Fiber composite core stranded metal wire sucker rod and preparation method and application thereof

A technology of fiber composite material and metal wire, which is applied in the direction of drill pipe, earthwork drilling, drilling equipment, etc., can solve the problems of poor corrosion resistance and impact resistance of sucker rods, large damage of sucker rods, and influence on use and promotion, etc., to achieve Excellent impact resistance, improve service life, and improve the effect of impact resistance

Active Publication Date: 2019-12-13
SHANDONG UNIV
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the inventors have further researched and found that although this type of carbon fiber sucker rod has a relatively good flexibility effect, with the continuous improvement of the reliability of modern oil production and the continuous improvement of energy saving and production increase requirements, the composite material sucker rod with a single structure is also not resistant to corrosion. And the problem of poor impact resistance; and the impact on the well wall during operation is relatively large, and the damage to the sucker rod is relatively large, which affects its use and promotion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber composite core stranded metal wire sucker rod and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] As mentioned above, although the carbon fiber sucker rod has better flexibility, the composite sucker rod with a single structure also has the problems of poor corrosion resistance and poor impact resistance; moreover, it has a large impact on the well wall during operation. The damage to the sucker rod is relatively large. Therefore, the invention provides a fiber composite material core stranded metal wire sucker rod and a preparation method thereof.

[0027] In some typical embodiments, in the rigid layer, the fiber filaments are high modulus carbon fibers, or high modulus carbon fibers mixed with glass fibers and / or inorganic ceramic fibers.

[0028] Further, the inorganic ceramic fiber includes: any one of alumina fiber, silicon carbide fiber, boron carbide fiber, basalt fiber, quartz fiber and the like.

[0029] In some typical embodiments, in the rigid layer, the thermosetting resin includes: any one of epoxy resin, phenolic resin, unsaturated polyester resin, u...

Embodiment 1

[0050] refer to figure 1 , an example of a fiber composite material core stranded metal wire sucker rod, its structure includes: a rod body, a wire structure layer and an impact-resistant and anti-corrosion thermoplastic layer; wherein:

[0051] The rod body is divided into a rigid layer 1 and a protective layer 2 wound on the surface of the rigid layer; the rigid layer 1 has a diameter of 7.0mm and is made of T700 carbon fiber filaments compounded with epoxy resin, and the thickness of the protective layer 2 is 0.5 mm. mm, its material is glass fiber reinforced yarn; the resin content in the rod body is 20%.

[0052] The metal wire structure layer 3 is formed by twisting metal wires on the surface of the protective layer, and three layers of circular high-strength stainless steel wires are twisted, wherein the inner layer of metal wires is twisted clockwise, the second outer layer is twisted counterclockwise, and the outermost The layers are twisted clockwise and the wires a...

Embodiment 2

[0062] A fiber composite material core stranded metal wire sucker rod, the same as embodiment 1, the difference is:

[0063] The diameter of the rigid layer 1 is 8mm, which is made of M40 carbon fiber mixed with high-strength basalt fiber and then compounded with epoxy resin. The thickness of the protective layer 2 is 1.5mm, which is formed by mixing glass fibers and basalt fibers; the resin content in the rod body is 21%.

[0064] The metal wire structure layer 3 is formed by twisting metal wires on the surface of the protective layer, and three layers of Z-shaped high-strength aluminum alloy wires are twisted, wherein the metal wires of the inner layer are twisted clockwise, and the second outer layer is twisted counterclockwise. The outer layer is twisted clockwise, and the cross-section of the high-strength aluminum alloy wire is equivalent to a round wire with a diameter of 1.5 mm. The strength of the high-strength aluminum alloy wire is greater than 1000 MPa, the fillin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of composite sucker rods, in particular to a fiber composite core stranded metal wire sucker rod and a preparation method and application thereof. The sucker rod structure comprises a rod body, a metal wire structural layer and an impact-resistant anti-corrosion thermoplastic layer, wherein the rod body is divided into a rigid layer and a protective layer wound on the surface of the rigid layer; the rigid layer is formed by composite thermosetting resin of fiber filaments, and the protective layer is made of high-strength fibers; the metal wire structural layer is formed by stranding metal wire on the surface of the protective layer; and the impact-resistant anti-corrosion thermoplastic layer is coated on the surface of the metal wire structurelayer. The sucker rod has good impact resistance and bending performance, one or more layers of high-strength metal wires are stranded outside, the sucker rod is endowed with excellent impact resistance, meanwhile, the weight of the sucker rod is increased to a certain extent, the sucker rod can be guaranteed to be in a stretched state all the time in the running process, the operation can be completed without using a counterweight rod, and the cost is reduced.

Description

technical field [0001] The invention relates to the technical field of composite sucker rods, in particular to a fiber composite core stranded metal wire sucker rod and its preparation method and application. Background technique [0002] The information disclosed in the Background of the Invention is only intended to increase the understanding of the general background of the invention, and is not necessarily to be taken as an acknowledgment or any form of suggestion that the information constitutes the prior art that is already known to those skilled in the art. [0003] With the development of my country's oil recovery technology, under the background of deteriorating oil production environment, the field of oil production puts forward higher requirements on the efficiency of oil production and the effective utilization of abandoned oil wells. Traditional steel sucker rods are gradually being replaced by composite material sucker rods. . At present, the composite sucker r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E21B17/00E21B17/10B29C48/154B29C48/92
CPCB29C48/154B29C48/92B29C2948/926B29C2948/92704E21B17/00E21B17/1071E21B17/1085
Inventor 朱波王永伟乔琨高学平赵圣尧刘玉兰张敏刘兵刘洪广
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com