High-hardness anti-shearing aluminum alloy building material for doors and windows
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of aluminum alloy profiles and high hardness, which is applied in the field of building materials, can solve problems such as potential safety hazards, and achieve the effects of long service life, good weather resistance, and scientific and reasonable component ratios
Inactive Publication Date: 2020-01-03
沐鼎节能科技有限公司
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] With the rapid development of the economy, the construction industry has also developed rapidly. With the vigorous construction of high-rise buildings, higher requirements have been put forward for the hardness and shear resistance of aluminum alloy materials for doors and windows. Alloy materials can no longer meet the needs of high-rise buildings, and there are certain safety hazards
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] A high-hardness shear-resistant aluminum alloy building material for doors and windows, which includes an aluminum alloy profile body and a gold coating on the surface of the aluminum alloy profile body;
[0019] The aluminum alloy profile body is made of the following raw materials in parts by weight:
[0020] 30 parts of aluminum, 30 parts of manganese, 30 parts of copper, 15 parts of nickel, 20 parts of molybdenum, and 30 parts of chromium.
[0021] The golden coating is formed by electroplating zinc and copper elements.
Embodiment 2
[0023] A high-hardness shear-resistant aluminum alloy building material for doors and windows, an aluminum alloy profile body, and a gold coating on the surface of the aluminum alloy profile body;
[0024] The aluminum alloy profile body is made of the following raw materials in parts by weight:
[0025] 20 parts of aluminum, 20 parts of manganese, 20 parts of copper, 10 parts of nickel, 15 parts of molybdenum, and 20 parts of chromium.
[0026] The golden coating is formed by electroplating zinc and copper elements.
Embodiment 3
[0028] A high-hardness shear-resistant aluminum alloy building material for doors and windows, an aluminum alloy profile body, and a gold coating on the surface of the aluminum alloy profile body;
[0029] The aluminum alloy profile body is made of the following raw materials in parts by weight:
[0030] 10 parts of aluminum, 10 parts of manganese, 15 parts of copper, 5 parts of nickel, 10 parts of molybdenum, 10 parts of chromium;
[0031] The golden coating is formed by electroplating zinc and copper elements.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-hardness anti-shearing aluminum alloy building material for doors and windows. The high-hardness anti-shearing aluminum alloy building material comprises an aluminum alloy profile body and a golden plated layer plated on the surface of the aluminum alloy profile body; the aluminum alloy profile body is prepared from the following raw materials in parts by weight: 10-30 parts of aluminum, 10-30 parts of manganese, 15-30 parts of copper, 5-15 parts of nickel, 10-20 parts of molybdenum and 10-30 parts of chrome; and the golden plated layer is electroplated by zinc and copper. The aluminum alloy building material provided by the invention is scientific and reasonable in component ratio, is used for the doors and the windows, is high in hardness, resistant to shearing, high in strength, long in service life and good in weather resistance, can be used for 50 years or above, and can meet mechanical property requirements of high-rise buildings with 30 floors or above.
Description
technical field [0001] The invention relates to a building material, in particular to a high-hardness shear-resistant aluminum alloy building material for doors and windows. Background technique [0002] With the rapid development of the economy, the construction industry has also developed rapidly. With the vigorous construction of high-rise buildings, higher requirements have been put forward for the hardness and shear resistance of aluminum alloy materials for doors and windows. Alloy materials can no longer meet the needs of high-rise buildings, and there are certain safety hazards. [0003] Therefore, it is very necessary to design a kind of high hardness, shear resistance, high-strength aluminum alloy building material that a kind of door and window is used on the basis of prior art. Contents of the invention [0004] Purpose of the invention: The purpose of the invention is to aim at the defects of the prior art, and provide a high hardness, shear resistance, high ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more