Preparation method of waterproof fireproof paint

A technology for fire-retardant coatings and preparation steps, which is applied to fire-resistant coatings, coatings, protein coatings, etc., can solve the problems of poor water resistance, poor fire-proof effect, and many engineering rework of fire-resistant coatings, and achieves good heat insulation effect and spacing. The effect of enlargement and high temperature resistance

Inactive Publication Date: 2019-08-23
曾祥民
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem mainly solved by the present invention is that the water resistance of the currently used fireproof coatings is poor, so that many painted fireproof coatings will quickly cause bulges and fall off under the washing of rainwater, resulting in many engineering reworks and poor fireproofing effects The defect of the present invention provides a kind of preparation method of waterproof and fireproof coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0030] Preparation of inorganic powder:

[0031] Put expanded graphite and sericite into a pulverizer at a mass ratio of 2:1, pulverize at a speed of 900r / min for 1 hour, and put the ground material into a planetary ball mill after pulverization. After grinding for 20 minutes under the condition of 120 r / min, pass through a 50-mesh sieve to obtain inorganic powder.

[0032] Preparation of modified inorganic powder:

[0033] Collect kelp and put it into a grinder, grind for 20 minutes to obtain kelp powder, mix the kelp powder with the above-mentioned inorganic powder in a mass ratio of 1:5 to obtain a substrate to be fermented, and mix 14 parts of the fermentation substrate by weight. Put the material, 2 parts of river bottom sludge and 4 parts of distilled water into the fermenter, seal the mouth of the fermenter, place the fermenter in a greenhouse with a temperature of 20°C, and ferment for 1 week to obtain modified inorganic powder for later use.

[0034] Preparation of mo...

example 2

[0043] Preparation of inorganic powder:

[0044] Put expanded graphite and sericite into a pulverizer at a mass ratio of 2:1, pulverize at a speed of 950r / min for 1 hour, and put the ground material into a planetary ball mill after pulverization. After grinding for 25 minutes under the condition of 130 r / min, pass through a 50-mesh sieve to obtain inorganic powder.

[0045] Preparation of modified inorganic powder:

[0046] Collect kelp and put it into a grinder, grind for 25 minutes to obtain kelp powder, mix the kelp powder with the above-mentioned inorganic powder in a mass ratio of 1:5 to obtain a substrate to be fermented, and mix 15 parts of the fermentation substrate by weight. Put the material, 2 parts of river bottom sludge and 5 parts of distilled water into the fermenter, seal the mouth of the fermenter, place the fermenter in a greenhouse with a temperature of 25° C., and ferment for 1 week to obtain modified inorganic powder for future use.

[0047] Preparation ...

example 3

[0056] Preparation of inorganic powder:

[0057] Put the expanded graphite and sericite into the pulverizer at a mass ratio of 2:1, pulverize at a speed of 1000r / min for 2 hours, and put the ground material into a planetary ball mill after pulverization. After grinding for 30 minutes under the condition of 140 r / min, pass through a 50-mesh sieve to obtain inorganic powder.

[0058] Preparation of modified inorganic powder:

[0059] Collect kelp and put it into a grinder, grind for 30 minutes to obtain kelp powder, mix the kelp powder with the above-mentioned inorganic powder in a mass ratio of 1:5 to obtain a substrate to be fermented, and mix 16 parts of the fermentation substrate by weight. Put the material, 3 parts of river bottom sludge and 6 parts of distilled water into the fermenter, seal the mouth of the fermenter, place the fermenter in a greenhouse with a temperature of 30° C., and ferment for 2 weeks to obtain modified inorganic powder for future use.

[0060] Pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a waterproof fireproof paint, and belongs to the technical field of paint preparation. According to the preparation method, expandable graphite and sericite are taken as raw materials to form a carbonaceous layer with excellent bonding effect with a building substrate; sea-tangle is adopted as a raw material to provide an obtained fireproof paint with water resistance; glass fiber excellent in thermal insulation effect is adopted to improve the water resistance of the fireproof paint greatly, glass fiber and an alkali solution are reacted to improve the bulking capacity of glass fiber, glass fiber thermal insulation performance flame resistance are improved greatly, and the thermal insulation performance flame resistance of the fireproof paint are improved; rice husk is taken as a raw material to obtain lignin, lignin is decomposed into cellulose for bonding and stretching effect in the fireproof paint; a modified inorganic matter powder, standby modified glass fiber, the above modified phenolic resin, and egg white protein are mixed and stirred to form a structure similar to a foam thermal insulation layer, so that the thermal insulation performance flame resistance of the fireproof paint are improved greatly, and a promising application prospect is achieved.

Description

technical field [0001] The invention relates to a preparation method of a waterproof and fireproof coating, which belongs to the technical field of coating preparation. Background technique [0002] With the continuous and rapid growth of my country's economy and the massive construction of infrastructure, people's living standards have improved and their awareness of environmental protection has gradually increased. In modern home decoration, the use of various flammable materials is becoming more and more common. In recent years, several fires have occurred across the country, causing a large number of casualties and property losses. Therefore, building fire protection has become the main technical index affecting building safety performance. [0003] A very common fire prevention treatment method is to use fire retardant coatings. Coating fire-resistant coatings on the interior and exterior walls of buildings not only plays a decorative role on materials, but also prolo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/14C09D189/00C09D5/18C09D7/62
CPCC08L2201/02C09D5/18C09D7/62C09D7/70C09D161/14C08L89/00C08K9/02C08K7/14C08K7/24C08K3/34C08K13/06
Inventor 曾祥民
Owner 曾祥民
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap