A technology for asphalt pavement and road construction, used in roads, roads, road repair and other directions, can solve the problem of difficult peeling of the protective film, and achieve the effects of good protection, high heat sealing strength and good tear resistance.

Active Publication Date: 2019-08-16
山东惠民腾达交通工程有限责任公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to solve the problem that the existing protective film is not easy to peel off, the present invention provides a protective film and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Protective film material for asphalt pavement during road construction and road construction method
  • Protective film material for asphalt pavement during road construction and road construction method
  • Protective film material for asphalt pavement during road construction and road construction method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026]The protective film material used for road construction asphalt pavement includes the first PET layer, the first SBS layer, the second PET layer, the first SIS layer, the first polyethylene layer, the second polyethylene layer, the second The SBS layer and the third PET layer, wherein the first PET layer has a first melt flow rate based on the ASTM-D-1238 test, the first SBS layer has a second melt flow rate based on the ASTM-D-1238 test, The second PET layer has a third melt flow rate based on the ASTM-D-1238 test, the first SIS layer has a fourth melt flow rate based on the ASTM-D-1238 test, and the first polyethylene layer has a melt flow rate based on the ASTM-D-1238 test. -Fifth melt flow rate based on the 1238 test, the second polyethylene layer has a sixth melt flow rate based on the ASTM-D-1238 test, and the second SBS layer has a seventh melt flow rate based on the ASTM-D-1238 test rate and the third PET layer has an eighth melt flow rate based on the ASTM-D-123...

Embodiment 2

[0028] The protective film material used for road construction asphalt pavement includes the first PET layer, the first SBS layer, the second PET layer, the first SIS layer, the first polyethylene layer, the second polyethylene layer, the second The SBS layer and the third PET layer, wherein the first PET layer has a first melt flow rate based on the ASTM-D-1238 test, the first SBS layer has a second melt flow rate based on the ASTM-D-1238 test, The second PET layer has a third melt flow rate based on the ASTM-D-1238 test, the first SIS layer has a fourth melt flow rate based on the ASTM-D-1238 test, and the first polyethylene layer has a melt flow rate based on the ASTM-D-1238 test. -Fifth melt flow rate based on the 1238 test, the second polyethylene layer has a sixth melt flow rate based on the ASTM-D-1238 test, and the second SBS layer has a seventh melt flow rate based on the ASTM-D-1238 test rate and the third PET layer has an eighth melt flow rate based on the ASTM-D-12...

Embodiment 3

[0030] The protective film material used for road construction asphalt pavement includes the first PET layer, the first SBS layer, the second PET layer, the first SIS layer, the first polyethylene layer, the second polyethylene layer, the second The SBS layer and the third PET layer, wherein the first PET layer has a first melt flow rate based on the ASTM-D-1238 test, the first SBS layer has a second melt flow rate based on the ASTM-D-1238 test, The second PET layer has a third melt flow rate based on the ASTM-D-1238 test, the first SIS layer has a fourth melt flow rate based on the ASTM-D-1238 test, and the first polyethylene layer has a melt flow rate based on the ASTM-D-1238 test. -Fifth melt flow rate based on the 1238 test, the second polyethylene layer has a sixth melt flow rate based on the ASTM-D-1238 test, and the second SBS layer has a seventh melt flow rate based on the ASTM-D-1238 test rate and the third PET layer has an eighth melt flow rate based on the ASTM-D-12...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a protective film material for asphalt pavement during road construction. The protective film material sequentially comprises a first polyethylene terephthalate (PET) layer, afirst styrene-butadiene-styrene (SBS) layer, a second PET layer, a first styrene-isoprene-styrene (SIS) layer, a first polyethylene layer, a second polyethylene layer, a second SBS layer and a third PET layer from inside to outside, wherein the first PET layer has a first melt flow rate based on ASTM-D-1238 test, the first SBS layer has a second melt flow rate based on ASTM-D-1238 test, the secondPET layer has a third melt flow rate based on ASTM-D-1238 test, the first SIS layer has a fourth melt flow rate based on ASTM-D-1238 test, the first polyethylene layer has a fifth melt flow rate based on ASTM-D-1238 test, the second polyethylene layer has a sixth melt flow rate based on ASTM-D-1238 test, the second SBS layer has a seventh melt flow rate based on ASTM-D-1238 test, and the third PET layer has an eighth melt flow rate based on ASTM-D-1238 test. The protective film material disclosed by the invention is good in tear resistance and high in heat sealing strength and can well protect an asphalt construction pavement.

Description

technical field [0001] The invention relates to the technical field of road construction, in particular to a protective film material used for road construction asphalt pavement and a road construction method. Background technique [0002] Asphalt pavement refers to various types of pavement paved with asphalt materials mixed with mineral materials. Asphalt binder improves the ability of paving aggregates to resist road damage from driving and natural factors, making the road smooth, less dusty, impermeable and durable. Therefore, asphalt pavement is the most widely used high-grade pavement in road construction. [0003] Prior art CN109016716A discloses a high-barrier strength cross film, which includes: HDPE layer, HDPE and first color masterbatch mixed layer, HDPE and second color masterbatch mixed layer, adhesive layer, HDPE layer from top to bottom , HDPE and the first color masterbatch mixing layer, HDPE and the second color masterbatch mixing layer, PVA coating layer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/36B32B27/30B32B27/08B32B27/32B32B33/00E01C23/03
CPCB32B27/08B32B27/302B32B27/32B32B27/36B32B33/00B32B2250/24B32B2307/31B32B2307/558B32B2307/5825B32B2307/7265E01C23/03
Inventor 李雪刘宁张春燕巩志忠黄永斌王涛桑童童王振松许瑞刚李阳阳
Owner 山东惠民腾达交通工程有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap