Water-based environment-friendly paint and preparation method thereof

An environmentally friendly paint and water-based technology, applied in the field of paint, can solve problems such as poor adsorption capacity, achieve fast drying and curing speed, overcome construction difficulties, and achieve good overall performance.

Inactive Publication Date: 2020-03-17
郭涛
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention has good high temperature resistance, high coating hardness and good toughness, but it still contains more volatile substances, and its environmental protection performance needs to be further improved. Moreover, when the invention is applied to interior decoration, its adsorption capacity is insufficient after rolling and smearing. good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based environment-friendly paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of water-based environmental protection paint, it is characterized in that, comprises each raw material of following parts by weight to make: hyperbranched polyurethane acrylate 40 parts, based on acrylonitrile cross-linked polymer hollow microsphere 4 parts, chloro (difluoro) allyl acetate Ionized N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid 3 parts, 2,2-dimethylethylene boronic acid pinacol ester 1 part, N,N'-(1,2- Dihydroxyethylene) diacrylamide 1 part, benzoin 0.3 part, shell powder 10 parts, sodium hexametaphosphate 1 part, tributyl phosphate 0.5 part, water 25 parts.

[0031]The preparation method for ionizing N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid with allyl chloro(difluoro)acetate comprises the following steps: allyl chloro(difluoro)acetate Add 10g, 12.5g of N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid into 80g of diethyl ether, stir and react at 30°C for 4 hours, then remove the solvent by rotary evaporation, and wash the crude pr...

Embodiment 2

[0035] A kind of water-based environmental protection paint, it is characterized in that, comprises each raw material of following parts by weight to make: hyperbranched polyurethane acrylate 42 parts, based on acrylonitrile cross-linked polymer hollow microsphere 5 parts, chloro (difluoro) allyl acetate Ionized N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid 3.5 parts, 2,2-dimethylethylene boronic acid pinacol ester 1.5 parts, N,N'-(1,2- Dihydroxyethylene) diacrylamide 1.5 parts, benzoin ethyl ether 0.4 parts, pumice powder 11 parts, polycarboxylate sodium salt 1.5 parts, defoamer Deqian 31000.6 parts, water 27 parts.

[0036] The preparation method of ionizing N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid with allyl chloro(difluoro)acetate comprises the steps of: allyl chloro(difluoro)acetate Add 10 g of N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid 12.5 g into 90 g of ethyl acetate, stir and react at 33°C for 4.5 hours, then remove the solvent by rotary evapora...

Embodiment 3

[0040] A kind of water-based environmental protection paint, it is characterized in that, comprises each raw material of following parts by weight to make: hyperbranched polyurethane acrylate 45 parts, based on acrylonitrile cross-linked polymer hollow microsphere 6 parts, chloro (difluoro) allyl acetate Ionized N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid 4 parts, 2,2-dimethylethylene boronic acid pinacol ester 2 parts, N,N'-(1,2- 2 parts of dihydroxyethylene) diacrylamide, 0.45 parts of diphenyl ethyl ketone, 13 parts of attapulgite, 2 parts of sodium hexametaphosphate, 0.8 parts of defoamer BYK0888, 30 parts of water.

[0041] The preparation method for ionizing N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid with allyl chloro(difluoro)acetate comprises the following steps: allyl chloro(difluoro)acetate Add 10g, 12.5g of N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid into 100g of acetone, stir and react at 35°C for 5 hours, then remove the solvent by rotary eva...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based environment-friendly paint. The water-based environment-friendly paint is characterized by being prepared from the following raw materials by weight: 40-50 partsof hyperbranched urethane acrylate, 4-8 parts of acrylonitrile-based cross-linked polymer hollow microspheres, 3-5 parts of allyl chloro(difluoro)acetate ionized N, N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid, 1-3 parts of 2, 2-dimethylethenylboronic acid pinacol ester, 1-3 parts of N, N'-(1, 2-dihydroxyethylene)diacrylamide, 0.3-0.6 part of a photoinitiator, 10-15 parts of filler, 1-3 partsof a dispersing agent, 0.5-1.5 parts of a defoaming agent and 25-35 parts of water. The invention also discloses a preparation method of the water-based environment-friendly paint. The water-based environment-friendly paint disclosed by the invention has the characteristics of good comprehensive performance, large adhesive force to a base material, excellent storage and transportation stability, excellent corrosion resistance, flame retardance and high temperature resistance, fast drying and curing speed, convenient construction, large coating hardness, good toughness and weather resistance, and long in service life.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based environmental protection coating and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of industry, the problem of environmental pollution has attracted more and more attention. Countries around the world are taking strict measures to limit the emission of volatile organic compounds. Green materials have become the mainstream in the field of material research and application. In order to adapt to this trend, water-based coatings emerged as the times require and have become an extremely active research and development field. It is the development trend of the coatings industry at present and even in the future. It will definitely become the "new darling" of the coatings market and has a large market. potential. [0003] Water-based coatings use water as the dispersion medium and diluent. Different from tradition...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/16C09D133/20C09D5/08C09D5/18C09D7/63C09D7/65
CPCC08L2201/02C08L2201/08C08L2205/20C09D5/08C09D7/63C09D7/65C09D7/70C09D175/16C08L33/20C08K13/02C08K5/42C08K5/55C08K5/20
Inventor 郭涛
Owner 郭涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com