Degradable biaxially-oriented polylactic acid cigarette film and preparation method thereof

A technology of biaxial stretching and polylactic acid, applied in chemical instruments and methods, sustainable manufacturing/processing, flat products, etc., can solve problems such as environmental pollution and difficult application of optical properties, and achieve the effect of overcoming non-degradable

Active Publication Date: 2020-02-11
JIANGYIN ZHONGDA FLEXIBLE PLASTIC NEW MATERIALS CO LTD
View PDF7 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is: to overcome the environmental pollution caused by the existing polypropylene cigarette film and the problem that the existing polylactic acid film is difficult to apply to the cigarette film in terms of sliding performance, antistatic performance, optical performance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Degradable biaxially-oriented polylactic acid cigarette film and preparation method thereof
  • Degradable biaxially-oriented polylactic acid cigarette film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] A degradable biaxially stretched polylactic acid cigarette film, consisting of three layers of co-extruded outer layer A, core layer B and inner surface layer C, the layers A, B and C respectively include heat-sealable PLA or crystalline Type PLA, by mass percentage,

[0026] The A layer includes 80-90% heat-sealing type I PLA, 8-15% slip agent and 2-5% anti-blocking agent, and the heat-sealing type I PLA is composed of 70-80% crystalline PLA and 20-30% amorphous PLA composition;

[0027] The B layer includes 90-95% crystalline PLA, 1-5% antistatic agent, 1-2% stiffening agent, and 1-5% toughening agent;

[0028] The C layer includes 94-97% heat-sealing type II PLA, 2-3% slip agent and 1-3% anti-blocking agent, and the heat-sealing type II PLA consists of 75-85% crystalline PLA and 15-25% % composition of amorphous PLA.

[0029] The slip agent is one or more of oleic acid amide, erucamide and silicone; the anti-blocking agent is one of silicon dioxide, titanium dioxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of polylactic acid films, especially to a degradable biaxially-oriented polylactic acid cigarette film and a preparation method thereof. The invention overcomes the problems that an existing polypropylene cigarette film is non-degradable and an existing degradable polylactic acid film is difficult to be applied to cigarette films. According to a technical scheme, the degradable biaxially-oriented polylactic acid cigarette film is composed of a layer A, a layer B and a layer C which are co-extruded and stretched. The layer A comprises, by mass, 80%-90% of heat-seal I-type PLA, 8%-15% of a slipping agent and 2%-5% of an anti-blocking agent, wherein the heat-seal I-type PLA is composed of 70%-80% of crystalline PLA and 20%-30% of non-crystalline PLA. The layer B comprises 90-95% of crystalline PLA, 1-5% of an antistatic agent, 1-2% of a stiffening agent and 1-5% of a toughening agent. The layer C comprises 94-97% of heat-seal II-type PLA, 2-3%of a slipping agent and 1-3% of an anti-blocking agent, wherein the heat-seal II-type PLA is composed of 75-85% of crystalline PLA and 15-25% of non-crystalline PLA. The preparation method comprises the following steps: drying the above components according to the use amounts, carrying out melt extrusion, performing biaxially stretching, carrying out corona treatment, and then successively conducting rolling, aging, and slitting.

Description

technical field [0001] The invention relates to the technical field of polylactic acid films, in particular to a degradable biaxially stretched polylactic acid cigarette film and a preparation method thereof. Background technique [0002] The small packs of cigarettes or the large packs of whole cigarettes are wrapped with a cigarette film that mainly acts as a moisture-proof function. The current cigarette film is generally made of biaxially oriented polypropylene film. The advantage of this film is that it has good transparency. , good dimensional stability, high mechanical strength, and strong water vapor barrier ability; the disadvantage is that this kind of film is not degradable, and the annual consumption of cigarette film in my country exceeds 100,000 tons. From the perspective of energy saving and environmental protection, polypropylene cigarette film has a lot of white pollution and The problem of consuming large amounts of oil resources. [0003] Polylactic acid (a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/36B32B27/18B32B27/06B32B33/00C08L67/04C08L83/04C08K5/20C08K3/36C08K3/22C08K3/26C08K3/30C08K3/34C08L57/02C08L29/04C08J5/18B29D7/01B65D65/40
CPCB29D7/01B32B27/08B32B27/18B32B27/36B32B33/00B32B2250/03B32B2250/244B32B2307/54B32B2307/716B32B2367/00B32B2553/00B65D65/40C08J5/18C08J2367/04C08J2429/04C08J2457/02C08J2467/04C08J2483/04C08K3/34C08K3/36C08K5/20C08K2003/2241C08K2003/265C08K2003/3045C08K2201/011Y02W90/10
Inventor 王润霄刘俊萍朱罕王勇军黄刚庄阿强
Owner JIANGYIN ZHONGDA FLEXIBLE PLASTIC NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com