Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method of solid vanadyl sulfate

A technology of solid sulfuric acid and vanadyl, applied in chemical instruments and methods, vanadium compounds, inorganic chemistry, etc., can solve the problems of environmental pollution, excessive ammonia nitrogen in extraction wastewater, etc., and achieve the effects of low cost, preventing overflow and improving the efficiency of back extraction.

Active Publication Date: 2022-04-15
INST OF RESOURCES UTILIZATION & RARE EARTH DEV GUANGDONG ACAD OF SCI
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the first stage of the method, the alkaline extraction, impurity removal and purification process needs to introduce ammonium chloride as a stripping agent, which will cause the environmental problem of excessive ammonia nitrogen pollution in the extraction wastewater.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A preparation method of solid vanadyl sulfate, said method comprising the steps of:

[0035] (1) Take 1000ml vanadium concentration as 30g / L, pH value is 3.1 converter steelmaking vanadium slag calcification roasting, the obtained vanadium leaching solution after leaching carries out extraction and clarification treatment, wherein oil-water ratio O / A=1:2, extraction time 10min, clarification 10min extracts and removes iron, obtains the raffinate containing vanadium, and the extraction system used for extraction is N235 (trioctylamino ammonium), TBP (tributyl phosphate) and sulfonated kerosene, and the volume ratio of the three is 30: 10:60; after the separation of the two phases, use 2M sulfuric acid solution to back-extract the organic phase for regeneration, wherein the oil-water ratio O / A=3:1, the back-extraction time is 10min, and the clarification treatment after back-extraction is 3min;

[0036] (2) Add sulfuric acid to the vanadium-containing raffinate after iron...

Embodiment 2

[0042] A preparation method of solid vanadyl sulfate, said method comprising the steps of:

[0043] (1) Take 1000ml of converter steelmaking vanadium slag with a vanadium concentration of 25g / L and a pH value of 9.1 for sodium roasting and leaching to extract and clarify the vanadium leaching solution, wherein the oil-water ratio O / A=1:5, extract Time 10min, clarification 10min extraction and iron removal, obtain raffinate containing vanadium, the extraction system used for extraction is N235 (trioctylamino ammonium), TBP (tributyl phosphate) and sulfonated kerosene, the volume ratio of the three is 30 :10:60; after the two phases are separated, use 2M sulfuric acid solution to back-extract the organic phase for regeneration, wherein the oil-water ratio O / A=4:1, the back-extraction time is 10min, and the clarification treatment after back-extraction is 3min;

[0044] (2) Add sulfuric acid to the vanadium-containing raffinate after iron removal to adjust the pH of the solution ...

Embodiment 3

[0050] A preparation method of solid vanadyl sulfate, said method comprising the steps of:

[0051] (1) Take 1000ml vanadium concentration as 20g / L, pH value is 2.5 converter steelmaking vanadium slag calcification roasting, the obtained vanadium leaching solution after leaching carries out extraction and clarification treatment, and wherein oil-water ratio O / A=1:3, extraction time 10min, clarification 10min extracts and removes iron, obtains the raffinate containing vanadium, and the extraction system used for extraction is N235 (trioctylamino ammonium), TBP (tributyl phosphate) and sulfonated kerosene, and the volume ratio of the three is 30: 10:60; after the separation of the two phases, use 2M sulfuric acid solution to back-extract the organic phase for regeneration, wherein the oil-water ratio O / A=3:1, the back-extraction time is 10min, and the clarification treatment after back-extraction is 3min;

[0052] (2) Add sulfuric acid to the vanadium-containing raffinate after ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of solid vanadyl sulfate, which takes the vanadium-containing solution obtained after roasting and leaching the vanadium slag of the steelmaking converter as the object, through targeted iron removal, and then carries out the conversion of vanadium, and then removes impurities by solvent extraction Purification, high-purity vanadyl sulfate solution is obtained through mixed acid back extraction, and solid vanadyl sulfate is obtained by direct negative pressure distillation and crystallization. This method has a simple process flow and low cost, and can realize large-scale industrial production. The present invention purifies the tetravalent vanadium solution by adopting the impurity removal and purification technology of the solvent extraction method, controls appropriate technical parameter conditions, and can effectively remove impurity elements such as iron, manganese, chromium, zinc, calcium, and magnesium.

Description

technical field [0001] The invention belongs to the technical field of impurity removal and purification of inorganic compound materials, and in particular relates to a preparation method of solid vanadyl sulfate. Background technique [0002] Vanadium is a rare metal that can store sunlight. All-vanadium redox flow battery is recognized as the preferred technology for large-scale grid energy storage and a reliable solution for efficient solar energy storage. Solar energy has the characteristics of volatility and dispersion, and it is necessary to develop an efficient energy storage system to deal with the unbalanced grid connection of solar power generation and the time difference between supply and demand. [0003] All-vanadium redox flow battery (VRB) is an excellent energy storage device, and the battery capacity depends on the amount of electrolyte. VRB batteries have no solid-state reaction, no change in the structure and form of electrode materials, and the electroly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G31/00
CPCC01G31/00C01P2006/80
Inventor 郭秋松杨莉花曹洪杨戴子林饶帅刘志强李伟高远陶进长张魁芳
Owner INST OF RESOURCES UTILIZATION & RARE EARTH DEV GUANGDONG ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com