Metalized slurry of power battery sealing connector and preparation method of metalized slurry

A power battery, metallization technology, applied in conductive materials dispersed in non-conductive inorganic materials, cable/conductor manufacturing, circuits, etc., can solve problems affecting the stability of metallization process and air tightness, tension and poor consistency and other problems to achieve the effect of ensuring thickness consistency, easy operation, and avoiding cracks

Inactive Publication Date: 2019-08-13
LOUDI ANTAEUS ELECTRONICS CERAMICS
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The interface, tension and wettability consistency between the carrier and the solid powder in the existing thick film slurry is poor, which affects the stability and air tightness of the metallization process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A new energy electric vehicle power battery sealing connector metallization paste, including metallization raw materials and organic adhesives, the mass ratio of the metallization raw materials and organic adhesives is 4:1, the metallization raw materials include Metal powder and metal oxide activator, the components and mass percentage of the metal powder are: 30% molybdenum powder, 20% manganese powder, the components and mass percentage of the metal oxide activator are alumina powder 10%, silicon dioxide 8%, titanium dioxide 2%, tantalum pentoxide 2%; the organic binder includes ethyl cellulose, terpineol, silicone defoamer, hydroxyl polyether modified polydimethyl base siloxane, the mass ratio of ethyl cellulose, terpineol, silicone defoamer, and hydroxyl polyether modified polydimethylsiloxane is 10:1000:3:5.

[0024] A method for preparing a metallized slurry for a new energy electric vehicle power battery sealing connector, comprising the following steps: (1) pre...

Embodiment 2

[0026] A new energy electric vehicle power battery sealing connector metallization paste, including metallization raw materials and organic adhesives, the mass ratio of the metallization raw materials and organic adhesives is 9:1, the metallization raw materials include Metal powder and metal oxide activator, the components and mass percentage of the metal powder are: 50% molybdenum powder, 10% manganese powder, the components and mass percentage of the metal oxide activator are alumina powder 15%, silicon dioxide 15%, titanium dioxide 1%, tantalum pentoxide 1%; the organic binder includes ethyl cellulose, terpineol, silicone defoamer, hydroxyl polyether modified polydimethyl base siloxane, the mass ratio of ethyl cellulose, terpineol, silicone defoamer, and hydroxyl polyether modified polydimethylsiloxane is 15:1199:3:5.

[0027]A method for preparing a metallized slurry for a new energy electric vehicle power battery sealing connector, comprising the following steps: (1) pre...

Embodiment 3

[0029] A new energy electric vehicle power battery sealing connector metallization paste, including metallization raw materials and organic adhesives, the mass ratio of the metallization raw materials and organic adhesives is 4:1, the metallization raw materials include Metal powder and metal oxide activator, the components and mass percentage of the metal powder are: 35% molybdenum powder, 15% manganese powder, the components and mass percentage of the metal oxide activator are alumina powder 12%, silicon dioxide 12%, titanium dioxide 1%, tantalum pentoxide 2%; the organic binder includes ethyl cellulose, terpineol, silicone defoamer, silicone leveling agent, the The mass ratio of ethyl cellulose, terpineol, silicone defoamer, and silicone leveling agent is 12:1100:3:5.

[0030] A method for preparing a metallized slurry for a new energy electric vehicle power battery sealing connector, comprising the following steps: (1) preparing a metal oxide active agent: taking the compo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses metalized slurry of a power battery sealing connector and a preparation method of the metalized slurry. The metalized slurry comprises a metalized raw material and an organic adhesive, and the mass ratio of the metalized raw material to the organic adhesive is 8-9 : 1-2. The metalized raw material comprises a metal oxide active agent, and the metal oxide active agent comprises the following components in percentage by mass: 10-15% of aluminum oxide powder, 8-15% of silicon dioxide, 1-2% of titanium dioxide and 1-2% of tantalum pentoxide. The organic adhesive comprises ethyl cellulose, terpene alcohol, organic silicon defoamer and an organic silicon flatting agent, and the mass ratio of the ethyl cellulose to the terpene alcohol to the organic silicon defoamer to theorganic silicon flatting agent is 10-15 : 1000-1199 : 3 : 5. The roughness of the metalized surface of the sintered battery sealing connector is reduced to be less than or equal to 1.0 [mu]m, and themetalized sealing strength is improved to be more than or equal to 120Mpa.

Description

technical field [0001] The invention belongs to the technical field of electric vehicle power batteries, and in particular relates to a metallization paste for a sealed connector of a power battery and a preparation method thereof. Background technique [0002] Due to the performance characteristics of ceramics such as high strength, small dielectric constant, high volume resistivity, small dielectric loss and high thermal shock resistance, ceramic parts themselves are excellent insulating materials, and they do not have solderability themselves. Solder usually cannot Its infiltration and metallization are an effective way to realize the sealing of ceramics and metals. [0003] The raw materials and formulations used in ceramic metallization are the key to metallization. In actual production, different manufacturers have different special raw material formulas. The paste or slurry composed of specific formula raw materials can effectively achieve the coating of specific pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/22H01B13/00
CPCH01B1/22H01B13/00
Inventor 张桓桓康丁华周伍
Owner LOUDI ANTAEUS ELECTRONICS CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products