A coral fleece and fabric technology, which is applied in the field of preparation of coral fleece fabrics, can solve the problems of easy lodging and bulkiness of coral fleece fabrics, and achieve the effects of crisp appearance, good hygroscopicity and fine surface.

Active Publication Date: 2020-05-08
JIANGSU HENGLI CHEM FIBER
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the technical problems of easy lodging and low bulkiness of coral fleece fabrics in the prior art, and the purpose is to provide a preparation method of coral fleece fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for coral velvet fabric
  • Preparation method for coral velvet fabric
  • Preparation method for coral velvet fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of preparation method of coral fleece fabric, its process is as follows:

[0035] (1) Preparation of special-shaped semi-dull polyester drawn yarn:

[0036] (1.1) Extrude the PET melt (with an intrinsic viscosity of 0.61dL / g) from the trilobal spinneret hole on the spinneret and cool it with ring blowing; wherein, the number of spinneret holes is 24, and the trilobal spinneret The three lobes of the spinneret hole are of unequal width, and are equally spaced on the same circle, and along the clockwise direction, the width of the narrowest lobe is 0.1mm, 0.06mm, 0.1mm, 0.09mm, 0.06mm, 0.06mm, 0.08mm, 0.07mm, 0.12mm, 0.09mm, 0.08mm, 0.12mm, 0.09mm, 0.06mm, 0.07mm, 0.1mm, 0.07mm, 0.08mm, 0.09mm, 0.07mm, 0.1mm, 0.06mm, 0.1mm , 0.08mm, the width of the remaining two leaves is fixed, and the ratio of the maximum width of the narrowest leaf to the width of the remaining two leaves is 1.0:1.5:1.7, the length of all three leaves is the same, and the ratio of the length t...

Embodiment 2

[0045] A kind of preparation method of coral fleece fabric, its process is as follows:

[0046] (1) Preparation of special-shaped semi-dull polyester drawn yarn:

[0047] (1.1) The PET melt (intrinsic viscosity is 0.62dL / g) is extruded from the trilobal spinneret hole on the spinneret and cooled by ring blowing; wherein, the number of spinneret holes is 24, and the trilobal spinneret The three lobes of the spinneret hole are of unequal width, and are equally spaced on the same circle, and along the clockwise direction, the width of the narrowest lobe is 0.09mm, 0.06mm, 0.07mm, 0.1mm, 0.07mm, 0.08mm, 0.09mm, 0.07mm, 0.1mm, 0.06mm, 0.1mm, 0.08mm, 0.08mm, 0.08mm, 0.12mm, 0.1mm, 0.11mm, 0.07mm, 0.09mm, 0.1mm, 0.1mm, 0.1mm, 0.06mm , 0.09mm, the width of the other two leaves is fixed, and the ratio of the maximum width of the narrowest leaf to the width of the remaining two leaves is 1.0:1.6:1.55, the length of all three leaves is the same, and the ratio of the length to width of t...

Embodiment 3

[0056] A kind of preparation method of coral fleece fabric, its process is as follows:

[0057] (1) Preparation of special-shaped semi-dull polyester drawn yarn:

[0058] (1.1) The PET melt (intrinsic viscosity is 0.64dL / g) is extruded from the trilobal spinneret hole on the spinneret and cooled by ring blowing; wherein, the number of spinneret holes is 24, and the trilobal spinneret The three lobes of the spinneret hole are of unequal width, and are equally spaced on the same circle, and along the clockwise direction, the width of the narrowest lobe is 0.09mm, 0.06mm, 0.12mm, 0.11mm, 0.07mm, 0.06mm, 0.1mm, 0.08mm, 0.1mm, 0.09mm, 0.09mm, 0.09mm, 0.07mm, 0.11mm, 0.12mm, 0.1mm, 0.11mm, 0.07mm, 0.09mm, 0.1mm, 0.1mm, 0.1mm, 0.06mm , 0.09mm, the width of the other two leaves is fixed, and the ratio of the maximum width of the narrowest leaf to the width of the remaining two leaves is 1.0:1.9:1.8, the length of all three leaves is the same, and the ratio of the length to width of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
heightaaaaaaaaaa
Basis weightaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a coral velvet fabric. According to the preparation method, plush grey cloth is manufactured by weaving special-shaped semi-dull polyester drawn yarn as a raw material of wool yarn and polyester FDY yarn as a raw material of ground yarn, and then the coral velvet fabric is obtained through presetting, soft finish, fluff opening, napping, after-finish and resetting, wherein the wool yarn obtained by carrying out heat treatment and twisting on the special-shaped semi-dull polyester drawn yarn; a preparation process for the special-shaped semi-dullpolyester drawn yarn comprises the following steps of cooling through ring blowing after a PET melt is extruded from trilobal spinneret holes in a spinneret plate, and preparing the special-shaped semi-dull polyester drawn yarn according to an FDY process, wherein three leaves of each trilobal spinneret hole have the same length and different widths, the trilobal spinneret holes are distributed in a concentric circle, the center line of the narrowest leaf passes through the center of the circle and the pointing is away from the center of the circle. The preparation method disclosed by the invention is easy to operate, fluff of the prepared coral velvet fabric is fluffy, full, soft in hand feeling and good in warmth retention property.

Description

technical field [0001] The invention belongs to the technical field of textiles and relates to a method for preparing a coral fleece fabric. Background technique [0002] Coral fleece is a coral-like textile fabric with colorful colors and good coverage. It has fine texture, soft hand feeling, no pilling, not easy to shed, and beautiful appearance. In view of the obvious advantages of coral fleece, the demand for coral fleece products is on the rise, and the application fields are becoming more and more extensive. For example, gloves, nightgowns, fashion scarves, bath skirts, bathrobes, blankets, slippers, etc. are common in the market. Many products are made of coral. Cashmere is the raw material. This is due to its fine texture, no lint, no pilling, excellent water absorption performance, and beautiful appearance. The coral fleece fabric has a high fiber density, is coral-like, and has a soft body like coral. [0003] The coral fleece of the prior art has fine fineness, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/092D01D5/23D01D5/253D01F1/10D01F6/92D04C1/02D06C7/02D06C11/00D06C13/00
CPCD01D5/092D01D5/23D01D5/253D01F1/10D01F6/92D04C1/02D06C7/02D06C11/00D06C13/00D10B2401/022
Inventor 张元华朱承乾黄金刚沈建根
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap