High-temperature-resistant and corrosion-resistant sinking roller and manufacturing method thereof

A manufacturing method and corrosion-resistant technology, applied in coating, metal material coating process, hot-dip plating process, etc., can solve the problem of sinking roller being easily damaged by corrosion, achieve good wear resistance, prolong service life, slow down The effect of corrosion rate

Active Publication Date: 2019-10-08
MAANSHAN IRON & STEEL CO LTD
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] Aiming at the problem that the sinking roll of the hot-dip aluminum plating production line is easily damaged by corrosion in the prior art, the present invention provides a high-temperature-resistant and corrosion-resistant sinking roll and its manufacturing method. The coating material greatly slows down the corrosion rate of the sinking roller and effectively prolongs the service life of the sinking roller

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant and corrosion-resistant sinking roller and manufacturing method thereof
  • High-temperature-resistant and corrosion-resistant sinking roller and manufacturing method thereof
  • High-temperature-resistant and corrosion-resistant sinking roller and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0055] The present invention will be further described below in conjunction with specific embodiments and accompanying drawings.

[0056] Table 1 is the material and process parameter data of embodiment and comparative example;

[0057] Table 2 is a comparison of the performance of the sink rolls of the examples and the comparative examples.

[0058] Table 1

[0059]

[0060] Table 1 (continued)

[0061]

[0062] Table 2 (√ stands for qualified, × stands for unqualified)

[0063] category Coating Toughness Coating high temperature wear resistance Coating high temperature corrosion resistance Sinking roller life Example 1 √ √ √ 120h Example 2 √ √ √ 150h Example 3 √ √ √ 132h Comparative example 1 √ √ × 96h Comparative example 2 √ × √ 80h Comparative example 3 × × × 72h

[0064] figure 1 It is a structural schematic diagram of the sinking roller of the present application, figure 2 For the sin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant and corrosion-resistant sinking roller and a manufacturing method thereof, and belongs to the field of hot dipping equipment. The high-temperature-resistant and corrosion-resistant sinking roller comprises a roller body and a roller shaft, the surfaces of the roller body and the roller shaft are sprayed with coatings, and coating materials are prepared from following raw materials including, by weight, 70-90 parts of WC, 8-15 parts of Co and 3-15 parts of Cr3C2; the surface of the roller body is circumferentially provided with a groove, thebottom surface of the groove is a circular arc transition curved surface; the roller body is made of 316L stainless steel; and the roller shaft is made of a tungsten chromium cobalt alloy. The sinkingroller is made through groove processing, pre-treatment, coating material preparation and supersonic flame spraying. According to the high-temperature-resistant and corrosion-resistant sinking rollerand the manufacturing method, the surfaces of the roller body and the roller shaft of the sinking roller are sprayed with the coating materials with the specific components, the corrosion rate of thesinking roller is greatly reduced, and the service life of the sinking roller is effectively prolonged.

Description

technical field [0001] The invention belongs to the field of hot-dipping equipment, and more specifically relates to a high-temperature-resistant and corrosion-resistant sinking roller and a manufacturing method thereof. Background technique [0002] Hot-dip aluminized steel sheet has excellent corrosion resistance, high temperature oxidation resistance, heat reflectivity and ecological characteristics, and its service life is more than 5 times longer than that of hot-dip galvanized sheet. It is widely used in automobiles, home appliances and other fields at home and abroad. [0003] The temperature in the pot of the hot-dip aluminum plating production line is relatively high, nearly 700°C, and the aluminum liquid will strongly corrode the sinking roller, correcting roller and their bearings in the aluminum pot. At the same time, aluminum slag is more likely to be produced in the aluminum pot, and the accumulation of aluminum slag on the surface of ordinary sinking rolls wil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/12C23C2/40C23C4/06C23C4/02C22C29/08C23C4/129C22C19/07C22C30/00
CPCC22C19/07C22C29/08C22C30/00C23C2/003C23C2/12C23C2/40C23C4/02C23C4/06C23C4/129
Inventor 李伟刚赵云龙王滕柴立涛周忠臣张百勇何峰
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com