High-strength stainless steel hollow composite plate for building construction or template and preparation method of composite plate

A technology of building construction and stainless steel, applied in the direction of chemical instruments and methods, laminated, layered products, etc., can solve the problems that cannot be applied to the fields of building construction and formwork, and cannot meet the load-bearing strength and life requirements of ordinary building wall panels or floor slabs, Low strength and other problems, to achieve high toughness, expand the scope and scene of adaptation, and reduce the effect of self-weight

Active Publication Date: 2019-09-17
前海索新发展科技(深圳)有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitations of its material and processing technology, this kind of honeycomb hollow board has very low strength and limited service life within a few years, so it cannot be applied to the field of building construction and formwork in essence.
[0005] Furthermore, at present, for example, the yield strength of a 2.5mm thick stainless steel plate is generally less than 0.235kMPa, which cannot meet the load-bearing strength and 70-year life requirements of ordinary building wall panels or floor slabs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength stainless steel hollow composite plate for building construction or template and preparation method of composite plate
  • High-strength stainless steel hollow composite plate for building construction or template and preparation method of composite plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] see Figure 1-2 , the invention provides a high-strength stainless steel hollow composite panel for building construction or formwork, characterized in that it comprises:

[0052] Stainless steel panel 1;

[0053] Stainless steel bottom plate 3;

[0054] A stainless steel honeycomb panel 2, which is arranged between the stainless steel panel 1 and the stainless steel bottom plate 3, and the stainless steel honeycomb panel 2 is integrally formed by molding; and

[0055] Stainless steel side plates 4, 5, which are arranged for edge sealing between the stainless steel panel 1 and the stainless steel bottom plate 3;

[0056] The chemical composition and mass fraction of the stainless steel panel 1, stainless steel bottom plate 3, stainless steel honeycomb panel 2 and stainless steel side panels 4 and 5 are: C 0.065~0.19, Si≤1, Mn≤1, P≤0.080, S≤0.015 , 13.00≤Cr≤15.00, 1.5≤Ni≤2.2, Mo≤0.15, Cu≤0.25, the balance is Fe;

[0057] The high-strength stainless steel hollow compo...

Embodiment 2

[0082] see Figure 1-2 , the invention provides a high-strength stainless steel hollow composite panel for building construction or formwork, characterized in that it comprises:

[0083] Stainless steel panel 1;

[0084] Stainless steel bottom plate 3;

[0085] A stainless steel honeycomb panel 2, which is arranged between the stainless steel panel 1 and the stainless steel bottom plate 3, and the stainless steel honeycomb panel 2 is integrally formed by molding; and

[0086] The stainless steel side panels 4 and 5 are arranged between the stainless steel panel 1 and the stainless steel bottom panel 3 for edge sealing, and are arranged around the stainless steel honeycomb panel 2 .

[0087] Preferably, the wall thickness of the stainless steel panel 1 and the stainless steel bottom plate 3 is 0.5mm, the wall thickness of the honeycomb of the stainless steel honeycomb panel 2 is 0.5mm, the center distance of the honeycomb is 100mm, and the size of the honeycomb is

[0088]...

Embodiment 3

[0097] Preferably, see Figure 1-2 , the present invention also provides a high-strength stainless steel hollow composite panel for building construction or formwork, characterized in that it comprises:

[0098] Stainless steel panel 1;

[0099] Stainless steel bottom plate 3;

[0100] A stainless steel honeycomb panel 2, which is arranged between the stainless steel panel 1 and the stainless steel bottom plate 3, and the stainless steel honeycomb panel 2 is integrally formed by molding; and

[0101] The stainless steel side plates 4, 5 are arranged between the stainless steel panel 1 and the stainless steel bottom plate 3, and are arranged around the stainless steel honeycomb panel 2.

[0102]Preferably, the chemical composition and mass fraction of the stainless steel panel 1, stainless steel bottom plate 3, stainless steel honeycomb panel 2 and stainless steel side panels 4, 5 are: C 0.065~0.19, Si≤1, Mn≤1, P≤0.080, S≤0.015, 13.00≤Cr≤15.00, 1.5≤Ni≤2.2, Mo≤0.15, Cu≤0.25, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-strength stainless steel hollow composite plate for building construction or template. The composite plate comprises a stainless steel surface plate, a stainless steel bottom plate, a stainless steel honeycomb plate and stainless steel side plates, wherein the stainless steel honeycomb plate is arranged between the stainless steel surface plate and the stainless steel bottom plate, and the stainless steel honeycomb plate is obtained by adopting mold pressing integrated molding; and the stainless steel side plates are arranged between the stainless steel surface plate and the stainless steel bottom plate for edge sealing.

Description

technical field [0001] The invention belongs to the technical field of building construction or formwork of buildings such as buildings, and more specifically relates to a high-strength stainless steel hollow composite plate for building construction or formwork and a manufacturing method thereof. Background technique [0002] At present, the traditional cast-in-place shear wall structure has problems such as heavy on-site workload, waste of building materials, waste of building water, and serious environmental pollution. The vertical connection structure of prefabricated shear walls mostly adopts sleeve grouting connection, steel bar welding connection and indirect lap joint grouting anchor connection. The sleeve grouting connection has problems such as high cost of the sleeve and is not suitable for the use of steel bars with thinner cross-sections; the steel bar welding connection has problems such as heavy on-site welding workload and difficult to guarantee welding quali...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/18B32B15/01B32B3/12B32B7/04B32B37/10C22C38/02C22C38/04C22C38/42C22C38/44C21D8/02
CPCB32B3/12B32B7/04B32B15/011B32B37/10C21D8/0205C22C38/02C22C38/04C22C38/42C22C38/44
Inventor 沈玮琳
Owner 前海索新发展科技(深圳)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More