A kind of photo-thermal dual curing 3D printing method and its product

A 3D printing and dual curing technology, applied in the field of 3D printing, can solve the problems of loss of toughness and brittle products, and achieve the effect of improving the elongation at break, strengthening the application value, and broadening the scope of application.

Active Publication Date: 2021-09-28
HANGZHOU NORMAL UNIVERSITY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] It can be seen that if the epoxy resin thermal curing system is used as the dark curing system in the light-dark dual curing system in 3D printing, the thermal curing temperature of the epoxy resin will generally be higher than that of the first-stage light-curing polymer glass. temperature (the glass transition temperature of this product is higher than room temperature), so the light-cured polymerization product becomes brittle after returning to room temperature, resulting in epoxy resin light-dark dual-cure products are easy to become brittle and lose basic toughness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of photo-thermal dual curing 3D printing method and its product
  • A kind of photo-thermal dual curing 3D printing method and its product
  • A kind of photo-thermal dual curing 3D printing method and its product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Preparation of polyurethane polyacrylate: mix 1mol PPG-1000 with DBT accounting for 0.5% by weight of PPG-1000, add dropwise to 2mol HDI, react at 60°C for 1h, then add 2mol HEA, react at 60°C for 3h, Obtain polyether urethane acrylate;

[0026] (2) Light-thermal dual curing 3D printing: mix the polyether urethane acrylate obtained in step (1) with HDDA and TPO according to the following mass percentages, and use a light-curing printer for 3D printing to obtain a photopolymer. Test The glass transition temperature of the photopolymer is -18°C, which is lower than room temperature; then according to the following mass percentage, mix polyether urethane acrylate, HDDA, TPO, dicyandiamide curing agent and bisphenol A epoxy resin and then photocure and print , and then heated to 160 ° C for 6 hours to obtain 3D printed products; the dicyandiamide curing agent is produced by Guangzhou Xinxi Metallurgical Chemical Co., Ltd., the brand name is SH-300, and the bisphenol A e...

Embodiment 2

[0029] (1) Preparation of polyurethane polyacrylate: mix 1mol PCDL-1000 with DBT accounting for 0.5% by weight of PCDL-1000, add dropwise to 2mol HDI, react at 60°C for 1h, then add 2mol HEA, react at 60°C for 3h, Obtain polyester urethane acrylate;

[0030] (2) Photo-thermal dual curing 3D printing: mix the polyester urethane acrylate obtained in step (1) with HDDA and TPO according to the following mass percentage, and use a light-curing printer to perform 3D printing to obtain a polymer, and test the polymer. The glass transition temperature is -11°C, which is lower than room temperature; according to the following mass percentage, mix polyester urethane acrylate, HDDA, TPO, imidazole curing agent and polyurethane modified epoxy resin evenly, light-cure and print, and heat to After curing at 110°C for 6 hours, the 3D printed product was obtained; the imidazole curing agent was produced by Guangzhou Xinxi Metallurgical Chemical Co., Ltd., the brand name is SH-A80, and the po...

Embodiment 3

[0033] (1) Preparation of polyurethane polyacrylate: mix 1mol PCDL-1000 with DBT accounting for 0.5% by weight of PCDL-1000, add dropwise to 2mol HDI, react at 60°C for 1h, then add 2mol HEA, react at 60°C for 3h, Obtain polyester urethane acrylate;

[0034](2) Photo-thermal dual curing 3D printing: the polyester urethane acrylate obtained in step (1) is mixed with IBOA and TPO according to the following mass percentage, and 3D printing is performed using a light-curing printer to obtain a polymer, and the polymer is tested. The glass transition temperature is 6°C, which is lower than room temperature; according to the following mass percentage, mix polyester urethane acrylate, IBOA, TPO, ammonium blocked Lewis acid salt and alicyclic epoxy resin evenly, light-cure 3D printing, and then heat After curing at 100°C for 6 hours, 3D printed products were obtained; the ammonium-blocked Lewis acid salt was purchased from Shenzhen Kaiji Applied Materials Co., Ltd., trade name Vicbase...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method of light-thermal dual curing 3D printing and its products, comprising the following steps: mixing raw materials, performing light-curing 3D printing, and then heating and curing to obtain 3D printed products; the raw materials include: polyurethane acrylic acid Esters, diluents, initiators, epoxy resins and thermotropic curing agents; Among them, polyurethane acrylate is obtained by reacting isocyanate with polyols, and then capped with hydroxyl-containing acrylates, and polyols have a molecular weight of not less than 1000 Polyester polyol or polyether polyol. The method of the invention avoids the phenomenon that the thermal curing of the epoxy resin causes the polymerization product to become brittle, realizes the dual curing of the epoxy resin to obtain basic toughness, and satisfies the application in industrial manufacturing.

Description

technical field [0001] The invention relates to the field of 3D printing, in particular to a method of photothermal dual curing 3D printing and a product thereof. Background technique [0002] Light-curing 3D printing products are thermosetting resins. Thermosetting materials are a type of cross-linked polymer materials with a network structure. The biggest weakness of the cross-network structure of thermosetting resins is that they are brittle after curing and have poor impact and stress crack resistance. , the plastic deformation is constrained, which limits their application in some fields. In addition, due to the limitation of photocuring printing technology, photosensitive resins with small molecular weight and low viscosity are generally used, and the polymerization degree of photosensitive resin monomers is not high during the printing process, so the mechanical properties of the obtained 3D printed products are insufficient. The introduction of light-dark dual-curin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L51/08C08L63/00C08F283/00C08F220/18C08F222/14C08G18/67C08G18/48C08G18/44B33Y70/00
CPCB33Y70/00C08F283/008C08G18/44C08G18/4825C08G18/672C08L51/08C08L63/00C08G18/48C08F220/1811
Inventor 陈遒刘丹丹来国桥胡自强
Owner HANGZHOU NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products