCl; centrifuge and wash the suspension several times until pH = 7, and freeze-dry at -80°C after ultrasonication for 2 hours to obtain graphene oxide;

[0046] 2) Modification of graphene oxide: add 0.0670g graphene oxide prepared in step 1) to 10mL DMF to obtain graphene oxide / DMF suspension, ultrasonically disperse for 1h, add 0.3350g chitosan under the condition of 500rpm magnetic stirring, 25 °C for 12 hours to obtain a modified gra...

Embodiment 3

[0053] 1) Preparation of graphene oxide: Take 1g flake graphite, add it to 23mL concentrated sulfuric acid and mix well, keep magnetic stirring; slowly add 3gKMnO in batches at low temperature (4 , 0.5gNaNO 3 , the reaction continued for 4 hours, raised to medium temperature (35°C) and reacted for 2 hours, then raised the temperature to 98°C; added 44mL deionized water to the system, and added 5% H2O dropwise after 10min 2 o 2 Until the solution is golden yellow and no bubbles are generated, finally add 20mL of 5% HCl; centrifuge and wash the suspension several times until PH = 7, and freeze-dry at -80°C after ultrasonication for 2 hours to obtain graphene oxide;

[0054] 2) Modification of graphene oxide: Add 0.1005g of graphene oxide prepared in step 1) to 10mL of DMF to obtain a graphene oxide / DMF suspension, ultrasonically disperse for 1h, and add 0.5025g of chitosan under the condition of 500rpm magnetic stirring, React at 25°C for 12 hours to obtain a modified graphene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a high-strength and high-barrier TPU composite material, which belongs to the technical field of polymer composite material synthesis. In this method, polytetramethylene ether glycol and 4,4'-diphenylmethane diisocyanate are reacted to obtain an isocyanate group-terminated TPU prepolymer, and modified graphene oxide is added to the TPU prepolymer, and 1, 4-Butanediol participates in the in-situ polymerization process together as a compound chain extender to complete the chain extension reaction and obtain a high-strength and high-barrier TPU composite material. Modified graphene oxide increases the number of reaction sites in the reaction system and increases the crosslinking degree of the composite material. There are a large number of covalent bonds and hydrogen bonds in the prepared TPU composite material, which leads to the dispersion of modified graphene oxide in the TPU matrix. Good performance, the interface bonding force with the TPU matrix is ​​enhanced, and the barrier properties and mechanical properties of the TPU composite are improved.

Description

technical field [0001] The invention belongs to the technical field of polymer composite material synthesis, and in particular relates to a preparation method of a high-strength and high-barrier TPU composite material. Background technique [0002] Thermoplastic polyurethane (TPU) is a block polymer composed of a soft soft segment and a rigid hard segment. The soft segment is composed of a polymeric polyol with a large molecular weight, and the hard segment is composed of a small molecule polyol and a diisocyanate. TPU has the characteristics of both elastomers and plastics, and has excellent performance characteristics such as wear resistance, oil resistance and ozone resistance. It is widely used in the fields of adhesives, medical devices, fabrics, coatings and other materials. However, the barrier properties of TPU films to oxygen and other small molecules are not good. Improving the barrier properties of TPU films simply by adding fillers will lead to a decrease in mech...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/76C08G18/64C08G18/48C08G18/10C08G18/32C08K9/02C08K3/04
CPCC08G18/10C08G18/4854C08G18/6484C08G18/7671C08K9/02C08K3/042C08G18/3206C08G18/64
Inventor 郑玉婴张钊滟
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com