A method for making a highly weather-resistant and fragile label material

A technology for label materials and manufacturing methods, which is applied to film/sheet adhesives, identification devices, film/sheet release coatings, etc., and can solve problems such as poor aging resistance and poor fragility of PVC fragile labels

Active Publication Date: 2021-12-14
浙江龙游道明光学有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a new manufacturing method of highly weather-resistant and fragile label materials for the disadvantages of poor aging resistance of paper fragile labels and poor fragility of PVC fragile labels in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for making a highly weather-resistant and fragile label material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] A method for making a highly weather-resistant and fragile label material, comprising the following steps:

[0065] Q1: Select a non-corona-treated PET substrate with a thickness of 36 μm, apply a weather-resistant layer coating on the surface of the PET substrate, place it at a temperature of 70 ° C for 2 minutes, and then dry it at 100 ° C for 3 minutes Form weather-resistant layer, make composite membrane A and wind up;

[0066] Q2: Coat the color layer paint on the surface of the weather-resistant layer of composite film A, place it in an environment with a temperature of 60°C to dry for 3 minutes, and then dry it in an environment with a temperature of 100°C for 3 minutes to form a color layer to obtain a composite film B and winding;

[0067] Q3: Form a covering layer on the surface of the colored layer of the composite film B, make a composite film C and wind it up;

[0068] Q4: Coat the pressure-sensitive adhesive layer paint on the grid-shaped release paper o...

Embodiment 2

[0109] A method for manufacturing a highly weather-resistant and fragile label material, comprising the following steps:

[0110] Q1: Select a non-corona-treated PET substrate with a thickness of 100 μm, apply a weather-resistant layer coating on the surface of the PET substrate, place it at 100°C for 3 minutes, and then dry it at 150°C for 5 minutes Form weather-resistant layer, make composite membrane A and wind up;

[0111] Q2: Coat the color layer paint on the surface of the weather-resistant layer of the composite film A, place it in an environment with a temperature of 100°C to dry for 5 minutes, and then dry it in an environment with a temperature of 150°C for 6 minutes to form a color layer to obtain a composite film B and winding;

[0112] Q3: Form a covering layer on the surface of the colored layer of the composite film B, make a composite film C and wind it up;

[0113] Q4: Coat the pressure-sensitive adhesive layer paint on the grid-like release paper or release...

Embodiment 3

[0154] A method for making a highly weather-resistant and fragile label material, comprising the following steps:

[0155] Q1: Select a non-corona-treated PET substrate with a thickness of 70 μm, apply a weather-resistant layer coating on the surface of the PET substrate, place it at a temperature of 85°C for 2.5 minutes, and then dry it at 125°C for 4 minutes Form weather-resistant layer, make composite membrane A and wind up;

[0156] Q2: Coat the color layer paint on the surface of the weather-resistant layer of the composite film A, place it in an environment with a temperature of 80°C to dry for 4 minutes, and then dry it in an environment with a temperature of 125°C for 4.5 minutes to form a color layer to obtain a composite film B and winding;

[0157] Q3: Form a covering layer on the surface of the colored layer of the composite film B, make a composite film C and wind it up;

[0158] Q4: Coat the pressure-sensitive adhesive layer coating on the grid-shaped release p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for making a highly weather-resistant and fragile label material, which includes the following steps: Q1: Select a non-corona-treated PET substrate with a thickness of 36 μm to 100 μm, and apply a weather-resistant coating on the surface of the PET substrate to obtain Composite film A and winding; Q2: Coating the color layer paint on the weather-resistant layer surface of composite film A to prepare composite film B and winding; Q3: Forming a covering layer on the surface of the color layer of composite film B to obtain a composite film C and rewinding; Q4: Coating the pressure-sensitive adhesive layer coating on the grid-shaped release paper or release film to obtain the composite film D; The sensitive adhesive layer is compounded to produce a highly weather-resistant and fragile label material. Through the above steps, the present invention can finally produce a highly weather-resistant and fragile label material, which has excellent chemical stability and physical properties, and meets high weather-resistant grade and fragile requirements, and has broad market prospects.

Description

technical field [0001] The invention relates to the technical field of label products, in particular to a method for making a highly weather-resistant and fragile label material. Background technique [0002] At present, fragile labels made of paper materials are widely used in the market, and paper fragile labels are widely used on the surface of machinery and equipment to play the role of identification and anti-counterfeiting, but there are major defects in the actual application process. If the paper fragile label is in the outdoor environment for a long time, the anti-counterfeiting effect will be greatly reduced due to its poor aging resistance. There are some fragile labels made of PVC on the market, but because the flexibility of the PVC material itself is too high, it cannot be fragile, and at the same time, the weather resistance level is low and it cannot be used outdoors for a long time, so the anti-counterfeiting effect is also low. It cannot meet the needs of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/25C09J7/50C09J7/38C09J7/40C09D133/04C09D129/14G09F3/02
CPCC09J7/255C09J7/50C09J7/385C09J7/40C09D133/04C09D129/14G09F3/02C09J2467/006C09J2203/334C09J2301/122C09J2301/302
Inventor 吴伟斌苏国芳舒林飞胡敏超姜振中
Owner 浙江龙游道明光学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap