A kind of zifs nanosheet/chitosan/diatomite hybrid and preparation method thereof

A diatomite and hybrid technology, applied in the field of flame retardants, can solve the problem of low flame retardant efficiency of diatomite

Active Publication Date: 2021-09-28
ANHUI UNIVERSITY OF ARCHITECTURE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some researchers have applied diatomaceous earth to flame-retardant polymers, and their research has found that the disk-like structure of diatomite can act as a physical barrier to a certain extent, thereby improving the flame retardancy of polymers; however, using silicon alone The flame retardant efficiency is not high when using algae

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1. Preparation of Flame Retardant and Smoke Suppressant

[0018] a) preparation concentration is the chitosan aqueous solution of 0.010kg / L and the zinc nitrate hexahydrate aqueous solution that concentration is 0.009kg / L respectively, the solvent is deionized water, the two kinds of solutions are mixed and ultrasonically dispersed, and the mixed solution is moved into In the flask, mechanically stirred and reacted for 2 hours, 2-methylimidazole was dissolved in deionized water to prepare an aqueous solution with a concentration of 0.024kg / L, and dropped into the above-mentioned flask, reacted for 2 hours, centrifugally washed and dried to obtain the intermediate product ZC, wherein The volume ratio of chitosan, zinc nitrate hexahydrate, and 2-methylimidazole solution is 2:3:3;

[0019] b) Prepare the dispersion of the above-mentioned intermediate product ZC with a concentration of 0.010kg / L, take diatomaceous earth to prepare a dispersion with a concentration of 0.013k...

Embodiment 2

[0026] 1. Preparation of Flame Retardant and Smoke Suppressant

[0027] a) preparation concentration is the chitosan aqueous solution of 0.010kg / L and the cobalt nitrate hexahydrate aqueous solution that concentration is 0.020kg / L respectively, solvent is deionized water, two kinds of solutions are mixed and ultrasonically dispersed, mixed solution is moved into In the flask, mechanically stirred and reacted for 2 hours, 2-methylimidazole was dissolved in deionized water to prepare an aqueous solution with a concentration of 0.024kg / L, and was dropped into the above-mentioned flask, reacted for 4 hours, centrifugally washed and dried to obtain the intermediate product ZC, wherein The volume ratio of chitosan, zinc nitrate hexahydrate, and 2-methylimidazole solution is 2:3:3;

[0028] b) Prepare the dispersion of the above-mentioned intermediate product ZC with a concentration of 0.010kg / L, take diatomaceous earth to prepare a dispersion with a concentration of 0.010kg / L, mix t...

Embodiment 3

[0035] 1. Preparation of Flame Retardant and Smoke Suppressant

[0036] a) preparation concentration is the chitosan aqueous solution of 0.010kg / L and the cobalt nitrate hexahydrate aqueous solution that concentration is 0.020kg / L respectively, solvent is deionized water, two kinds of solutions are mixed and ultrasonically dispersed, mixed solution is moved into In the flask, mechanically stirred and reacted for 2 hours, 2-methylimidazole was dissolved in deionized water to prepare an aqueous solution with a concentration of 0.024kg / L, and dropped into the above-mentioned flask, reacted for 3 hours, centrifugally washed and dried to obtain the intermediate product ZC, wherein The volume ratio of chitosan, zinc nitrate hexahydrate, and 2-methylimidazole solution is 2:3:3;

[0037] b) Prepare the dispersion liquid of the above-mentioned intermediate product ZC with a concentration of 0.010kg / L, take diatomaceous earth to prepare a dispersion liquid with a concentration of 0.012k...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strength at breakaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of flame retardants, and specifically relates to a ZIFs nanosheet / chitosan / diatomite hybrid, wherein chitosan molecules are first combined with cobalt or zinc ions in ZIFs nanosheets through nitrogen elements , and then prepared by combining amino groups with hydroxyl groups on the surface of diatomite. When the hybrid is added to the polymer, chitosan can be used as an effective carbon source, and diatomaceous earth and ZIFs nanosheets have a certain physical barrier effect. At the same time, cobalt oxide or zinc oxide produced by thermal decomposition of ZIFs nanosheets and SiO 2 The acidic active sites on the surface can promote the formation of a dense carbon layer, which can play a good barrier role, thereby improving the flame retardant and smoke suppression properties of polymer materials. The invention also relates to a preparation method of the above-mentioned hybrid compound, which has low requirements for reaction, easy-to-obtain raw materials and simple process, uses water as a solvent, has no pollution to the environment, and is environmentally friendly.

Description

technical field [0001] The invention belongs to the field of flame retardants, and in particular relates to a ZIFs nanosheet / chitosan / diatomite hybrid and a preparation method thereof. Background technique [0002] With the rapid development of polymer materials, it is widely used in various fields of the national economy. However, polymer materials are flammable and release a large amount of toxic and harmful substances during combustion. Some traditional flame retardants contain toxic and harmful substances. With the improvement of people's awareness of environmental protection, people pay more and more attention to the development of low-toxicity and environment-friendly flame retardants. [0003] Diatomaceous earth is a siliceous rock, a biogenic siliceous sedimentary rock composed mainly of the remains of ancient diatoms. Its chemical composition is SiO 2 Mainly, available SiO 2 ·nH 2 O said. my country's diatomite reserves are 320 million tons, and the prospectiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L5/08C08K3/36C08K5/3445
CPCC08K3/36C08K5/3445C08K2201/011C08L5/08
Inventor 徐文总闫弘毅钟迪杨凯杜艳平
Owner ANHUI UNIVERSITY OF ARCHITECTURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com