Gray cast iron cylinder sleeve material and preparing method thereof

A technology of cylinder liner and gray cast iron, applied in the field of gray cast iron cylinder liner material and its preparation, can solve the problems of high cost, poor corrosion resistance, poor organizational stability, etc., achieve excellent wear reduction and corrosion resistance, and overcome low strength , high-strength effect

Active Publication Date: 2019-12-24
ZYNP GRP
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The tensile strength of bainite gray cast iron obtained by alloying and heat treatment can reach 400MPa, and the hardness can reach 330HB, but the high cost of bainite materials, poor structural stability, and poor corrosion resistance limit its wide application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gray cast iron cylinder sleeve material and preparing method thereof
  • Gray cast iron cylinder sleeve material and preparing method thereof
  • Gray cast iron cylinder sleeve material and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Pig iron, scrap steel, recycled material, iron sulfur powder, ferrosilicon, ferrophosphorus, ferromanganese, ferrochrome, electrolytic copper, ferroniobium, and ferroantimony are batched and melted, and the composition range is adjusted to the design range. The reading spectrometer detects the composition of molten iron, and the detection results are:

[0042] Carbon 3.43wt%, sulfur 0.065wt%, silicon 2.25wt%, phosphorus 0.091wt%, manganese 0.47wt%, chromium 0.42wt%, copper 0.65wt%, niobium 0.32wt%, antimony 0.038wt%, and the balance is iron.

[0043] The smelted molten iron was subjected to centrifugal casting of a metal model to obtain a blank with an outer circle of 136mm, an inner diameter of 107mm and a length of 252mm; the pouring temperature of the centrifugal casting was 1421°C, the pouring speed was 4kg / s, and the rotation speed was 1400 rpm.

[0044] The mold temperature of the obtained blank was 805°C. After exiting the mold, the blank was quickly air-cooled to...

Embodiment 2

[0049] Pig iron, scrap steel, recycled material, iron sulfur powder, ferrosilicon, ferrophosphorus, ferromanganese, ferrochrome, electrolytic copper, ferroniobium, and ferroantimony are melted as raw materials, and the composition range is adjusted to the design range, using photoelectric direct reading The spectrometer detects the composition of molten iron, and the detection results are:

[0050] Carbon 3.25wt%, sulfur 0.072wt%, silicon 2.43wt%, phosphorus 0.078wt%, manganese 0.35wt%, chromium 0.33wt%, copper 0.72wt%, niobium 0.42wt%, antimony 0.025wt%, and the balance is iron.

[0051] The smelted molten iron was subjected to centrifugal casting of a metal model to obtain a blank with an outer circle of 132mm, an inner diameter of 105mm, and a length of 257mm; 1385 rpm.

[0052] The mold temperature of the obtained blank was 792°C. After exiting the mold, the blank was quickly air-cooled to 580°C and then air-cooled to room temperature, and then annealed in a trolley annea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention provides a gray cast iron cylinder sleeve material. The components of the gray cast iron cylinder sleeve material include 3.25-3.5 wt% of carbon, 0.06-0.08 wt% of sulfur, 2.0-2.5 wt% ofsilicon, 0.06-0.1 wt% of phosphorus, 0.3-0.5 wt% of manganese, 0.3-0.5 wt% of chromium, 0.6-0.8 wt% of copper, 0.35-0.45 wt% of niobium, 0.02-0.04 wt% of antimony and the balance iron. By means of thealloy element and process design of the cylinder sleeve material, the metallographic structure of the prepared gray cast iron cylinder sleeve material comprises flake graphite, fine lamellar pearliteand about 1% of iron phosphide eutectic, and meanwhile niobium carbonitride is evenly distributed in the metallographic structure. The prepared cylinder sleeve material has high strength and excellent wear reduction partner adaptability and corrosion resistance and is stable in structure and low in cost.

Description

technical field [0001] The invention relates to the technical field of automobile engine accessories, in particular to a gray cast iron cylinder liner material and a preparation method thereof. Background technique [0002] Cylinder liners are the core components of automobile engines. At present, the materials of cylinder liners are mostly gray cast iron. The gray cast iron cylinder liner material mainly improves its strength and wear resistance through alloy strengthening and heat treatment; the tensile strength of pearlitic gray cast iron is generally below 320MPa, and the hardness is generally less than 280HB. The tensile strength of bainitic gray cast iron obtained by alloying and heat treatment can reach 400MPa, and the hardness can reach 330HB, but the disadvantages of bainitic material, such as high cost, poor structural stability and poor corrosion resistance, limit its wide application. Therefore, developing a gray cast iron cylinder liner material with high stren...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C37/10C22C37/06C21D1/26C21D5/00
CPCC21D1/26C21D5/00C21D2211/006C21D2211/009C22C33/08C22C37/06C22C37/10
Inventor 徐超薛慧敏卢琼秦小才
Owner ZYNP GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More