Electrode wire containing carton on surface layer for low-speed wire-cutting electrical discharge machining and preparation method thereof

A technology of wire electrode and slow wire walking, which is applied in electric processing equipment, electrode manufacturing, metal processing equipment, etc., to achieve the effects of improving processing accuracy, improving surface finish, and stabilizing the discharge gap

Active Publication Date: 2019-08-16
NINGBO BODE HIGHTECH CO LTD
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In particular, the processing accuracy, surface finish and processing speed have developed by leaps and bounds compared with the first generation of copper wire, but the development of the industry will never satisfy the status quo. In the new manufacturing environment, the current slow-moving wire Spark machining users are facing new difficulties and challenges

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrode wire containing carton on surface layer for low-speed wire-cutting electrical discharge machining and preparation method thereof
  • Electrode wire containing carton on surface layer for low-speed wire-cutting electrical discharge machining and preparation method thereof
  • Electrode wire containing carton on surface layer for low-speed wire-cutting electrical discharge machining and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1. Prepare brass grades H65 and wire blanks with a diameter of Φ1.2mm. After electroplating pretreatment, carry out alkali cleaning and pickling. After the surface of the wire blanks is cleaned, enter the electroplating tank. The bath liquid is zinc sulfate 1000g / L, CHO A mixed solution of 20g / L of organic matter, 15g / L of aluminum salt and 15g / L of potassium salt, the production speed is set to 100m / min, the electroplating current is 900A, the voltage is 8V, and the coating thickness of the final electroplating wire billet is 10 microns. The surface roughness of the blank is Ra 0.12 μm.

[0038] 2. Carry out the carbon precipitation reaction in the annealing furnace with 97% nitrogen content, the reaction temperature is 150°C, the reaction time is 10 hours, the furnace temperature is 50°C, and the uniformity in the furnace is ±10 ℃.

[0039] 3. The wire blank after the carbon precipitation reaction is cleaned with aviation kerosene, stretched to Φ0.6mm after cleaning,...

Embodiment 2

[0045] 1. Prepare brass grades H65 and wire blanks with a diameter of Φ1.2mm. After electroplating pretreatment, carry out alkali cleaning and pickling. After the surface of the wire blanks is cleaned, enter the electroplating tank. The bath liquid is zinc sulfate 1000g / L, CHO A mixed solution of 20g / L of organic matter, 15g / L of aluminum salt and 15g / L of potassium salt, the production speed is set to 100m / min, the electroplating current is 2000A, the voltage is 9V, and the coating thickness of the final electroplating wire billet is 20 microns. The surface roughness of the blank is Ra 0.15 μm.

[0046] 2. Carry out the carbon precipitation reaction in the annealing furnace with 97% nitrogen content, the reaction temperature is 750°C, the reaction time is 3 hours, the furnace temperature is 80°C, and the uniformity in the furnace is ±10 ℃.

[0047] 3. The wire billet after the carbon precipitation reaction is cleaned with aviation kerosene, and drawn to the specification of ...

Embodiment 3

[0053] 1. Prepare brass grades H65 and wire blanks with a diameter of Φ1.2mm. After electroplating pretreatment, carry out alkali cleaning and pickling. After the surface of the wire blanks is cleaned, enter the electroplating tank. The bath liquid is zinc sulfate 1000g / L, CHO A mixed solution of 20g / L of organic matter, 15g / L of aluminum salt and 15g / L of potassium salt, the production speed is set to 100m / min, the electroplating current is 900A, the voltage is 8V, and the coating thickness of the final electroplating wire billet is 10 microns. The surface roughness of the blank is Ra 0.12 μm.

[0054] 2. Carry out carbon precipitation reaction in the annealing furnace with 97% nitrogen content in the plated wire blank. The reaction temperature is 750°C, the reaction time is 10 hours, the furnace temperature is 80°C, and the uniformity in the furnace is ±10 ℃.

[0055] 3. The wire billet after the carbon precipitation reaction is cleaned with aviation kerosene, and drawn to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an electrode wire containing carton on the surface layer for low-speed wire-cutting electrical discharge machining and a preparation method thereof. The electrode wire is characterized by comprising a core material (1), a carbide layer (3) on the outermost layer, and a phase change layer (2) positioned between the core material (1) and the carbide layer (3). The electrode wire with the special structure can improve the machining speed by above 15% compared with a plating wire, and is higher in machining precision compared with the plating wire. The electrode wire is simple in machining process, greatly improves the performances, and achieves higher market competitiveness compared with the plating wire.

Description

technical field [0001] The invention relates to the technical field of slow wire electric discharge machining, in particular to a carbon-containing electrode wire for slow wire electric discharge machining and a preparation method thereof. Background technique [0002] WEDM (Wire cut Electrical Discharge Machining) is also called wire cutting. The principle is to use the continuously moving electrode wire as the electrode, conduct pulse spark discharge on the workpiece to etch the metal, and finally process and shape it according to the set trajectory. Compared with other processing methods, WEDM has better roundness error, straight line error and dimensional error, and is widely used in aerospace manufacturing. Especially since 1980, as the molds of precision machinery parts, home appliances, and communication equipment have gradually become more sophisticated, wire discharge machining has become an indispensable processing method in the mold manufacturing industry. In re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23H7/10B23H7/22
CPCB23H7/10B23H7/22B23H7/08C25D7/0607C25D5/50C25D3/22C25D5/34C25D5/605B23H1/06
Inventor 林火根孟宪旗梁志宁吴桐胡美俊顾洪方陈益波
Owner NINGBO BODE HIGHTECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com